Dendritic Growth During Phase Transformation in Ni-Mo System Induced by Ion Beam

1986 ◽  
Vol 74 ◽  
Author(s):  
B. X. Liu ◽  
L. J. Huang ◽  
C. H. Shang
Keyword(s):  
Dendritic Growth ◽  
Room Temperature ◽  
Ion Beam ◽  
Cluster Formation ◽  
Beam Current ◽  
Beam Current Density ◽  
X Ray Diffraction ◽  
X Ray ◽  
Transmission Electron ◽  
Amorphous Phase Formation

AbstractMultilayered Ni-Mo films were irradiated by 200keV Xe ions at room temperature to various doses. The beam current density was confined to be less than lμA/cm2 to avoid overheating. The experimental evidences from X-ray diffraction, electrical resistivity, as well 4 as Rutherford Backscattering, indicate that a dose of 7 × 1014/cm2 was the critical one for uniform mixing of the layers and amorphous phase formation in Ni65 Mo35 films. Under this critical dose, various dendritic patterns were formed as revealed by bright field transmission electron microscopy. The microscopic mechanisms of the ion induced dendritic growth are attributed to the cluster formation and the aggregation of the formed clusters.

Room Temperature Synthesis of Cu2O Nanospheres: Optical Properties and Thermal Behavior

2014 ◽  
Vol 21 (1) ◽  
pp. 108-119 ◽  
Author(s):  
Daniela Nunes ◽  
Lídia Santos ◽  
Paulo Duarte ◽  
Ana Pimentel ◽  
Joana V. Pinto ◽  
...  
Keyword(s):  
Electron Microscopy ◽  
Transmission Electron Microscopy ◽  
Thermal Behavior ◽  
Room Temperature ◽  
Diffuse Reflectance Spectroscopy ◽  
Ion Beam ◽  
X Ray Diffraction ◽  
Scanning Calorimetry ◽  
X Ray ◽  
Transmission Electron

AbstractThe present work reports a simple and easy wet chemistry synthesis of cuprous oxide (Cu2O) nanospheres at room temperature without surfactants and using different precursors. Structural characterization was carried out by X-ray diffraction, transmission electron microscopy, and scanning electron microscopy coupled with focused ion beam and energy-dispersive X-ray spectroscopy. The optical band gaps were determined from diffuse reflectance spectroscopy. The photoluminescence behavior of the as-synthesized nanospheres showed significant differences depending on the precursors used. The Cu2O nanospheres were constituted by aggregates of nanocrystals, in which an on/off emission behavior of each individual nanocrystal was identified during transmission electron microscopy observations. The thermal behavior of the Cu2O nanospheres was investigated with in situ X-ray diffraction and differential scanning calorimetry experiments. Remarkable structural differences were observed for the nanospheres annealed in air, which turned into hollow spherical structures surrounded by outsized nanocrystals.

Photoluminescence Enhancement of CdS Nanocrystals Fabricated on Dithiocarbamate Functionalized PET Substrates

2012 ◽  
Vol 512-515 ◽  
pp. 1511-1515
Author(s):  
Chun Lin Zhao ◽  
Li Xing ◽  
Xiao Hong Liang ◽  
Jun Hui Xiang ◽  
Fu Shi Zhang ◽  
...  
Keyword(s):  
Room Temperature ◽  
Hexagonal Structure ◽  
Diffraction Measurement ◽  
X Ray Diffraction ◽  
Visible Absorption ◽  
X Ray ◽  
Cds Nanocrystals ◽  
Morphological Studies ◽  
Transmission Electron

Cadmium sulfide (CdS) nanocrystals (NCs) were self-assembled and in-situ immobilized on the dithiocarbamate (DTCs)-functionalized polyethylene glycol terephthalate (PET) substrates between the organic (carbon disulfide diffused in n-hexane) –aqueous (ethylenediamine and Cd2+ dissolved in water) interface at room temperature. Powder X-ray diffraction measurement revealed the hexagonal structure of CdS nanocrystals. Morphological studies performed by scanning electron microscopy (SEM) and high-resolution transmission electron microscope (HRTEM) showed the island-like structure of CdS nanocrystals on PET substrates, as well as energy-dispersive X-ray spectroscopy (EDS) confirmed the stoichiometries of CdS nanocrystals. The optical properties of DTCs modified CdS nanocrystals were thoroughly investigated by ultraviolet-visible absorption spectroscopy (UV-vis) and fluorescence spectroscopy. The as-prepared DTCs present intrinsic hydrophobicity and strong affinity for CdS nanocrystals.

scholarly journals Facile Organometallic Synthesis of Fe-Based Nanomaterials by Hot Injection Reaction

Nanomaterials ◽  
2021 ◽  
Vol 11 (5) ◽  
pp. 1141
Author(s):  
Georgia Basina ◽  
Hafsa Khurshid ◽  
Nikolaos Tzitzios ◽  
George Hadjipanayis ◽  
Vasileios Tzitzios
Keyword(s):  
Room Temperature ◽  
Colloidal Particles ◽  
Iron Pentacarbonyl ◽  
Vibrating Sample Magnetometer ◽  
X Ray Diffraction ◽  
Organometallic Synthesis ◽  
X Ray ◽  
Transmission Electron ◽  
Hot Injection ◽  
The Stability

Fe-based colloids with a core/shell structure consisting of metallic iron and iron oxide were synthesized by a facile hot injection reaction of iron pentacarbonyl in a multi-surfactant mixture. The size of the colloidal particles was affected by the reaction temperature and the results demonstrated that their stability against complete oxidation related to their size. The crystal structure and the morphology were identified by powder X-ray diffraction and transmission electron microscopy, while the magnetic properties were studied at room temperature with a vibrating sample magnetometer. The injection temperature plays a very crucial role and higher temperatures enhance the stability and the resistance against oxidation. For the case of injection at 315 °C, the nanoparticles had around a 10 nm mean diameter and revealed 132 emu/g. Remarkably, a stable dispersion was created due to the colloids’ surface functionalization in a nonpolar solvent.

Synthesis and Photoluminescence Properties of Novel SnO2 Zigzag Nanoribbons

2010 ◽  
Vol 97-101 ◽  
pp. 4213-4216
Author(s):  
Jian Xiong Liu ◽  
Zheng Yu Wu ◽  
Guo Wen Meng ◽  
Zhao Lin Zhan
Keyword(s):  
Electron Microscopy ◽  
Room Temperature ◽  
Vapour Deposition ◽  
Chemical Vapour ◽  
Photoluminescence Properties ◽  
X Ray Diffraction ◽  
X Ray ◽  
Selected Area Electron Diffraction ◽  
Transmission Electron ◽  
Ceramic Boat

Novel single-crystalline SnO2 zigzag nanoribbons have been successfully synthesized by chemical vapour deposition. Sn powder in a ceramic boat covered with Si plates was heated at 1100°C in a flowing argon atmosphere to get deposits on a Si wafers. The main part of deposits is SnO2 zigzag nanoribbons. They were characterized by means of X-ray diffraction (XRD), field-emission scanning electron microscopy (FE-SEM), energy-dispersive X-ray spectroscopy (EDX), transmission electron microscopy (TEM) and selected-area electron diffraction (SAED). SEM observations reveal that the SnO2 zigzag nanoribbons are almost uniform, with lengths near to several hundred micrometers and have a good periodically tuned microstructure as the same zigzag angle and growth directions. Possible growth mechanism of these zigzag nanoribbons was discussed. A room temperature PL spectrum of the zigzag nanoribbons shows three peaks at 373nm, 421nm and 477nm.The novel zigzag microstructures will provide a new candidate for potential application.

Formation and Thermal Stability of Nd0.32Y0.68Si1.7 Layers Formed by Channeled Ion Beam Synthesis

1998 ◽  
Vol 514 ◽  
Author(s):  
M. F. Wu ◽  
A. Vantomne ◽  
S. Hogg ◽  
H. Pattyn ◽  
G. Langouche ◽  
...  
Keyword(s):  
Thermal Stability ◽  
Ion Beam ◽  
Hexagonal Structure ◽  
Orthorhombic Structure ◽  
X Ray Diffraction ◽  
X Ray ◽  
Transmission Electron ◽  
Good Crystalline Quality ◽  
Ion Beam Synthesis ◽  
Thermal Stability Of

ABSTRACTThe Nd-disilicide, which exists only in a tetragonal or an orthorhombic structure, cannot be grown epitaxially on a Si(111) substrate. However, by adding Y and using channeled ion beam synthesis, hexagonal Nd0.32Y0.68Si1.7 epilayers with lattice constant of aepi = 0.3915 nm and cepi = 0.4152 nm and with good crystalline quality (χmin of Nd and Y is 3.5% and 4.3 % respectively) are formed in a Si(111) substrate. This shows that the addition of Y to the Nd-Si system forces the latter into a hexagonal structure. The epilayer is stable up to 950 °C; annealing at 1000 °C results in partial transformation into other phases. The formation, the structure and the thermal stability of this ternary silicide have been studied using Rutherford backscattering/channeling, x-ray diffraction and transmission electron microscopy.

Preparation and Properties of Nano-Crystalline Cellulose Electro-Rheological Fluid

2015 ◽  
Vol 815 ◽  
pp. 217-221
Author(s):  
Ling Li Xu ◽  
Xing Ling Shi ◽  
Qing Liang Wang
Keyword(s):  
Room Temperature ◽  
Silicone Oil ◽  
Strong Acid ◽  
Crystalline Cellulose ◽  
Methyl Silicone ◽  
Shearing Stress ◽  
X Ray Diffraction ◽  
X Ray ◽  
Nano Crystalline ◽  
Transmission Electron

nanocrystalline cellulose (NCC) was prepared from micro-crystalline cellulose (MCC) by strong acid hydrolysis. The characteristics of such particle were studied by transmission electron microscopy, X-ray diffraction and Fourier transform infrared spectroscopy. Electro-rheological fluids (ERF) were prepared by dispersing NCC and MCC in methyl-silicone oil, and their ER effects were measured. Experimental results indicated that NCC ERF exhibited a remarkable ER effect. The highest static shearing stress of NCC ERF (3.5 g/ml) was 5.1 kPa at the room temperature under a 4 .2 kV/mm electric field, increased about 5.5 times compared to MCC ERF, and sedimentation of NCC ERF was not observed even after 60 days.

New method for the production of bulk amorphous materials of Nd–Fe–B alloys

2005 ◽  
Vol 20 (3) ◽  
pp. 563-566 ◽  
Author(s):  
Tetsuji Saito ◽  
Hiroyuku Takeishi ◽  
Noboru Nakayama
Keyword(s):  
Electron Microscopy ◽  
Amorphous Materials ◽  
Room Temperature ◽  
Amorphous Structure ◽  
X Ray Diffraction ◽  
Bulk Materials ◽  
X Ray ◽  
Transmission Electron ◽  
Melt Spun ◽  
Melt Spun Ribbons

We report a new compression shearing method for the production of bulk amorphous materials. In this study, amorphous Nd–Fe–B melt-spun ribbons were successfully consolidated into bulk form at room temperature by the compression shearing method. X-ray diffraction and transmission electron microscopy studies revealed that the amorphous structure was well maintained in the bulk materials. The resultant bulk materials exhibited the same magnetic properties as the original amorphous Nd–Fe–B materials.

A Chemical Solution Route to Rapid Synthesis of Homogeneous Bi100−xSbx Alloys Nanoparticles at Room Temperature

2007 ◽  
Vol 7 (2) ◽  
pp. 525-529 ◽  
Author(s):  
Bo Zhou ◽  
Jun-Jie Zhu
Keyword(s):  
Room Temperature ◽  
Raw Materials ◽  
X Ray Diffraction ◽  
X Ray ◽  
Selected Area Electron Diffraction ◽  
Transmission Electron ◽  
Solution Route ◽  
Diffraction Patterns ◽  
Co Reduction ◽  
Chemical Solution Route

A chemical co-reduction route in aqueous solution was developed to synthesize Bi100−xSbx alloys at room temperature. The hydrolyses of Bi(III) and Sb(III) were effectively avoided by selecting proper raw materials and coordinator. X-ray diffraction analysis indicated that the as-prepared Bi100−xSbx alloys were homogeneous and phase-pure, and the Bi/Sb ratios in the alloys were very close to those in the aqueous solutions. The transmission electron microscope observation showed that the as-prepared Bi100−xSbx (x = 0∼100) alloys were particles with a size of tens of nanometers. The selected area electron diffraction patterns confirmed the high crystallinity, the homogeneousness, and the composition controllability of as-prepared alloys. All these characters and the nanometer-scaled size of the alloys are believed to be beneficial to the thermoelectric property of the Bi100−xSbx alloys.

Relationship Between Microstructure and Hardness of ZrN/TiN Multi-Layers with Various Bilayer Thicknesses

2010 ◽  
Vol 63 ◽  
pp. 392-395
Author(s):  
Yoshifumi Aoi ◽  
Satoru Furuhata ◽  
Hiromi Nakano
Keyword(s):  
Mechanical Property ◽  
Electron Microscope ◽  
Transmission Electron Microscope ◽  
Ion Beam ◽  
Ion Beam Sputtering ◽  
X Ray Diffraction ◽  
X Ray ◽  
Transmission Electron ◽  
Beam Sputtering ◽  
Microstructure And Mechanical Property

ZrN/TiN multi-layers were synthesized by ion beam sputtering technique. Microstructure and mechanical property of the ZrN/TiN multi-layers were characterized and the relationships between microstructure and hardness of the ZrN/TiN multi-layers with various bilayer thicknesses and thickness ratios were investigated. The microstructure of multi-layers have been investigated using transmission electron microscope (TEM) and X-ray diffraction (XRD).

Effects of Bi Doping on the In15Sb85 Phase Change Recording Thin Film

2008 ◽  
Vol 47-50 ◽  
pp. 813-816
Author(s):  
Sin Liang Ou ◽  
Po Cheng Kuo ◽  
Shu Chi Sheu ◽  
Chih Hsiang Hsiao ◽  
Don Yau Chiang ◽  
...  
Keyword(s):  
Room Temperature ◽  
X Ray Diffraction ◽  
Crystallization Activation Energy ◽  
Composite Target ◽  
X Ray ◽  
Transmission Electron ◽  
Thermal Analyzer ◽  
Crystallization Speed ◽  
Bi Doping ◽  
Si Wafer

The (In15Sb85)100-xBix films (x = 0~18.3) were deposited on nature oxidized Si wafer and glass substrate at room temperature by magnetron co-sputtering of Sb target and InBi composite target. The optical and thermal properties of the films were examined by reflectivity thermal analyzer. Microstructures of the films were analyzed by X-ray diffraction and transmission electron microscope. The crystallization activation energy of the (In15Sb85)100-xBix film (x = 0~18.3) was decreased with increasing Bi content, this indicated that the crystallization speed was improved by doping Bi. The structure of as-deposited (In15Sb85)100-xBix films was amorphous and it would transform to Sb, InSb, Bi, and BiIn2 coexisting phases after annealing at 250 °C for 30 min.

Sign in / Sign up

Export Citation Format

Share Document