Electrical Behaviour of Natural Manganese Dioxide (NMD)

1996 ◽  
Vol 431 ◽  
Author(s):  
H. F. Gorgulho ◽  
R. Z. D. Fernandes ◽  
J. M. Pernaut
Keyword(s):  
Particle Size ◽  
Electrical Properties ◽  
Impedance Spectroscopy ◽  
Direct Current ◽  
Charge Separation ◽  
Ionic Transport ◽  
Electrical Behaviour ◽  
X Ray Diffraction ◽  
X Ray ◽  
Physical Treatments

AbstractNMD samples from Brazil have been submitted to magnetic and particle size separations and characterized by X-ray diffraction and fluorescence and thermogravimetric analyses. Results showed that simple physical treatments can lead to more than 60% enriched MnO2 materials which could satistify some electrochemical applications. The electrical properties of the samples conditionated as pressed pellets have been investigated by four-points direct current probe and impedance spectroscopy, varying the conditions of preparation and measurement. It is proposed that the higher frequency impedance is equivalent to the intrinsic electronic resistance of the MnO2 phases while at lower frequencies occurs an interphase charge separation coupled with a possible ionic transport. The corresponding contact resistance depends on the article size distribution of the material, the compactation pressure of pellets and the iron content of the materials. The interphase dielectric relaxation does not behave ideally; the depression of the impedance semicircles as shown in the Nyquist plane is assumed to be related to the roughness of the bulk interfaces.

scholarly journals Use of Impedance Spectroscopy in the Study of the Effect of Cr Concentration on the Electrical Properties of SnO2-Based Ceramics

2005 ◽  
Vol 498-499 ◽  
pp. 337-341 ◽  
Author(s):  
Daniela Russo Leite ◽  
W.C. Las ◽  
G. Brankovic ◽  
M.A. Zaghete ◽  
M. Cilense ◽  
...  
Keyword(s):  
Grain Size ◽  
Electrical Properties ◽  
Impedance Spectroscopy ◽  
Diffraction Analysis ◽  
Grain Boundaries ◽  
Relative Density ◽  
Pechini Method ◽  
X Ray Diffraction ◽  
X Ray ◽  
Cr Concentration

This paper reports a study of influence of Cr concentration on the electrical properties and microstructure of SnO2-based powders doped with Mn and Nb, prepared by an organic route (Pechini method). All the samples were compacted into discs and sintered at 1300°C for 3h, resulting in ceramics with relative density varying between 78% and 98%. The powders were characterized by X-ray diffraction analysis. Impedance spectroscopy characterization indicated that the conductivity decreases as Cr concentration increases, probably due to Cr segregation at grain boundaries, which reduces grain size, increasing the number of resistive boundaries.

scholarly journals Synthesis and Electrical Properties of Ag8SnSe6 Argyrodite Thin Films

2017 ◽  
Vol 18 (1) ◽  
pp. 78-83
Author(s):  
I.V. Semkiv ◽  
N.A. Ukrainets ◽  
V.V. Kusnezh ◽  
E.O. Zmiiovska ◽  
R.Yu. Petrus ◽  
...  
Keyword(s):  
Thin Films ◽  
Cyclic Voltammetry ◽  
Electrical Properties ◽  
Impedance Spectroscopy ◽  
Resistive Switching ◽  
Cell Structure ◽  
Orthorhombic Structure ◽  
X Ray Diffraction ◽  
Graphite Electrodes ◽  
X Ray

The synthesis of Ag8SnSe6 argyrodite thin films with thickness 500 nm by selenization of Ag-Sn film at 480 oC was carried out. Thin films were investigated by X-ray diffraction. Ternary Ag8SnSe6 synthesized in orthorhombic structure with the lattice parameters a = 7.9081(6) Å, b = 7.8189(7) Å, c = 11.0464(9) Å, V = 683.03(10) Å3. Resistive switching cell based on Ag8SnSe6 argyrodite with silver and graphite electrodes was fabricated. Electrical properties of cell were investigated using impedance spectroscopy and cyclic voltammetry. Cell structure and process in this cell were modeled by electric equvivalent circuit. Resistive switching phenomena in Ag/Ag8SnSe6/C cell at certain applied voltage were demonstrated.

Changing the Static and Dynamic Lattice Effects for the Improvement of the Ionic Transport Properties Within the Argyrodite Li6PS5-xSexI

2019 ◽  
Author(s):  
Roman Schlem ◽  
Michael Ghidiu ◽  
Sean Culver ◽  
Anna-Lena Hansen ◽  
Wolfgang Zeier
Keyword(s):  
Ionic Conductivity ◽  
Activation Barrier ◽  
Parent Compound ◽  
Ionic Transport ◽  
X Ray Diffraction ◽  
X Ray ◽  
Lattice Effects ◽  
Solid State Batteries ◽  
All Solid State Batteries ◽  
Pulse Echo

<p>The lithium argyrodites Li<sub>6</sub>PS<sub>5</sub>X (X = Cl, Br, I) have been gaining momentum as candidates for electrolytes in all-solid-state batteries. While these materials have been well-characterized structurally, the influences of the static and dynamic lattice properties are not fully understood. Recent improvements to the ionic conductivity of Li<sub>6</sub>PS<sub>5</sub>I (which as a parent compound is a poor ionic conductor) via elemental substitutions have shown that a multitude of influences affect the ionic transport in the lithium argyrodites, and that even poor conductors in this class have room left for improvement.</p><p>Here we explore the influence of isoelectronic substitution of sulfur with selenium in Li<sub>6</sub>PS<sub>5-<i>x</i></sub>Se<i><sub>x</sub></i>I. Using a combination of X-ray diffraction, impedance spectroscopy, Raman spectroscopy, and pulse-echo speed of sound measurements,we explore the influence of the static and dynamic lattice on the ionic transport. The substitution of S<sup>2-</sup>with Se<sup>2- </sup>broadens the diffusion pathways and structural bottlenecks, as well as leading to a softer more polarizable lattice, all of which lower the activation barrier and lead to an increase in the ionic conductivity. This work sheds light on ways to systematically understand and improve the functional properties of this exciting material family. </p>

Fabrication and study the effect of the laser on the properties of the compound Tl2-xHgxBa2-ySryCa2Cu3O10+δ superconductor

2018 ◽  
pp. 168
Author(s):  
A. Kareem Dahash Ali ◽  
Nihad Ali Shafeek
Keyword(s):  
Transition Temperature ◽  
Solid State ◽  
Hydrostatic Pressure ◽  
Electrical Properties ◽  
Co2 Laser ◽  
Temperature Shift ◽  
Unit Cell ◽  
X Ray Diffraction ◽  
X Ray ◽  
Structural And Electrical Properties

This study included the fabrication of    compound (Tl2-xHgxBa2-ySryCa2Cu3O10+δ) in a manner solid state and under hydrostatic pressure ( 8 ton/cm2) and temperature annealing(850°C), and determine the effect of the laser on the structural and electrical properties elements in the compound, and various concentrations of x where (x= 0.1,0.2,0.3 ). Observed by testing the XRD The best ratio of compensation for x is 0.2 as the value of a = b = 5.3899 (A °), c = 36.21 (A °) show that the installation of four-wheel-based type and that the best temperature shift is TC= 142 K  .When you shine a CO2 laser on the models in order to recognize the effect of the laser on these models showed the study of X-ray diffraction of these samples when preparing models with different concentrations of the values ​​of x, the best ratio of compensation is 0.2 which showed an increase in the values ​​of the dimensions of the unit cell a=b = 5.3929 (A °), c = 36.238 (A°). And the best transition temperature after shedding laser is TC=144 K. 

scholarly journals Mining Wastes of an Albite Deposit as Raw Materials for Vitrified Mullite Ceramics

Minerals ◽  
2021 ◽  
Vol 11 (3) ◽  
pp. 232
Author(s):  
Pedro J. Sánchez-Soto ◽  
Eduardo Garzón ◽  
Luis Pérez-Villarejo ◽  
George N. Angelopoulos ◽  
Dolores Eliche-Quesada
Keyword(s):  
Particle Size ◽  
Raw Materials ◽  
Phase Evolution ◽  
Particle Size Analysis ◽  
Size Analysis ◽  
Mining Wastes ◽  
X Ray Diffraction ◽  
X Ray ◽  
Maximum Value

In this work, an examination of mining wastes of an albite deposit in south Spain was carried out using X-ray Fluorescence (XRF), X-ray diffraction (XRD), particle size analysis, thermo-dilatometry and Differential Thermal Analysis (DTA) and Thermogravimetric (TG) analysis, followed by the determination of the main ceramic properties. The albite content in two selected samples was high (65–40 wt. %), accompanied by quartz (25–40 wt. %) and other minor minerals identified by XRD, mainly kaolinite, in agreement with the high content of silica and alumina determined by XRF. The content of Na2O was in the range 5.44–3.09 wt. %, being associated with albite. The iron content was very low (<0.75 wt. %). The kaolinite content in the waste was estimated from ~8 to 32 wt. %. The particle size analysis indicated values of 11–31 wt. % of particles <63 µm. The ceramic properties of fired samples (1000–1350 °C) showed progressive shrinkage by the thermal effect, with water absorption and open porosity almost at zero at 1200–1250 °C. At 1200 °C, the bulk density reached a maximum value of 2.38 g/cm3. An abrupt change in the phase evolution by XRD was found from 1150 to 1200 °C, with the disappearance of albite by melting in accordance with the predictions of the phase diagram SiO2-Al2O3-Na2O and the system albite-quartz. These fired materials contained as main crystalline phases quartz and mullite. Quartz was present in the raw samples and mullite was formed by decomposition of kaolinite. The observation of mullite forming needle-shape crystals was revealed by Scanning Electron Microscopy (SEM). The formation of fully densified and vitrified mullite materials by firing treatments was demonstrated.

scholarly journals Local Strain Distribution in ZnO Microstructures Visualized with Scanning Nano X‐Ray Diffraction and Impact on Electrical Properties

2021 ◽  
pp. 2100201
Author(s):  
Philipp Jordt ◽  
Stjepan B. Hrkac ◽  
Jorit Gröttrup ◽  
Anton Davydok ◽  
Christina Krywka ◽  
...  
Keyword(s):  
Electrical Properties ◽  
Strain Distribution ◽  
Local Strain ◽  
X Ray Diffraction ◽  
X Ray

scholarly journals Synthesis of magnesium carbonate hydrate from natural talc

2020 ◽  
Vol 18 (1) ◽  
pp. 951-961
Author(s):  
Qiuju Chen ◽  
Tao Hui ◽  
Hongjuan Sun ◽  
Tongjiang Peng ◽  
Wenjin Ding
Keyword(s):  
Crystal Structure ◽  
Particle Size ◽  
Crystal Growth ◽  
Crystal Morphology ◽  
Magnesium Carbonate ◽  
Organic Additives ◽  
X Ray Diffraction ◽  
Morphological Transformation ◽  
X Ray ◽  
Carbonation Process

AbstractVarious morphologies of magnesium carbonate hydrate had been synthesized without using any organic additives by carefully adjusting the reaction temperature and time during the talc carbonation process. At lower temperatures, magnesium carbonate hydrate was prone to display needle-like morphology. With the further increase of the carbonation temperature, the sheet-like crystallites became the preferred morphology, and at higher aging temperatures, these crystallites tended to assemble into layer-like structures with diverse morphologies, such as rose-like particles and nest-like structure. The reaction time had no effect on the crystal morphology, but it affected the particle size and situation of the crystal growth. X-Ray diffraction results showed that these various morphologies were closely related to their crystal structure and compositions. The needle-like magnesium carbonate hydrate had a formula of MgCO3·3H2O, whereas with the morphological transformation from needle-like to sheet-like, rose-like, and nest-like structure, their corresponding compositions also changed from MgCO3·3H2O to 4MgCO3·Mg(OH)2·8H2O, 4MgCO3·Mg(OH)2·5H2O, and 4MgCO3·Mg(OH)2·4H2O.

scholarly journals Photocurrent density and electrical properties of Bi0.5Na0.5TiO3-BaNi0.5Nb0.5O3 ceramics

2021 ◽  
Author(s):  
Mingqiang Zhong ◽  
Qin Feng ◽  
Changlai Yuan ◽  
Xiao Liu ◽  
Baohua Zhu ◽  
...  
Keyword(s):  
Electrical Properties ◽  
Photovoltaic Effect ◽  
Short Circuit ◽  
Short Circuit Current ◽  
Photocurrent Density ◽  
Open Circuit ◽  
Light Conditions ◽  
X Ray Diffraction ◽  
Solid State Method ◽  
X Ray

AbstractIn this work, the (1−x)Bi0.5Na0.5TiO3-xBaNi0.5Nb0.5O3 (BNT-BNN; 0.00 ⩽ x ⩽ 0.20) ceramics were prepared via a high-temperature solid-state method. The crystalline structures, photovoltaic effect, and electrical properties of the ceramics were investigated. According to X-ray diffraction, the system shows a single perovskite structure. The samples show the normal ferroelectric loops. With the increase of BNN content, the remnant polarization (Pr) and coercive field (Ec) decrease gradually. The optical band gap of the samples narrows from 3.10 to 2.27 eV. The conductive species of grains and grain boundaries in the ceramics are ascribed to the double ionized oxygen vacancies. The open-circuit voltage (Voc) of ∼15.7 V and short-circuit current (Jsc) of ∼1450 nA/cm2 are obtained in the 0.95BNT-0.05BNN ceramic under 1 sun illumination (AM1.5G, 100 mW/cm2). A larger Voc of 23 V and a higher Jsc of 5500 nA/cm2 are achieved at the poling field of 60 kV/cm under the same light conditions. The study shows this system has great application prospects in the photovoltaic field.

scholarly journals Thermal, Structural, and Physical Properties of Freeze Dried Tropical Fruit Powder

2014 ◽  
Vol 2014 ◽  
pp. 1-10 ◽  
Author(s):  
K. A. Athmaselvi ◽  
C. Kumar ◽  
M. Balasubramanian ◽  
Ishita Roy
Keyword(s):  
Particle Size ◽  
Physical Properties ◽  
Average Particle Size ◽  
Average Particle ◽  
X Ray Diffraction ◽  
Tropical Fruit ◽  
X Ray ◽  
Freeze Dried ◽  
Fruit Powder ◽  
Lcr Meter

This study evaluates the physical properties of freeze dried tropical (guava, sapota, and papaya) fruit powders. Thermal stability and weight loss were evaluated using TGA-DSC and IR, which showed pectin as the main solid constituent. LCR meter measured electrical conductivity, dielectric constant, and dielectric loss factor. Functional groups assessed by FTIR showed presence of chlorides, and O–H and N–H bonds in guava, chloride and C–H bond in papaya, and chlorides, and C=O and C–H bonds in sapota. Particle size and type of starch were evaluated by X-ray diffraction and microstructure through scanning electronic microscopy. A semicrystalline profile and average particle size of the fruit powders were evidenced by X-ray diffraction and lamellar/spherical morphologies by SEM. Presence of A-type starch was observed in all three fruits. Dependence of electric and dielectric properties on frequency and temperature was observed.

The Microstructure and Electrical Property of Porous Cu Film on Soft PVDF Substrate

2012 ◽  
Vol 472-475 ◽  
pp. 1451-1454
Author(s):  
Xue Hui Wang ◽  
Wu Tang ◽  
Ji Jun Yang
Keyword(s):  
Electrical Properties ◽  
Film Surface ◽  
X Ray Diffraction ◽  
Si Substrate ◽  
X Ray ◽  
Cu Films ◽  
Cu Film ◽  
Diffraction Peaks ◽  
Sputtering Pressure ◽  
Effect Method

The porous Cu film was deposited on soft PVDF substrate by magnetron sputtering at different sputtering pressure. The microstructure and electrical properties of Cu films were investigated as a function of sputtering pressure by X-ray diffraction XRD and Hall effect method. The results show that the surface morphology of Cu film is porous, and the XRD revealed that there are Cu diffraction peaks with highly textured having a Cu-(220) or a mixture of Cu-(111) and Cu-(220) at sputtering pressure 0.5 Pa. The electrical properties are also severely influenced by sputtering pressure, the resistivity of the porous Cu film is much larger than that fabricated on Si substrate. Furthermore, the resistivity increases simultaneously with the increasing of Cu film surface aperture, but the resistivity of Cu film still decreases with the increasing grain size. It can be concluded that the crystal structure is still the most important factor for the porous Cu film resistivity.

Sign in / Sign up

Export Citation Format

Share Document