Fiber Push-Out Testing of Intermetallic Matrix Composites at Elevated Temperatures

1992 ◽  
Vol 273 ◽  
Author(s):  
Jeffrey I. Eldridge
Keyword(s):  
Residual Stresses ◽  
Metal Matrix Composites ◽  
Metal Matrix ◽  
Elevated Temperatures ◽  
Matrix Composites ◽  
Fiber Reinforced ◽  
Intermetallic Matrix ◽  
Intermetallic Matrix Composites ◽  
Increasing Temperature ◽  
Push Out

ABSTRACTA newly developed apparatus for performing fiber push-out testing at elevated temperatures has been applied towards testing fiber-reinforced intermetallic and metal matrix composites. This new capability shows the effects of the relief of residual stresses and increased matrix ductility with increasing temperature on fiber debonding and sliding behavior.

scholarly journals Tensile and fatigue properties of fiber-reinforced metal matrix composites Cf/5056Al

2021 ◽  
Vol 30 ◽  
pp. 2633366X2092971
Author(s):  
Ying Ba ◽  
Shu Sun
Keyword(s):  
Metal Matrix Composites ◽  
Metal Matrix ◽  
High Strength ◽  
Longitudinal Direction ◽  
Fatigue Properties ◽  
Matrix Composites ◽  
Weak Interface ◽  
Fiber Reinforced ◽  
Alloy Matrix ◽  
Medium Strength

Fiber-reinforced metal matrix composites have mechanical properties highly dependent on directions, possessing high strength and fatigue resistance in fiber longitudinal direction achieved by weak interface bonding. However, the disadvantage of weak interface combination is the reduction of transversal performances. In this article, tensile and fatigue properties of carbon fiber-reinforced 5056 aluminum alloy matrix (Cf/5056Al) composite under the condition of medium-strength interface combination are carried out. The fatigue damage mechanisms of Cf/5056Al composite under tension–tension and tension–compression loads are not the same, but the fatigue life curves are close, which may be the result of the medium-strength interface combination.

Damage of Short-Fiber-Reinforced Metal Matrix Composites Considering Cooling and Thermal Cycling

1999 ◽  
Vol 122 (2) ◽  
pp. 203-208 ◽  
Author(s):  
Chuwei Zhou ◽  
Wei Yang ◽  
Daining Fang
Keyword(s):  
Thermal Cycling ◽  
Metal Matrix Composites ◽  
Stress Drop ◽  
Metal Matrix ◽  
Failure Modes ◽  
Short Fiber ◽  
Uniaxial Tensile ◽  
Matrix Composites ◽  
Fiber Reinforced ◽  
Matrix Damage

Mechanical properties and damage evolution of short-fiber-reinforced metal matrix composites (MMC) are studied under a micromechanics model accounting for the history of cooling and thermal cycling. A cohesive interface is formulated in conjunction with the Gurson-Tvergaard matrix damage model. Attention is focused on the residual stresses and damages by the thermal mismatch. Substantial stress drop in the uniaxial tensile response is found for a computational cell that experienced a cooling process. The stress drop is caused by debonding along the fiber ends. Subsequent thermal cycling lowers the debonding stress and the debonding strain. Micromechanics analysis reveals three failure modes. When the thermal histories are ignored, the cell fails by matrix damage outside the fiber ends. With the incorporation of cooling, the cell fails by fiber end debonding and the subsequent transverse matrix damage. When thermal cycling is also included, the cell fails by jagged debonding around the fiber tops followed by necking instability of matrix ligaments. [S0094-4289(00)01202-0]

Sign in / Sign up

Export Citation Format

Share Document