Activated Carbon Filaments with Mainly Mesopores

1996 ◽  
Vol 431 ◽  
Author(s):  
Weiming Lu ◽  
D. D. L. Chung
Keyword(s):  
Activated Carbon ◽  
Specific Surface ◽  
Pore Size ◽  
Surface Area ◽  
Specific Surface Area ◽  
Carbon Filaments

AbstractActivated carbon filaments of diameter ∼ 0.1 μm, mean pore size (BJH) 65 Å, specific surface area 1540 m2/g and burn-off 64% (yield 36%) were obtained by activating carbon filaments of diameter ∼ 0.1 μm in CO2 + N2 (1:1) at 970°C for 100 min. Prior to this activation, the filaments were surface oxidized by exposure to ozone (0.3 vol.% in air) at 150°C for 3 min.

Mesoporous Activated Carbon Filaments

1996 ◽  
Vol 454 ◽  
Author(s):  
Weiming Lu ◽  
D. D. L. Chung
Keyword(s):  
Activated Carbon ◽  
Specific Surface ◽  
Pore Size ◽  
Surface Area ◽  
Specific Surface Area ◽  
Mesoporous Activated Carbon ◽  
Carbon Filaments

ABSTRACTActivated carbon filaments of diameter ∼0.1 μm, main pore size (BJH) 55 Å, specific surface area 1310 m2/g and yield 36.2% were obtained by activating carbon filaments of diameter ∼ 0.1 urn in C02 + N2 (1:1) at 970°C for 80 min. Prior to this activation, the filaments were surface oxidized by exposure to ozone.

scholarly journals Novel Activated Carbon Nanofibers Composited with Cost-Effective Graphene-Based Materials for Enhanced Adsorption Performance toward Methane

Polymers ◽  
2020 ◽  
Vol 12 (9) ◽  
pp. 2064
Author(s):  
Faten Ermala Che Othman ◽  
Norhaniza Yusof ◽  
Noorfidza Yub Harun ◽  
Muhammad Roil Bilad ◽  
Juhana Jaafar ◽  
...  
Keyword(s):  
Graphene Oxide ◽  
Activated Carbon ◽  
Specific Surface ◽  
Pore Size ◽  
Reduced Graphene Oxide ◽  
Surface Area ◽  
Carbon Nanofibers ◽  
Specific Surface Area ◽  
Activated Carbon Nanofibers ◽  
Reduced Graphene

Various types of activated carbon nanofibers’ (ACNFs) composites have been extensively studied and reported recently due to their extraordinary properties and applications. This study reports the fabrication and assessments of ACNFs incorporated with graphene-based materials, known as gACNFs, via simple electrospinning and subsequent physical activation process. TGA analysis proved graphene-derived rice husk ashes (GRHA)/ACNFs possess twice the carbon yield and thermally stable properties compared to other samples. Raman spectra, XRD, and FTIR analyses explained the chemical structures in all resultant gACNFs samples. The SEM and EDX results revealed the average fiber diameters of the gACNFs, ranging from 250 to 400 nm, and the successful incorporation of both GRHA and reduced graphene oxide (rGO) into the ACNFs’ structures. The results revealed that ACNFs incorporated with GRHA possesses the highest specific surface area (SSA), of 384 m2/g, with high micropore volume, of 0.1580 cm3/g, which is up to 88% of the total pore volume. The GRHA/ACNF was found to be a better adsorbent for CH4 compared to pristine ACNFs and reduced graphene oxide (rGO/ACNF) as it showed sorption up to 66.40 mmol/g at 25 °C and 12 bar. The sorption capacity of the GRHA/ACNF was impressively higher than earlier reported studies on ACNFs and ACNF composites. Interestingly, the CH4 adsorption of all ACNF samples obeyed the pseudo-second-order kinetic model at low pressure (4 bar), indicating the chemisorption behaviors. However, it obeyed the pseudo-first order at higher pressures (8 and 12 bar), indicating the physisorption behaviors. These results correspond to the textural properties that describe that the high adsorption capacity of CH4 at high pressure is mainly dependent upon the specific surface area (SSA), pore size distribution, and the suitable range of pore size.

Preparation and Characterization of Microporous Activated Carbon from Raw Petroleum Cokes

2015 ◽  
Vol 814 ◽  
pp. 286-291
Author(s):  
Bo Tao Wang
Keyword(s):  
Methylene Blue ◽  
Activated Carbon ◽  
Specific Surface ◽  
Pore Size Distribution ◽  
Pore Size ◽  
Surface Area ◽  
Specific Surface Area ◽  
High Specific Surface Area ◽  
Activation Time ◽  
Activation Temperature

Adopting the chemical activation method, the high specific surface area activated carbon (AC) was prepared by the solid mixing method using Daqing petroleum cokes as raw materials and KOH as activator. The influence of the ratio of KOH to carbon, activation temperature and activation time on the iodine and methylene blue adsorption properties of the AC were studied. The micro-graphitic structure of the AC was studied by X-ray diffraction (XRD). The BET specific surface area, BJH pore size distribution and pore volume of the AC were determined by N2 adsorption (at 77K). The experimental results show that the high specific surface area AC can be prepared with the ratio of KOH to carbon of 4, activation temperature of 800°C and activation time of 1h. The specific surface area was as high as 2142 m2/g with the iodine adsorption value of 288mg/g and methylene blue adsorption value of 1266mg/g. The XRD and BJH results also show that amorphous carbon was the dominating form, and the pore size distribution represents micropore structure.

Preparation and Characterization of Mesoporous Activated Carbon Fiber

2011 ◽  
Vol 480-481 ◽  
pp. 6-10
Author(s):  
Yan Feng Yang ◽  
Xue Jun Zhang ◽  
Hai Yan Li
Keyword(s):  
Activated Carbon ◽  
Carbon Fiber ◽  
Specific Surface ◽  
Pore Size ◽  
Surface Area ◽  
Specific Surface Area ◽  
Raw Materials ◽  
Activated Carbon Fiber ◽  
Activation Process ◽  
Cobalt Salt

General purpose pitch-based carbon fiber (PCF) was pretreated with steam to develop pores on the surface of fiber. After immersed in cobalt salt solution, PCF was used as raw materials to prepare activated carbon fiber (ACF) through steam activation process. The effect of pretreatment of carbon fiber on specific surface area, mesopore volume and pore size distribution was investigated by N2 adsorption, and morphology of the resultant ACF was observed with scanning electron microscope(SEM). The results show that pretreatment of PCF enlarges specific surface area and mesopore ratio of ACF remarkably. The best ACF obtained in experiment is the one with specific surface area of 2670 m2/g and mesoporosity of 61.8%. Cobalt has evident catalysis in preparing ACF from activation of PCF, while specific surface area and pore size of ACF get smaller with cobalt salt immersion when pretreatment is too strong.

scholarly journals Surface oxidation of petroleum pitch to improve mesopore ratio and specific surface area of activated carbon

2021 ◽  
Vol 11 (1) ◽  
Author(s):  
Song Mi Lee ◽  
Seon Ho Lee ◽  
Doo-Hwan Jung
Keyword(s):  
Thermal Stability ◽  
Activated Carbon ◽  
Oxygen Uptake ◽  
Specific Surface ◽  
Pore Size ◽  
Surface Area ◽  
Specific Surface Area ◽  
Strong Influence ◽  
Surface Oxidation ◽  
Petroleum Pitch

AbstractIn this study, surface oxidation of petroleum pitch was performed to enhance the thermal stability, specific surface area, and mesopore ratio of activated carbon. The oxygen uptake of the pitch by surface oxidation has a strong influence on the formation of the specific surface area and pore size of activated carbon. It was confirmed that the oxygen uptake from the surface to the inner side of the surface oxidized pitch was the highest at the temperature of 330 °C (IP330-AC), with a mesopore ratio of 63.35% and specific surface area of 1811 m2 g−1. The oxygen content of the surface oxidized pitch increased proportionately with the mesopore ratio in activated carbon. The specific surface area and mesopore ratio of IP330-AC were respectively 163% and 487% higher than those of petroleum-based commercial activated carbon (A-BAC), and 102% and 491% higher than those of coconut-based commercial activated carbon (P60).

scholarly journals Experimental Study on Activated Carbon-MIL-101(Cr) Composites for Ethanol Vapor Adsorption

Materials ◽  
2021 ◽  
Vol 14 (14) ◽  
pp. 3811
Author(s):  
Zhongbao Liu ◽  
Jiayang Gao ◽  
Xin Qi ◽  
Zhi Zhao ◽  
Han Sun
Keyword(s):  
Activated Carbon ◽  
Specific Surface ◽  
Surface Area ◽  
Specific Surface Area ◽  
Ethanol Vapor ◽  
Future Application ◽  
Working Fluid ◽  
Relative Pressure ◽  
Adsorption Refrigeration ◽  
Vapor Adsorption

In this study, the hydrothermal method was used to synthesize MIL-101(Cr), and activated carbon (AC) with different content was incorporated in to MIL-101(Cr), thereby obtaining AC-MIL-101(Cr) composite material with a huge specific surface area. The physical properties of MIL-101(Cr) and AC-MIL-101(Cr) were characterized by powder X-ray diffraction (PXRD), scanning electron microscopy (SEM), thermogravimetric analysis (TGA), nitrogen adsorption and desorption and specific surface area testing, and ethanol vapor adsorption performance testing. The results show that with the increase of activated carbon content, the thermal stability of AC-MIL-101(Cr) is improved. Compared with the pure sample, the BET specific surface area and pore volume of AC-MIL-101(Cr) have increased; In the relative pressure range of 0–0.4, the saturated adsorption capacity of AC-MIL-101(Cr) to ethanol vapor decreases slightly. It is lower than MIL-101(Cr), but its adsorption rate is improved. Therefore, AC-MIL-101(Cr)/ethanol vapor has a good application prospect in adsorption refrigeration systems. The exploration of AC-MIL-101(Cr) composite materials in this paper provides a reference for the future application of carbon-based/MOFS composite adsorbent/ethanol vapor working fluid in adsorption refrigeration.

The relationship between geotechnical index properties and the pore-size distribution of compacted clayey silts

2015 ◽  
Vol 22 (6) ◽  
Author(s):  
Nazile Ural
Keyword(s):  
Specific Surface ◽  
Pore Size Distribution ◽  
Pore Size ◽  
Size Distribution ◽  
Surface Area ◽  
Specific Surface Area ◽  
Pore Volume ◽  
Correlation Coefficients ◽  
Liquid Limit ◽  
Index Properties

AbstractIn this study, the relationships between geotechnical index properties and the pore-size distribution of compacted natural silt and artificial soil mixtures, namely, silt with two different clays and three different clay percentages (10%, 20%, and 40%), were examined and compared. Atterberg’s limit tests, standard compaction tests, mercury intrusion porosimetry, X-ray diffraction, scanning electron microscopy (SEM) analysis, and Brunauer-Emmett-Teller specific surface analysis were conducted. The results show that the liquid limit, the cumulative pore volume, and specific surface area of artificially mixed soils increase with an increase in the percentage of clay. The cumulative pore volume and specific surface area with geotechnical index properties were compared. High correlation coefficients were observed between the specific areas and both the liquid limit and the plasticity index, as well as between the cumulative pore volume and both the clay percentage and the

Increase the Microporosity and CO2 Adsorption of a Commercial Activated Carbon

2015 ◽  
Vol 749 ◽  
pp. 17-21 ◽  
Author(s):  
Joanna Sreńscek Nazzal ◽  
Karolina Glonek ◽  
Jacek Młodzik ◽  
Urszula Narkiewicz ◽  
Antoni W. Morawski ◽  
...  
Keyword(s):  
Activated Carbon ◽  
Specific Surface ◽  
Surface Area ◽  
Specific Surface Area ◽  
Carbon Materials ◽  
Micropore Volume ◽  
Microporous Carbon ◽  
Microporous Carbons ◽  
Adsorption Capacities

Microporous carbons prepared from commercial activated carbon WG12 by KOH and/or ZnCl2 treatment were examined as adsorbents for CO2 capture. The micropore volume and specific surface area of the resulting carbons varied from 0.52 cm3/g (1374 m2/g) to 0.70 cm3/g (1800 m2/g), respectively. The obtained microporous carbon materials showed high CO2 adsorption capacities at 40 bar pressure reaching 16.4 mmol/g.

Study of the Porous Structure and High Adsorption Capacity of Biomass-Based Activated Carbon Prepared from Aspen Wood by Ferric Nitrate III Activation

2021 ◽  
Vol 15 (2) ◽  
pp. 131-144
Author(s):  
Chunjiang Jin ◽  
Huimin Chen ◽  
Luyuan Wang ◽  
Xingxing Cheng ◽  
Donghai An ◽  
...  
Keyword(s):  
Activated Carbon ◽  
Specific Surface ◽  
Adsorption Capacity ◽  
Surface Area ◽  
Specific Surface Area ◽  
Pore Volume ◽  
Mass Ratio ◽  
Aspen Wood ◽  
Surface Functional Groups ◽  
Wood Sawdust

In this study, aspen wood sawdust was used as the raw material, and Fe(NO3)3 and CO2 were used as activators. Activated carbon powder (ACP) was produced by the one-step physicochemical activation method in an open vacuum tube furnace. The effects of different mass ratios of Fe(NO3)3 and aspen wood sawdust on the pore structure of ACP were examined under single-variable experimental conditions. The mass ratio was 0–0.4. The detailed characteristics of ACP were examined by nitrogen adsorption, scanning electron microscopy, X-ray diffraction, and Fourier transform infrared spectroscopy. The adsorption capacity of ACP was established by simulating volatile organic compounds (VOCs) using ethyl acetate. The results showed that ACP has a good nanostructure with a large pore volume, specific surface area, and surface functional groups. The pore volume and specific surface area of Fe-AC-0.3 were 0.26 cm3/g and 455.36 m2/g, respectively. The activator played an important role in the formation of the pore structure and morphology of ACP. When the mass ratio was 0–0.3, the porosity increased linearly, but when it was higher than 0.3, the porosity decreased. For example, the pore volume and specific surface area of Fe-AC-0.4 reached 0.24 cm3/g and 430.87 m2/g, respectively. ACP presented good VOC adsorption performance. The Fe-AC-0.3 sample, which contained the most micropore structures, presented the best adsorption capacity for ethyl acetate at 712.58 mg/g. Under the action of the specific reaction products nitrogen dioxide (NO2) and oxygen, the surface of modified ACP samples showed different rich C/O/N surface functional groups, including C-H, C=C, C=O, C-O-C, and C-N.

Sign in / Sign up

Export Citation Format

Share Document