Redox Behavior of Palladium Ion in Oxide Glasses

1995 ◽  
Vol 412 ◽  
Author(s):  
Masaru Yamashita ◽  
Junji Nishii ◽  
Tomoko Akai ◽  
Hiroshi Yamanaka
Keyword(s):  
Raw Materials ◽  
Soda Lime ◽  
Metal Particles ◽  
Activity Measurement ◽  
Oxide Glasses ◽  
X Ray Diffraction ◽  
High Concentration ◽  
X Ray ◽  
Optical Absorbance ◽  
Electrochemical Oxygen

AbstractReduction and separation of Pd were investigated in soda-lime-alumino-borosilicate glass. The dependence on raw materials, melting atmosphere, concentration of Pd and melting temperature was examined by electrochemical oxygen activity measurement, optical absorbance, X-ray diffraction and microscopic observation. Pd ions were slowly reduced during melting and metal particles were formed. The separation was enhanced in a reducing atmosphere, at high temperature, for long melting periods and with high concentration of Pd. Pd metal particles of about 10 to 30 μm in diameter were observed by SEM and X-ray diffraction.

Cytomembrane Preservation in Tissue Dehydrated Only With Glutaraldehyde and Epon 812 Resin

1973 ◽  
Vol 31 ◽  
pp. 320-321
Author(s):  
Daniel C. Pease
Keyword(s):  
Diffraction Pattern ◽  
X Ray Diffraction ◽  
High Concentration ◽  
Unpublished Study ◽  
X Ray ◽  
Sectioned Material

A previous study demonstrated that tissue could be successfully infiltrated with 50% glutaraldehyde, and then subsequently polymerized with urea to create an embedment which retained cytomembrane lipids in sectioned material. As a result, the 180-190 Å periodicity characteristic of fresh, mammalian myelin was preserved in sections, as was a brilliant birefringence, and the capacity to bind OsO4 vapor in the hydrophobic bilayers. An associated (unpublished) study, carried out in co-operation with Drs. C.K. Akers and D.F. Parsons, demonstrated that the high concentration of glutaraldehyde (and urea) did not significantly alter the X-ray diffraction pattern of aldehyde-fixed, myelin. Thus, by itself, 50% glutaraldehyde has little effect upon cytomembrane systems and can be used with confidence for the first stages of dehydration.

scholarly journals X-ray and Neutron Study on the Structure of Hydrous SiO2 Glass up to 10 GPa

Minerals ◽  
2020 ◽  
Vol 10 (1) ◽  
pp. 84 ◽  
Author(s):  
Satoru Urakawa ◽  
Toru Inoue ◽  
Takanori Hattori ◽  
Asami Sano-Furukawa ◽  
Shinji Kohara ◽  
...  
Keyword(s):  
Oxide Glasses ◽  
Void Space ◽  
X Ray Diffraction ◽  
Amorphous Sio2 ◽  
Sio2 Glass ◽  
X Ray ◽  
X Ray Scattering ◽  
Medium Range ◽  
Two Phases ◽  
A Minor

The structure of hydrous amorphous SiO2 is fundamental in order to investigate the effects of water on the physicochemical properties of oxide glasses and magma. The hydrous SiO2 glass with 13 wt.% D2O was synthesized under high-pressure and high-temperature conditions and its structure was investigated by small angle X-ray scattering, X-ray diffraction, and neutron diffraction experiments at pressures of up to 10 GPa and room temperature. This hydrous glass is separated into two phases: a major phase rich in SiO2 and a minor phase rich in D2O molecules distributed as small domains with dimensions of less than 100 Å. Medium-range order of the hydrous glass shrinks compared to the anhydrous SiO2 glass by disruption of SiO4 linkage due to the formation of Si–OD deuterioxyl, while the response of its structure to pressure is almost the same as that of the anhydrous SiO2 glass. Most of D2O molecules are in the small domains and hardly penetrate into the void space in the ring consisting of SiO4 tetrahedra.

scholarly journals Waste and Solar Energy: An Eco-Friendly Way for Glass Melting

2021 ◽  
Vol 5 (2) ◽  
pp. 16
Author(s):  
Isabel Padilla ◽  
Maximina Romero ◽  
José I. Robla ◽  
Aurora López-Delgado
Keyword(s):  
Solar Energy ◽  
Environmental Sustainability ◽  
Raw Materials ◽  
Glass Melting ◽  
Glass Network ◽  
X Ray Diffraction ◽  
X Ray ◽  
Concentrated Solar Energy ◽  
Calcium Source ◽  
The Aluminum Industry

In this work, concentrated solar energy (CSE) was applied to an energy-intensive process such as the vitrification of waste with the aim of manufacturing glasses. Different types of waste were used as raw materials: a hazardous waste from the aluminum industry as aluminum source; two residues from the food industry (eggshell and mussel shell) and dolomite ore as calcium source; quartz sand was also employed as glass network former. The use of CSE allowed obtaining glasses in the SiO2-Al2O3-CaO system at exposure time as short as 15 min. The raw materials, their mixtures, and the resulting glasses were characterized by means of X-ray fluorescence, X-ray diffraction, and differential thermal analysis. The feasibility of combining a renewable energy, as solar energy and different waste for the manufacture of glasses, would highly contribute to circular economy and environmental sustainability.

scholarly journals Mining Wastes of an Albite Deposit as Raw Materials for Vitrified Mullite Ceramics

Minerals ◽  
2021 ◽  
Vol 11 (3) ◽  
pp. 232
Author(s):  
Pedro J. Sánchez-Soto ◽  
Eduardo Garzón ◽  
Luis Pérez-Villarejo ◽  
George N. Angelopoulos ◽  
Dolores Eliche-Quesada
Keyword(s):  
Particle Size ◽  
Raw Materials ◽  
Phase Evolution ◽  
Particle Size Analysis ◽  
Size Analysis ◽  
Mining Wastes ◽  
X Ray Diffraction ◽  
X Ray ◽  
Maximum Value

In this work, an examination of mining wastes of an albite deposit in south Spain was carried out using X-ray Fluorescence (XRF), X-ray diffraction (XRD), particle size analysis, thermo-dilatometry and Differential Thermal Analysis (DTA) and Thermogravimetric (TG) analysis, followed by the determination of the main ceramic properties. The albite content in two selected samples was high (65–40 wt. %), accompanied by quartz (25–40 wt. %) and other minor minerals identified by XRD, mainly kaolinite, in agreement with the high content of silica and alumina determined by XRF. The content of Na2O was in the range 5.44–3.09 wt. %, being associated with albite. The iron content was very low (<0.75 wt. %). The kaolinite content in the waste was estimated from ~8 to 32 wt. %. The particle size analysis indicated values of 11–31 wt. % of particles <63 µm. The ceramic properties of fired samples (1000–1350 °C) showed progressive shrinkage by the thermal effect, with water absorption and open porosity almost at zero at 1200–1250 °C. At 1200 °C, the bulk density reached a maximum value of 2.38 g/cm3. An abrupt change in the phase evolution by XRD was found from 1150 to 1200 °C, with the disappearance of albite by melting in accordance with the predictions of the phase diagram SiO2-Al2O3-Na2O and the system albite-quartz. These fired materials contained as main crystalline phases quartz and mullite. Quartz was present in the raw samples and mullite was formed by decomposition of kaolinite. The observation of mullite forming needle-shape crystals was revealed by Scanning Electron Microscopy (SEM). The formation of fully densified and vitrified mullite materials by firing treatments was demonstrated.

scholarly journals Ti/RuO2-IrO2-SnO2 Anode for Electrochemical Degradation of Pollutants in Pharmaceutical Wastewater: Optimization and Degradation Performances

2020 ◽  
Vol 13 (1) ◽  
pp. 126
Author(s):  
Guozhen Zhang ◽  
Xingxing Huang ◽  
Jinye Ma ◽  
Fuping Wu ◽  
Tianhong Zhou
Keyword(s):  
Removal Rate ◽  
Inorganic Compounds ◽  
Oxide Coating ◽  
X Ray Diffraction ◽  
Pharmaceutical Wastewater ◽  
High Concentration ◽  
Dimensionally Stable Anodes ◽  
X Ray ◽  
Initial Ph ◽  
Cod Removal Rate

Electrochemical oxidation technology is an effective technique to treat high-concentration wastewater, which can directly oxidize refractory pollutants into simple inorganic compounds such as H2O and CO2. In this work, two-dimensionally stable anodes, Ti/RuO2-IrO2-SnO2, have been developed in order to degrade organic pollutants from pharmaceutical wastewater. Characterization by scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDS), and X-ray diffraction (XRD) showed that the oxide coating was successfully fabricated on the Ti plate surface. Electrocatalytic oxidation conditions of high concentration pharmaceutical wastewater was discussed and optimized, and the best results showed that the COD removal rate was 95.92% with the energy consumption was 58.09 kW·h/kgCOD under the electrode distance of 3 cm, current density of 8 mA/cm2, initial pH of 2, and air flow of 18 L/min.

scholarly journals Leaching Titaniferous Magnetite Concentrate by Alkaline Aqueous Solution

2021 ◽  
Author(s):  
Ke Guo ◽  
Shaoyan Wang ◽  
Renfeng Song ◽  
Zhiqiang Zhang
Keyword(s):  
Aqueous Solution ◽  
Alkali Concentration ◽  
Water Usage ◽  
X Ray Diffraction ◽  
High Concentration ◽  
X Ray ◽  
Iron Concentrate ◽  
Titaniferous Magnetite ◽  
Magnetite Concentrate ◽  
Kinetics Of

AbstractLeaching titaniferous magnetite concentrate with alkali solution of high concentration under high temperature and high pressure was utilized to improve the grade of iron in iron concentrate and the grade of TiO2 in titanium tailings. The titaniferous magnetite concentrate in use contained 12.67% TiO2 and 54.01% Fe. The thermodynamics of the possible reactions and the kinetics of leaching process were analyzed. It was found that decomposing FeTiO3 with NaOH aqueous solution could be carried out spontaneously and the reaction rate was mainly controlled by internal diffusion. The effects of water usage, alkali concentration, reaction time, and temperature on the leaching procedure were inspected, and the products were characterized by X-ray diffraction, scanning electron microscope, and energy dispersive spectroscopy, respectively. After NaOH leaching and magnetic separation, the concentrate, with Fe purity of 65.98% and Fe recovery of 82.46%, and the tailings, with TiO2 purity of 32.09% and TiO2 recovery of 80.79%, were obtained, respectively.

Facile Solid State Method Route Synthesis and Enhance Visible Light Activities of BiVO4 by Doping Co

2016 ◽  
Vol 703 ◽  
pp. 316-320
Author(s):  
Hai Feng Chen ◽  
Jing Ling Hu ◽  
Bing Xu
Keyword(s):  
Solid State ◽  
Visible Light ◽  
Catalytic Effect ◽  
Catalytic Properties ◽  
Raw Materials ◽  
X Ray Diffraction ◽  
Solid State Method ◽  
Illumination Time ◽  
X Ray ◽  
State Method

Using NH4VO3, Bi (NO3)3•5H2O and Co (NO3)2•6H2O as raw materials, Co doped BiVO4 (Co/BiVO4) photocatalysts were successfully prepared by solid state method. And the photo catalytic properties were test in this work. Crystal structures of these samples were characterized by X-ray diffraction (XRD). The Methyl Orange (MO) was simulated as the sewage under the visible light to explorer the influence of the illumination time and the mass of photocatalyst. The visible-light absorption spectrum of BiVO4 was broadening with doping Co. It was found that the Co/BiVO4 had higher photocatalytic activity than pure BiVO4 .The reason of enhanced catalytic effect also had been analyzed and discussed in the article.

The Roman Ceramics of Salobrena (Granada-Spain) and their Raw Materials

1992 ◽  
Vol 267 ◽  
Author(s):  
Ana M De Andres ◽  
Isabel MuÑOZ
Keyword(s):  
Thermal Analysis ◽  
Differential Thermal Analysis ◽  
Raw Materials ◽  
Third Century ◽  
Western Coast ◽  
X Ray Diffraction ◽  
X Ray ◽  
The Third ◽  
Good Number ◽  
Scanning Electron

ABSTRACTNineteen roman ceramic sherds found near Salobreña (Granada, Spain), in the western coast of the Mediterranean Sea, as well as different ceramic clays from the surroundingsare studied. Both clays and ceramic sherds are characterizad by X-ray diffraction and spectrometry, differential thermal analysis, and scanning electron and optical microscopies. A good number of the ceramic pieces, among which some “Terrae Sigillatae”, have a composition similar to that of the local clays and, thus, have been probably manufactured at Salobreña. Only a few of them have a foreign origin. For most of them, the firing temperature was about 800-850 °C, although some have been produced at 900-1000 °C, and some others at 1000-1100 °C. It is concluded that Salobreña appearsto have been an important settlement just in the third century of the Christian era.

Magnetic Properties of Bulk Zn0.95-XMnXFe0.05O2 Prepared by Sol-Gel Method and Subsequent Hot Pressing

2011 ◽  
Vol 268-270 ◽  
pp. 356-359 ◽  
Author(s):  
Wen Song Lin ◽  
C. H. Wen ◽  
Liang He
Keyword(s):  
Magnetic Properties ◽  
Photoelectron Spectroscopy ◽  
Raw Materials ◽  
Sol Gel ◽  
Secondary Phase ◽  
X Ray Diffraction ◽  
Gel Method ◽  
X Ray ◽  
Sol Gel Method ◽  
Doped Zno

Mn, Fe doped ZnO powders (Zn0.95-xMnxFe0.05O2, x≤0.05) were synthesized by an ameliorated sol-gel method, using Zn(CH3COO)2, Mn(CH3COO)2and FeCl2as the raw materials, with the addition of vitamin C as a kind of chemical reducer. The resulting powder was subsequently compacted under pressure of 10 MPa at the temperature of 873K in vacuum. The crystal structure and magnetic properties of Zn0.95-xMnxFe0.05O2powder and bulk samples have been investigated by X-ray diffraction (XRD) and vibrating sample magnetometer (VSM). X-ray photoelectron spectroscopy (XPS) was used to study chemical valence of manganese, iron and zinc in the samples. The x-ray diffraction (XRD) results showed that Zn0.95-xMnxFe0.05O (x≤0.05) samples were single phase with the ZnO-like wurtzite structure. No secondary phase was found in the XRD spectrum. X-ray photoelectron spectroscopy (XPS) showed that Fe and Mn existed in Zn0.95-xMnxFe0.05O2samples in Fe2+and Mn2+states. The results of VSM experiment proved the room temperature ferromagnetic properties (RTFP) of Mn, Fe co-doped ZnO samples.

Solvothermal Synthesis of Bi2Se3 Hexagonal Nanosheet Crystals

2011 ◽  
Vol 236-238 ◽  
pp. 1712-1716 ◽  
Author(s):  
Hai Tao Liu ◽  
Jun Dai ◽  
Jia Jia Zhang ◽  
Wei Dong Xiang
Keyword(s):  
Electron Microscope ◽  
Solvothermal Synthesis ◽  
Solvothermal Method ◽  
Raw Materials ◽  
X Ray Diffraction ◽  
Uniform Size ◽  
X Ray ◽  
Selected Area Electron Diffraction ◽  
Transmission Electron ◽  
Scanning Electron

Bismuth selenide (Bi2Se3) hexagonal nanosheet crystals with uniform size were successfully prepared via a solvothermal method at 160°C for 22 h using bismuth trichloride(BiCl3) and selenium powder(Se) as raw materials, sodium bisulfite(NaHSO3) as a reducing agent, diethylene glycol(DEG) as solvent, and ammonia as pH regulator. Various techniques such as X-ray diffraction (XRD), field-emission scanning electron microscope (FESEM), high-resolution transmission electron microscope (HRTEM), and selected area electron diffraction (SAED) were used to characterize the obtained products. Results show that the as-synthesized samples are pure Bi2Se3 hexagonal nanosheet crystals. A possible growth mechanism for Bi2Se3 hexagonal nanosheet crystals is also discussed based on the experiment.

Sign in / Sign up

Export Citation Format

Share Document