Mechanical Properties of SiO2 vs. SiO2-TiO2 Bulk Glasses and Fibers

1991 ◽  
Vol 244 ◽  
Author(s):  
Suresh T. Gulati
Keyword(s):  
Mechanical Properties ◽  
Optical Fibers ◽  
Mechanical Performance ◽  
Fatigue Behavior ◽  
Deformation Mode ◽  
Strength Distribution ◽  
Fused Silica ◽  
Space Applications ◽  
Silica Glasses ◽  
Silica And Titania

ABSTRACTThe mechanical properties of silica and titania-doped silica glasses, in bulk and fiber forms, are presented. These include the elastic properties (E and ν), strength distribution (in tension and bending), fatigue behavior (dynamic and static loading) and fracture toughness. Following a brief review of above properties for fused silica and ULE™ glasses (Coming Codes 7940 and 7971), used primarily for space applications, the mechanical properties data for silica and titania-doped silica-clad optical fibers are presented. The enhancement of mechanical performance of titania-doped silica clad fiber is also discussed.The effect of titania doping on fundamental properties like stress-free activation energy, crack tip pH, and deformation mode of Si-O-Si bond is discussed. In addition, the crack velocity data obtained from DCDC specimens of homogeneous silica and titania-doped silica glasses are compared in an attempt to understand the role titania plays in improving the fatigue resistance of optical fibers.

scholarly journals A Minireview of the Natures of Radiation-Induced Point Defects in Pure and Doped Silica Glasses and Their Visible/Near-IR Absorption Bands, with Emphasis on Self-Trapped Holes and How They Can Be Controlled

2013 ◽  
Vol 2013 ◽  
pp. 1-14 ◽  
Author(s):  
David L. Griscom
Keyword(s):  
Dose Rate ◽  
Optical Fibers ◽  
Point Defects ◽  
Ir Absorption ◽  
Absorption Bands ◽  
Space Applications ◽  
Ambient Temperatures ◽  
Silica Glasses ◽  
Near Ir ◽  
Radiation Induced

The natures of most radiation-induced point defects in amorphous silicon dioxide (a-SiO2) are well known on the basis of 56 years of electron spin resonance (ESR) and optical studies of pure and doped silica glass in bulk, thin-film, and fiber-optic forms. Many of the radiation-induced defects intrinsic to pure and B-, Al-, Ge-, and P-doped silicas are at least briefly described here and references are provided to allow the reader to learn still more about these, as well as some of those defects not mentioned. The metastable self-trapped holes (STHs), intrinsic to both doped and undoped silicas, are argued here to be responsible for most transient red/near-IR optical absorption bands induced in low-OH silica-based optical fibers by ionizing radiations at ambient temperatures. However, accelerated testing of a-SiO2-based optical devices slated for space applications must take into account the highly supralinear dependence on ionizing-dose-rate of the initial STH creation rate, which if not recognized would lead to false negatives. Fortunately, however, it is possible to permanently reduce the numbers of environmentally or operationally created STHs by long-term preirradiation at relatively low dose rates. Finally, emphasis is placed on the importance and utility of rigorously derived fractal-kinetic formalisms that facilitate reliable extrapolation of radiation-induced optical attenuations in silica-based photonics recorded as functions of dose rate backward into time domains unreachable in practical laboratory times and forward into dose-rate regimes for which there are no present-day laboratory sources.

scholarly journals A New Approach in the Design of Microstructured Ultralight Components to Achieve Maximum Functional Performance

Materials ◽  
2021 ◽  
Vol 14 (7) ◽  
pp. 1588
Author(s):  
Amaia Calleja-Ochoa ◽  
Haizea Gonzalez-Barrio ◽  
Norberto López de Lacalle ◽  
Silvia Martínez ◽  
Joseba Albizuri ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Additive Manufacturing ◽  
Mechanical Performance ◽  
Functional Performance ◽  
Minimum Weight ◽  
Turbine Blades ◽  
High Ratio ◽  
Metal Powders ◽  
Space Applications ◽  
New Approach

In the energy and aeronautics industry, some components need to be very light but with high strength. For instance, turbine blades and structural components under rotational centrifugal forces, or internal supports, ask for low weight, and in general, all pieces in energy turbine devices will benefit from weight reductions. In space applications, a high ratio strength/weight is even more important. Light components imply new optimal design concepts, but to be able to be manufactured is the real key enable technology. Additive manufacturing can be an alternative, applying radical new approaches regarding part design and components’ internal structure. Here, a new approach is proposed using the replica of a small structure (cell) in two or three orders of magnitude. Laser Powder Bed Fusion (L-PBF) is one of the most well-known additive manufacturing methods of functional parts (and prototypes as well), for instance, starting from metal powders of heat-resistant alloys. The working conditions for such components demand high mechanical properties at high temperatures, Ni-Co superalloys are a choice. The work here presented proposes the use of “replicative” structures in different sizes and orders of magnitude, to manufacture parts with the minimum weight but achieving the required mechanical properties. Printing process parameters and mechanical performance are analyzed, along with several examples.

Mechanical properties and fatigue behavior of CO2 laser beam welded armor steel joints

2020 ◽  
Vol 62 (7) ◽  
pp. 689-697
Author(s):  
Zulkuf Balalan ◽  
Furkan Sarsilmaz ◽  
Omer Ekinci
Keyword(s):  
Mechanical Properties ◽  
Laser Beam ◽  
Co2 Laser ◽  
Fatigue Behavior ◽  
Armor Steel ◽  
Steel Joints

Weldability - Behavior of Welded Reinforcement

2019 ◽  
Vol 70 (10) ◽  
pp. 3469-3472
Keyword(s):  
Mechanical Properties ◽  
Chemical Composition ◽  
Mechanical Characteristics ◽  
Mechanical Performance ◽  
Current Work ◽  
Carbon Equivalent ◽  
Work Process ◽  
Ultimate Limit

Weldability involves two aspects: welding behavior of components and safety in operation. The two aspects will be reduced to the mechanical characteristics of the elements and to the chemical composition. In the case of steel reinforcing rebar’s, it is reduces to the percentage of Cech(carbon equivalent) and to the mechanical characteristics: the yielding limit, the ultimate limit, and the elongations which after that represent the ductility class in which the re-bars is framed. The paper will present some types of steel reinforcing rebar’s with its mechanical characteristics and the welding behavior of those elements. In the current work, process-related behavior of welded reinforcement, joint local and global mechanical properties, and their correlation with behavior of normal reinforcement and also the mechanical performance resulted in this type of joints. Keywords: welding behavior, ultimate limit, reinforcing rebar’s

scholarly journals Preparation of Long Sisal Fiber-Reinforced Polylactic Acid Biocomposites with Highly Improved Mechanical Performance

Polymers ◽  
2021 ◽  
Vol 13 (7) ◽  
pp. 1124
Author(s):  
Zhifang Liang ◽  
Hongwu Wu ◽  
Ruipu Liu ◽  
Caiquan Wu
Keyword(s):  
Mechanical Properties ◽  
Polylactic Acid ◽  
Mechanical Performance ◽  
Tensile Elongation ◽  
Sisal Fiber ◽  
Fiber Reinforced ◽  
Impact Performance ◽  
The Matrix ◽  
Blending Process ◽  
Extension Direction

Green biodegradable plastics have come into focus as an alternative to restricted plastic products. In this paper, continuous long sisal fiber (SF)/polylactic acid (PLA) premixes were prepared by an extrusion-rolling blending process, and then unidirectional continuous long sisal fiber-reinforced PLA composites (LSFCs) were prepared by compression molding to explore the effect of long fiber on the mechanical properties of sisal fiber-reinforced composites. As a comparison, random short sisal fiber-reinforced PLA composites (SSFCs) were prepared by open milling and molding. The experimental results show that continuous long sisal fiber/PLA premixes could be successfully obtained from this pre-blending process. It was found that the presence of long sisal fibers could greatly improve the tensile strength of LSFC material along the fiber extension direction and slightly increase its tensile elongation. Continuous long fibers in LSFCs could greatly participate in supporting the load applied to the composite material. However, when comparing the mechanical properties of the two composite materials, the poor compatibility between the fiber and the matrix made fiber’s reinforcement effect not well reflected in SSFCs. Similarly, the flexural performance and impact performance of LSFCs had been improved considerably versus SSFCs.

scholarly journals Tribological and Mechanical Properties of Multicomponent CrVTiNbZr(N) Coatings

Coatings ◽  
2021 ◽  
Vol 11 (1) ◽  
pp. 41
Author(s):  
Yin-Yu Chang ◽  
Cheng-Hsi Chung
Keyword(s):  
Mechanical Properties ◽  
Nitrogen Content ◽  
Adhesion Strength ◽  
Mechanical Performance ◽  
Bulk Material ◽  
High Entropy Alloy ◽  
Composition Gradient ◽  
Multilayered Structures ◽  
High Entropy ◽  
Alloy Target

Multi-element material coating systems have received much attention for improving the mechanical performance in industry. However, they are still focused on ternary systems and seldom beyond quaternary ones. High entropy alloy (HEA) bulk material and thin films are systems that are each comprised of at least five principal metal elements in equally matched proportions, and some of them are found possessing much higher strength than traditional alloys. In this study, CrVTiNbZr high entropy alloy and nitrogen contained CrVTiNbZr(N) nitride coatings were synthesized using high ionization cathodic-arc deposition. A chromium-vanadium alloy target, a titanium-niobium alloy target and a pure zirconium target were used for the deposition. By controlling the nitrogen content and cathode current, the CrNbTiVZr(N) coating with gradient or multilayered composition control possessed different microstructures and mechanical properties. The effect of the nitrogen content on the chemical composition, microstructure and mechanical properties of the CrVTiNbZr(N) coatings was investigated. Compact columnar microstructure was obtained for the synthesized CrVTiNbZr(N) coatings. The CrVTiNbZrN coating (HEAN-N165), which was deposited with nitrogen flow rate of 165 standard cubic centimeters per minute (sccm), exhibited slightly blurred columnar and multilayered structures containing CrVN, TiNbN and ZrN. The design of multilayered CrVTiNbZrN coatings showed good adhesion strength. Improvement of adhesion strength was obtained with composition-gradient interlayers. The CrVTiNbZrN coating with nitrogen content higher than 50 at.% possessed the highest hardness (25.2 GPa) and the resistance to plastic deformation H3/E*2 (0.2 GPa) value, and therefore the lowest wear rate was obtained because of high abrasion wear resistance.

Experimental investigation of the mechanical behavior of glass fiber/high fluidity polyamide-based composites for automotive market

2021 ◽  
pp. 073168442110140
Author(s):  
Hossein Ramezani-Dana ◽  
Moussa Gomina ◽  
Joël Bréard ◽  
Gilles Orange
Keyword(s):  
Mechanical Properties ◽  
Glass Fiber ◽  
Mechanical Performance ◽  
Physical And Mechanical Properties ◽  
Ultimate Strain ◽  
Uniaxial Tensile ◽  
Compression Tests ◽  
Automotive Market ◽  
Glass Fiber Reinforced ◽  
Glass Fiber Reinforcement

In this work, we examine the relationships between the microstructure and the mechanical properties of glass fiber–reinforced polyamide 6,6 composite materials ( V f = 54%). These materials made by thermocompression incorporate different grades of high fluidity polyamide-based polymers and two types of quasi-UD glass fiber reinforcement. One is a classic commercial fabric, while the other specially designed and manufactured incorporates weaker tex glass yarns (the spacer) to increase the planar permeability of the preform. The effects of the viscosity of the polymers and their composition on the wettability of the reinforcements were analyzed by scanning electron microscopy observations of the microstructure. The respective influences of the polymers and the spacer on the mechanical performance were determined by uniaxial tensile and compression tests in the directions parallel and transverse to the warp yarns. Not only does the spacer enhance permeability but it also improves physical and mechanical properties: tensile longitudinal Young’s modulus increased from 38.2 GPa to 42.9 GPa (13% growth), tensile strength increased from 618.9 MPa to 697 MPa (3% growth), and decrease in ultimate strain from 1.8% to 1.7% (5% reduction). The correlation of these results with the damage observed post mortem confirms those acquired from analyses of the microstructure of composites and the rheological behaviors of polymers.

scholarly journals Effects of a Twin-Screw Extruder Equipped with a Molten Resin Reservoir on the Mechanical Properties and Microstructure of Recycled Waste Plastic Polyethylene Pellet Moldings

Polymers ◽  
2021 ◽  
Vol 13 (7) ◽  
pp. 1058
Author(s):  
Hikaru Okubo ◽  
Haruka Kaneyasu ◽  
Tetsuya Kimura ◽  
Patchiya Phanthong ◽  
Shigeru Yao
Keyword(s):  
Mechanical Properties ◽  
Mechanical Performance ◽  
Value Added ◽  
Industrial Applications ◽  
Twin Screw Extruder ◽  
Screw Extruder ◽  
Polymer Properties ◽  
Wide Range ◽  
Twin Screw ◽  
Recycled Plastics

Each year, increasing amounts of plastic waste are generated, causing environmental pollution and resource loss. Recycling is a solution, but recycled plastics often have inferior mechanical properties to virgin plastics. However, studies have shown that holding polymers in the melt state before extrusion can restore the mechanical properties; thus, we propose a twin-screw extruder with a molten resin reservoir (MSR), a cavity between the screw zone and twin-screw extruder discharge, which retains molten polymer after mixing in the twin-screw zone, thus influencing the polymer properties. Re-extruded recycled polyethylene (RPE) pellets were produced, and the tensile properties and microstructure of virgin polyethylene (PE), unextruded RPE, and re-extruded RPE moldings prepared with and without the MSR were evaluated. Crucially, the elongation at break of the MSR-extruded RPE molding was seven times higher than that of the original RPE molding, and the Young’s modulus of the MSR-extruded RPE molding was comparable to that of the virgin PE molding. Both the MSR-extruded RPE and virgin PE moldings contained similar striped lamellae. Thus, MSR re-extrusion improved the mechanical performance of recycled polymers by optimizing the microstructure. The use of MSRs will facilitate the reuse of waste plastics as value-added materials having a wide range of industrial applications.

scholarly journals Microstructure and Mechanical Performance of Resistance Spot Welded Martensitic Advanced High Strength Steel

Processes ◽  
2021 ◽  
Vol 9 (6) ◽  
pp. 1021
Author(s):  
Yunzhao Li ◽  
Huaping Tang ◽  
Ruilin Lai
Keyword(s):  
Mechanical Properties ◽  
Failure Modes ◽  
Mechanical Performance ◽  
Strong Dependence ◽  
High Strength ◽  
Weld Nugget ◽  
Resistance Spot ◽  
Pull Out ◽  
Cross Tension ◽  
Spot Welded

Resistance spot welded 1.2 mm (t)-thick 1400 MPa martensitic steel (MS1400) samples are fabricated and their microstructure, mechanical properties are investigated thoroughly. The mechanical performance and failure modes exhibit a strong dependence on weld-nugget size. The pull-out failure mode for MS1400 steel resistance spot welds does not follow the conventional weld-nugget size recommendation criteria of 4t0.5. Significant softening was observed due to dual phase microstructure of ferrite and martensite in the inter-critical heat affected zone (HAZ) and tempered martensite (TM) structure in sub-critical HAZ. However, the upper-critical HAZ exhibits obvious higher hardness than the nugget zone (NZ). In addition, the mechanical properties show that the cross-tension strength (CTS) is about one quarter of the tension-shear strength (TSS) of MS1400 weld joints, whilst the absorbed energy of cross-tension and tension-shear are almost identical.

scholarly journals Functional Bionanocomposite Fibers of Chitosan Filled with Cellulose Nanofibers Obtained by Gel Spinning

Polymers ◽  
2021 ◽  
Vol 13 (10) ◽  
pp. 1563
Author(s):  
Sofia Marquez-Bravo ◽  
Ingo Doench ◽  
Pamela Molina ◽  
Flor Estefany Bentley ◽  
Arnaud Kamdem Tamo ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Mechanical Performance ◽  
Cellulose Nanofibers ◽  
Microstructural Characterization ◽  
Fiber Formation ◽  
Fiber Direction ◽  
Composite Fibers ◽  
X Ray Diffraction ◽  
Gel Spinning ◽  
X Ray

Extremely high mechanical performance spun bionanocomposite fibers of chitosan (CHI), and cellulose nanofibers (CNFs) were successfully achieved by gel spinning of CHI aqueous viscous formulations filled with CNFs. The microstructural characterization of the fibers by X-ray diffraction revealed the crystallization of the CHI polymer chains into anhydrous chitosan allomorph. The spinning process combining acidic–basic–neutralization–stretching–drying steps allowed obtaining CHI/CNF composite fibers of high crystallinity, with enhanced effect at incorporating the CNFs. Chitosan crystallization seems to be promoted by the presence of cellulose nanofibers, serving as nucleation sites for the growing of CHI crystals. Moreover, the preferential orientation of both CNFs and CHI crystals along the spun fiber direction was revealed in the two-dimensional X-ray diffraction patterns. By increasing the CNF amount up to the optimum concentration of 0.4 wt % in the viscous CHI/CNF collodion, Young’s modulus of the spun fibers significantly increased up to 8 GPa. Similarly, the stress at break and the yield stress drastically increased from 115 to 163 MPa, and from 67 to 119 MPa, respectively, by adding only 0.4 wt % of CNFs into a collodion solution containing 4 wt % of chitosan. The toughness of the CHI-based fibers thereby increased from 5 to 9 MJ.m−3. For higher CNFs contents like 0.5 wt %, the high mechanical performance of the CHI/CNF composite fibers was still observed, but with a slight worsening of the mechanical parameters, which may be related to a minor disruption of the CHI matrix hydrogel network constituting the collodion and gel fiber, as precursor state for the dry fiber formation. Finally, the rheological behavior observed for the different CHI/CNF viscous collodions and the obtained structural, thermal and mechanical properties results revealed an optimum matrix/filler compatibility and interface when adding 0.4 wt % of nanofibrillated cellulose (CNF) into 4 wt % CHI formulations, yielding functional bionanocomposite fibers of outstanding mechanical properties.

Sign in / Sign up

Export Citation Format

Share Document