Interdiffusion Kinetics and Magnetic Properties of TA-Permalloy Multilayers

1991 ◽  
Vol 232 ◽  
Author(s):  
I. Hashim ◽  
H. A. Atwater ◽  
K. T. Y. Kung ◽  
R. M. Valletta
Keyword(s):  
Magnetic Properties ◽  
Isothermal Annealing ◽  
Lattice Diffusion ◽  
X Ray Diffraction ◽  
X Ray ◽  
Transmission Electron ◽  
Short Period ◽  
Interface Roughening ◽  
Interdiffusion Kinetics ◽  
Kinetics Of

ABSTRACTThe interdiffusion kinetics of ultrahigh vacuum deposited Ta/Ni81Fe19 short-period multilayers films have been investigated, and changes in microstructure were related to magnetic properties. Small angle X-ray diffraction and transmission electron microscopy were used to study layer morphology evolution and interdiffusion during post-growth isothermal annealing in the temperature range 300 – 600°C. The kinetic analysis suggests that interface roughening due to grain growth, and grain-boundary mediated diffusion of Ta occurs concurrently at early anneal times in the Ni81Fe19 films. Subsequent grainboundary and lattice diffusion of Ta lead to a reduction of magnetization and increase in coercivity of Ni81Fe19.

Effect of Nitridation Magnetic Properties of Nanocrystalline Fe-Co Alloy Powders

2010 ◽  
Vol 654-656 ◽  
pp. 1106-1109
Author(s):  
Ya Qiong He ◽  
Chang Hui Mao ◽  
Jian Yang
Keyword(s):  
Grain Size ◽  
Magnetic Properties ◽  
Alloy Powder ◽  
High Energy ◽  
X Ray Diffraction ◽  
Powder Mixtures ◽  
X Ray ◽  
Transmission Electron ◽  
Nitridation Temperature ◽  
Microstructure And Magnetic Properties

Nanocrystalline Fe-Co alloy powders, which were prepared by high-energy mechanical milling, were nitrided under the mixing gas of NH3/H2 in the temperature range from 380°C to 510°C. X-ray diffraction (XRD) was used to analyze the grain size and reaction during the processing. The magnetic properties of the nitrided powders were measured by Vibrating Sample Magnetometer (VSM). The results show that with the appearance of Fe4N phase after nitride treatment, and the grain-size of FeCo phase decreases with the increase of nitridation temperature between 380°C to 450°C.The saturation magnetization of nitrided alloy powder treated at 480°C is about 18% higher than that of the initial Fe-Co alloy powder, accompanied by the reduction of the coercivity. Transmission electron microscope (TEM) was used, attempting to further analyze the effect of Fe4N phase on microstructure and magnetic properties of the powder mixtures.

Influence of Alloying Additions on Enhancement of Soft Magnetic Properties Effect and Crystallization in FeXSiB (X=Cu, V, Co, Zr, Nb) Amorphous Alloys

2007 ◽  
Vol 130 ◽  
pp. 171-174 ◽  
Author(s):  
Z. Stokłosa ◽  
G. Badura ◽  
P. Kwapuliński ◽  
Józef Rasek ◽  
G. Haneczok ◽  
...  
Keyword(s):  
Magnetic Properties ◽  
Amorphous Alloys ◽  
Crystallization Process ◽  
Annealing Temperature ◽  
Magnetic Measurements ◽  
X Ray Diffraction ◽  
Soft Magnetic ◽  
X Ray ◽  
Second Stage ◽  
Transmission Electron

The crystallization and optimization of magnetic properties effects in FeXSiB (X=Cu, V, Co, Zr, Nb) amorphous alloys were studied by applying X-ray diffraction methods, high resolution transmission electron microscopy (HRTEM), resistometric and magnetic measurements. The temperatures of the first and the second stage of crystallization, the 1h optimization annealing temperature and the Curie temperature were determined for different amorphous alloys. Activation energies of crystallization process were obtained by applying the Kissinger method. The influence of alloy additions on optimization effect and crystallization processes was carefully examined.

Nickel Ferrite: Combustion Synthesis, Characterization and Magnetic Properties

2005 ◽  
Vol 498-499 ◽  
pp. 618-623 ◽  
Author(s):  
Ana Cristina Figueiredo de Melo Costa ◽  
Lucianna Gama ◽  
M.R. Morelli ◽  
Ruth Herta Goldsmith Aliaga Kiminami
Keyword(s):  
Magnetic Properties ◽  
Nickel Ferrite ◽  
High Speed ◽  
High Specific Surface Area ◽  
Line Broadening ◽  
X Ray Diffraction ◽  
X Ray ◽  
Railway Systems ◽  
Transmission Electron ◽  
Dry Pressing

Nanosized spinel nickel ferrite particles have attracted considerable attention and efforts continue to investigate them for their technological importance to the microwave industries, high speed digital tap or disk recording, repulsive suspension for use in levitated railway systems, ferrofluids, catalysis and magnetic refrigeration systems. Nanosize nickel ferrite powders (NiFe2O4) have been prepared by combustion reaction using nitrates and urea as fuel. The resulting powders were characterized by X-ray diffraction (XRD), BET, and transmission electron microscopy (TEM). The results showed nanosize nickel ferrite powders with high specific surface area (55.21 m2/g). The powders showed extensive XRD line broadening and the crystallite size calculated from the XRD line broadening was 18.0 nm. The samples were uniaxially compacted by dry pressing, sintered at 1200°C/2h and characterized by bulk density, SEM and magnetic properties measurements. The samples showed uniform microstructures with grain size of 4.45 μm, maximum flux density of 0.18T, field coercive of the 488 A/m, and hysteresis loss of 47.58 W/kg.

ZnFe2O4 Modified by Fe(NO3)3 for the Synthesis of Ionic Ferrofluids

2010 ◽  
Vol 177 ◽  
pp. 32-36 ◽  
Author(s):  
An Rong Wang ◽  
Jian Li ◽  
Qing Mei Zhang ◽  
Hua Miao
Keyword(s):  
Particle Size ◽  
Magnetic Properties ◽  
Electron Microscope ◽  
Transmission Electron Microscope ◽  
Photoelectron Spectroscopy ◽  
Vibrating Sample Magnetometer ◽  
X Ray Diffraction ◽  
X Ray ◽  
Transmission Electron ◽  
Znfe2o4 Nanoparticles

Weak magnetic ZnFe2O4 nanoparticles were prepared by coprecipitation and treated with different concentrations of Fe(NO3)3 solution. Untreated and treated particles were studied using a vibrating sample magnetometer, transmission electron microscope, by X-ray diffraction, X-ray energy dispersive spectroscopy and X photoelectron spectroscopy. The results showed that, after treatment, the ZnFe2O4/γ-Fe2O3 forms disphase nanoparticles, with enlarged size, enhanced magnetic properties and with a surface parceled with Fe(NO3)3. The size of the particles and their magnetic properties are related to the concentration of the treatment solution. The particle size and magnetic properties could be controlled by controlling the concentration of treating solution, therefore nanoparticles can be more widely used.

TEM Study of FePt and FePt:C/FePt Composite Double-Layered Thin Films

2013 ◽  
Vol 275-277 ◽  
pp. 1952-1955
Author(s):  
Ling Fang Jin ◽  
Xing Zhong Li
Keyword(s):  
Electron Microscopy ◽  
Thin Films ◽  
Transmission Electron Microscopy ◽  
Grain Size ◽  
Magnetic Properties ◽  
Composite Layer ◽  
X Ray Diffraction ◽  
X Ray ◽  
Transmission Electron

New functional nanocomposite FePt:C thin films with FePt underlayers were synthesized by noneptaxial growth. The effect of the FePt layer on the ordering, orientation and magnetic properties of the composite layer has been investigated by adjusting FePt underlayer thickness from 2 nm to 14 nm. Transmission electron microscopy (TEM), together with x-ray diffraction (XRD), has been used to check the growth of the double-layered films and to study the microstructure, including the grain size, shape, orientation and distribution. XRD scans reveal that the orientation of the films was dependent on FePt underlayer thickness. In this paper, the TEM studies of both single-layered nonepitaxially grown FePt and FePt:C composite L10 phase and double-layered deposition FePt:C/FePt are presented.

EFFECT OF NANOCRYSTALLIZATION ANNEALING ON MAGNETIC PROPERTIES AND MAGNETOIMPEDANCE OF CO-BASE RIBBONS

2012 ◽  
Vol 05 ◽  
pp. 841-846
Author(s):  
AMIR KEYVANARA ◽  
REZA GHOLAMIPOUR ◽  
SHAMSEDIN MIRDAMADI ◽  
FARZAD SHAHRI ◽  
HOSSEIN SEPEHRI AMIN
Keyword(s):  
Electron Microscopy ◽  
Heat Treatment ◽  
Magnetic Properties ◽  
Structural Studies ◽  
X Ray Diffraction ◽  
X Ray ◽  
Transmission Electron ◽  
Melt Spun ◽  
Melt Spun Ribbons ◽  
Nanocrystalline Phases

Melt spun ribbons of Co 64 Fe 4 Ni 2 B 19 Si 8 Cr 3 alloy have been prepared and the nanocrystallization process was carried out by the heat treatment of the as spun ribbons above the crystallization temperature. Structural studies of the samples have been performed by transmission electron microscopy and X-ray diffraction. Magnetic properties of the samples and magnetoimpedance measurements were investigated and it was revealed that magnetic properties and magnetoimpedance of the samples deteriorate by the formation of nanocrystalline phases.

FERROMAGNETIC RESONANCE STUDY OF AMORPHOUS AND NANOCRYSTALLINE Fe81B13.5Si3.5C2 RIBBONS

2009 ◽  
Vol 23 (16) ◽  
pp. 3391-3402
Author(s):  
WEERAPHAT PON-ON ◽  
PONGTIP WINOTAI ◽  
I-MING TANG
Keyword(s):  
Ferromagnetic Resonance ◽  
Resonance Line ◽  
Isothermal Annealing ◽  
Amorphous Matrix ◽  
X Ray Diffraction ◽  
X Ray ◽  
Diffusion Controlled ◽  
Nano Grains ◽  
Relative Change ◽  
Kinetics Of

The nanocrystallization process in amorphous Fe 81 B 13.5 Si 3.5 C 2 ribbons caused by isothermal annealing below the crystallization temperature is studied. X-ray diffraction and Mossbauer spectroscopy measurements are used to identify the formation of new Fe containing compounds such as the ribbons annealed at various temperatures. The ferromagnetic resonance measurements for an as-cast ribbon and the 495°, 525°C and 600°C annealed ribbons exhibit a resonance line at 63.64 mT for φ = 0°. The sample annealed at 425°C shows two resonance peaks at 95.45 mT and 295.46 mT. These are due to the nanocrystalline α– Fe(Si) phase. The resonance-line widths are seen to broaden after the ribbons are annealed at 495°C and 525°C, at which time, the amorphous matrix crystallizes into nano-grains of α– Fe(Si) , t– Fe 2 B and t– Fe 3 B phases. The kinetics of the crystallization is discussed in terms of the relative change in the line width of the samples annealed at 495°C for different annealing times. These results yielded an Avrami exponent, n of 0.84 which is consistent with diffusion-controlled growth with a nucleation rate close to zero.

Fine Tuning Magnetic Properties of FePt:C Thin Films by FePt UnderLayers

2013 ◽  
Vol 313-314 ◽  
pp. 254-257
Author(s):  
Ling Fang Jin ◽  
Hong Zhuang
Keyword(s):  
Thin Film ◽  
Electron Microscopy ◽  
Thin Films ◽  
Magnetic Properties ◽  
Fine Tuning ◽  
Nanocomposite Films ◽  
Nanocomposite Thin Film ◽  
X Ray Diffraction ◽  
X Ray ◽  
Transmission Electron

Nonepitaxially grown FePt (x)/FePt:C thin films were synthesized, where FePt (x) (x=2, 5, 8, 11, 14 nm) layers were served as underlayers and FePt:C layer was nanocomposite with thickness of 5 nm. The effect of FePt underlayer on the ordering, orientation and magnetic properties of FePt:C thin films has been investigated by adjusting FePt underlayer thicknesses from 2 nm to 14 nm. X-ray diffraction (XRD), together with transmission electron microscopy (TEM) confirmed that the desired L10 phase was formed and films were (001) textured with FePt underlayer thickness decreased less 5 nm. For 5 nm FePt:C nanocomposite thin film with 2 nm FePt underlayer, the coercivity was 8.2 KOe and the correlation length of FePt:C nanocomposite film was 67 nm. These results reveal that the better orientation and magnetic properties for FePt:C nanocomposite films can be tuned by decreasing FePt underlayer thickness.

Grain Size Dependent Magnetic Properties of Nanocrystalline Sm [BE]Co [BD][BJ]/Cu

2001 ◽  
Vol 703 ◽  
Author(s):  
L. Bessais ◽  
C. Djéga-Mariadassou ◽  
J. Zhang ◽  
V. Lalanne ◽  
A. Percheron-Guégan
Keyword(s):  
Grain Size ◽  
Magnetic Properties ◽  
Rietveld Method ◽  
X Ray Diffraction ◽  
X Ray ◽  
Size Dependent ◽  
Transmission Electron ◽  
Average Grain Size ◽  
Magnetic Metal ◽  
Chemical Distribution

ABSTRACTThe evolution of both micro structural and magnetic properties of the Sm[BE]Co[BD][BJ] Cu powder, is studied as a function of soft co-milling time. The average grain size in the range 20 - 50 nm was determined by transmission electron microscopy coupled with x-ray diffraction using the Rietveld method. The particle shape and chemical distribution were investigated by elemental mapping, using wavelength dispersive x-ray analysis with electron microprobe analysis. The coercivity evolution shows that an optimum value of 6 kOe is obtained after 5 h co-milling. The microstructure analysis indicates that both materials are well mixed in nanometer scale. This technique appears as a potential route to synthesize nanocrystalline Sm[BE]Co[BD][BJ] isolated by non-magnetic metal Cu.

Research on Structural Properties of FePt: C Thin Films with FePt Underlayers

2013 ◽  
Vol 385-386 ◽  
pp. 7-10
Author(s):  
Ling Fang Jin ◽  
Hong Zhuang
Keyword(s):  
Electron Microscopy ◽  
Thin Films ◽  
Transmission Electron Microscopy ◽  
Magnetic Properties ◽  
Structural Properties ◽  
Composite Layer ◽  
X Ray Diffraction ◽  
X Ray ◽  
Transmission Electron

Nonepitaxially grown double-layered films were synthesized with a FePt: C composite layer on top of continuous FePt underlayer. The thickness of FePt was changed from 2 nm to 14 nm. Nanostructures, crystalline orientations and the effect of FePt underlayer on the ordering, orientation and magnetic properties of the thin films were investigated by transmission electron microscopy (TEM) and x-ray diffraction (XRD). XRD confirmed the formation of the ordered L10phase for 5 nm FePt: C film with FePt thickness decreased to 5 nm. TEM studies of FePt:C composite L10phase and double-layered deposition FePt:C/FePt were presented.