Investigation of a Nanoporous Gold / TiO2 Catalyst by Electron Microscopy and Tomography

2013 ◽  
Vol 1504 ◽  
Author(s):  
Kristian Frank ◽  
Andre Wichmann ◽  
Arne Wittstock ◽  
Marcus Bäumer ◽  
Lutz Mädler ◽  
...  
Keyword(s):  
Electron Microscopy ◽  
Transmission Electron Microscopy ◽  
Electrode Materials ◽  
Ion Beam ◽  
Anatase Phase ◽  
Nanoporous Gold ◽  
Dimensional Structure ◽  
Temperature Oxidation ◽  
Porous Gold ◽  
Transmission Electron

ABSTRACTNanoporous gold is a material with many possible applications e.g. in catalysts, sensors and electrode materials. We studied the functionalization of the nanoporous gold with TiO2 particles. Aiming at the low temperature oxidation of CO, the nanoporous gold can be coated with TiO2 in order to enhance catalytic activity. Structure and distribution of the TiO2 on the gold surface are important structural features, which were investigated by transmission electron microscopy. The preparation of the porous gold was tested with focused ion beam - preparation, conventional Ar+ ion beam preparation of nanoporous gold embedded in epoxy and ultramicrotome preparation of nanoporous gold embedded in epoxy. Considering the beam damage on the structure and the contamination of the surface, ultramicrotome preparation turned out to be the best solution. It was shown, that the gold ligaments are abundantly covered by approximately 5 nm TiO2 particles. The determination of the largest lattice fringe distance in high resolution mode revealed that the crystalline nanoparticles consist of the anatase phase. The spatial Ti distribution was measured with energy filtered transmission electron microscopy. Scanning transmission electron microscopy tomography was applied to reconstruct the three-dimensional structure of the gold coated with TiO2 particles.

TEM Sample Preparation Tricks for Advanced DRAMs

2015 ◽  
Author(s):  
Ching Shan Sung ◽  
Hsiu Ting Lee ◽  
Jian Shing Luo
Keyword(s):  
Electron Microscopy ◽  
Transmission Electron Microscopy ◽  
Sample Preparation ◽  
Integrated Circuit ◽  
Focused Ion Beam ◽  
Ion Beam ◽  
Tem Analysis ◽  
Cross Sectional ◽  
Transmission Electron ◽  
Characterization Of Materials

Abstract Transmission electron microscopy (TEM) plays an important role in the structural analysis and characterization of materials for process evaluation and failure analysis in the integrated circuit (IC) industry as device shrinkage continues. It is well known that a high quality TEM sample is one of the keys which enables to facilitate successful TEM analysis. This paper demonstrates a few examples to show the tricks on positioning, protection deposition, sample dicing, and focused ion beam milling of the TEM sample preparation for advanced DRAMs. The micro-structures of the devices and samples architectures were observed by using cross sectional transmission electron microscopy, scanning electron microscopy, and optical microscopy. Following these tricks can help readers to prepare TEM samples with higher quality and efficiency.

Transmission Electron Microscopy (TEM) Specimen Preparation Technique using Focused Ion Beam (FIB): Application to Material Characterization of Chemical Vapor Deposition of Tungsten (W) and Tungsten Silicides (WSix)

1997 ◽  
Author(s):  
K. Doong ◽  
J.-M. Fu ◽  
Y.-C. Huang
Keyword(s):  
Electron Microscopy ◽  
Transmission Electron Microscopy ◽  
Chemical Vapor Deposition ◽  
Vapor Deposition ◽  
Focused Ion Beam ◽  
Ion Beam ◽  
Chemical Vapor ◽  
Specimen Preparation ◽  
Preparation Technique ◽  
Transmission Electron

Abstract The specimen preparation technique using focused ion beam (FIB) to generate cross-sectional transmission electron microscopy (XTEM) samples of chemical vapor deposition (CVD) of Tungsten-plug (W-plug) and Tungsten Silicides (WSix) was studied. Using the combination method including two axes tilting[l], gas enhanced focused ion beam milling[2] and sacrificial metal coating on both sides of electron transmission membrane[3], it was possible to prepare a sample with minimal thickness (less than 1000 A) to get high spatial resolution in TEM observation. Based on this novel thinning technique, some applications such as XTEM observation of W-plug with different aspect ratio (I - 6), and the grain structure of CVD W-plug and CVD WSix were done. Also the problems and artifacts of XTEM sample preparation of high Z-factor material such as CVD W-plug and CVD WSix were given and the ways to avoid or minimize them were suggested.

A Methodology to Reduce Ion Beam Induced Damage in TEM Specimens Prepared by FIB

2002 ◽  
Author(s):  
Chin Kai Liu ◽  
Chi Jen. Chen ◽  
Jeh Yan.Chiou ◽  
David Su
Keyword(s):  
Electron Microscopy ◽  
Transmission Electron Microscopy ◽  
Sample Preparation ◽  
Integrated Circuit ◽  
Focused Ion Beam ◽  
Ion Beam ◽  
Specimen Preparation ◽  
Tem Analysis ◽  
Sensitive Issue ◽  
Transmission Electron

Abstract Focused ion beam (FIB) has become a useful tool in the Integrated Circuit (IC) industry, It is playing an important role in Failure Analysis (FA), circuit repair and Transmission Electron Microscopy (TEM) specimen preparation. In particular, preparation of TEM samples using FIB has become popular within the last ten years [1]; the progress in this field is well documented. Given the usefulness of FIB, “Artifact” however is a very sensitive issue in TEM inspections. The ability to identify those artifacts in TEM analysis is an important as to understanding the significance of pictures In this paper, we will describe how to measure the damages introduced by FIB sample preparation and introduce a better way to prevent such kind of artifacts.

scholarly journals Direct Characterization of the Relation between the Mechanical Response and Microstructure Evolution in Aluminum by Transmission Electron Microscopy In Situ Straining

Materials ◽  
2021 ◽  
Vol 14 (6) ◽  
pp. 1431
Author(s):  
Seiichiro Ii ◽  
Takero Enami ◽  
Takahito Ohmura ◽  
Sadahiro Tsurekawa
Keyword(s):  
Electron Microscopy ◽  
Transmission Electron Microscopy ◽  
Ion Beam ◽  
Elastic Behavior ◽  
Annealed Specimen ◽  
Displacement Curve ◽  
Dislocation Loops ◽  
Transmission Electron ◽  
Stress Drops

Transmission electron microscopy in situ straining experiments of Al single crystals with different initial lattice defect densities have been performed. The as-focused ion beam (FIB)-processed pillar sample contained a high density of prismatic dislocation loops with the <111> Burgers vector, while the post-annealed specimen had an almost defect-free microstructure. In both specimens, plastic deformation occurred with repetitive stress drops (∆σ). The stress drops were accompanied by certain dislocation motions, suggesting the dislocation avalanche phenomenon. ∆σ for the as-FIB Al pillar sample was smaller than that for the post-annealed Al sample. This can be considered to be because of the interaction of gliding dislocations with immobile prismatic dislocation loops introduced by the FIB. The reloading process after stress reduction was dominated by elastic behavior because the slope of the load–displacement curve for reloading was close to the Young’s modulus of Al. Microplasticity was observed during the load-recovery process, suggesting that microyielding and a dislocation avalanche repeatedly occurred, leading to intermittent plasticity as an elementary step of macroplastic deformation.

TEM Characterization of As-Deposited and Annealed Ni/Al Multilayer Thin Film

2010 ◽  
Vol 16 (6) ◽  
pp. 662-669 ◽  
Author(s):  
S. Simões ◽  
F. Viana ◽  
A.S. Ramos ◽  
M.T. Vieira ◽  
M.F. Vieira
Keyword(s):  
Electron Microscopy ◽  
Thin Films ◽  
Transmission Electron Microscopy ◽  
Cross Section ◽  
Ion Beam ◽  
Microstructural Characterization ◽  
Multilayer Thin Films ◽  
Tem Analysis ◽  
Plan View ◽  
Transmission Electron

AbstractReactive multilayer thin films that undergo highly exothermic reactions are attractive choices for applications in ignition, propulsion, and joining systems. Ni/Al reactive multilayer thin films were deposited by dc magnetron sputtering with a period of 14 nm. The microstructure of the as-deposited and heat-treated Ni/Al multilayers was studied by transmission electron microscopy (TEM) and scanning transmission electron microscopy (STEM) in plan view and in cross section. The cross-section samples for TEM and STEM were prepared by focused ion beam lift-out technique. TEM analysis indicates that the as-deposited samples were composed of Ni and Al. High-resolution TEM images reveal the presence of NiAl in small localized regions. Microstructural characterization shows that heat treating at 450 and 700°C transforms the Ni/Al multilayered structure into equiaxed NiAl fine grains.

Transmission Electron Microscopy of Semiconductor Based Products

1998 ◽  
Vol 523 ◽  
Author(s):  
John Mardinly ◽  
David W. Susnitzky
Keyword(s):  
Electron Microscopy ◽  
Transmission Electron Microscopy ◽  
Ion Beam ◽  
Semiconductor Industry ◽  
Size Reduction ◽  
Specimen Preparation ◽  
Specimen Thickness ◽  
Ion Milling ◽  
Feature Size ◽  
Transmission Electron

AbstractThe demand for increasingly higher performance semiconductor products has stimulated the semiconductor industry to respond by producing devices with increasingly complex circuitry, more transistors in less space, more layers of metal, dielectric and interconnects, more interfaces, and a manufacturing process with nearly 1,000 steps. As all device features are shrunk in the quest for higher performance, the role of Transmission Electron Microscopy as a characterization tool takes on a continually increasing importance over older, lower-resolution characterization tools, such as SEM. The Ångstrom scale imaging resolution and nanometer scale chemical analysis and diffraction resolution provided by modem TEM's are particularly well suited for solving materials problems encountered during research, development, production engineering, reliability testing, and failure analysis. A critical enabling technology for the application of TEM to semiconductor based products as the feature size shrinks below a quarter micron is advances in specimen preparation. The traditional 1,000Å thick specimen will be unsatisfactory in a growing number of applications. It can be shown using a simple geometrical model, that the thickness of TEM specimens must shrink as the square root of the feature size reduction. Moreover, the center-targeting of these specimens must improve so that the centertargeting error shrinks linearly with the feature size reduction. To meet these challenges, control of the specimen preparation process will require a new generation of polishing and ion milling tools that make use of high resolution imaging to control the ion milling process. In addition, as the TEM specimen thickness shrinks, the thickness of surface amorphization produced must also be reduced. Gallium focused ion beam systems can produce hundreds of Ångstroms of amorphised surface silicon, an amount which can consume an entire thin specimen. This limitation to FIB milling requires a method of removal of amorphised material that leaves no artifact in the remaining material.

In Situ High-Temperature Transmission Electron Microscopy Observations of the Formation of Nanocrystalline TiC from Nanocrystalline Anatase (TiO2)

1998 ◽  
Vol 4 (3) ◽  
pp. 269-277 ◽  
Author(s):  
A. Agrawal ◽  
J. Cizeron ◽  
V.L. Colvin
Keyword(s):  
Electron Microscopy ◽  
Transmission Electron Microscopy ◽  
High Temperature ◽  
Solid Phase ◽  
Anatase Phase ◽  
High Resolution Electron Microscopy ◽  
Rutile Phase ◽  
Transmission Electron ◽  
New Phase

In this work, the high-temperature behavior of nanocrystalline TiO2 is studied using in situ transmission electron microscopy (TEM). These nanoparticles are made using wet chemical techniques that generate the anatase phase of TiO2 with average grain sizes of 6 nm. X-ray diffraction studies of nanophase TiO2 indicate the material undergoes a solid-solid phase transformation to the stable rutile phase between 600° and 900°C. This phase transition is not observed in the TEM samples, which remain anatase up to temperatures as high as 1000°C. Above 1000°C, nanoparticles become mobile on the amorphous carbon grid and by 1300°C, all anatase diffraction is lost and larger (50 nm) single crystals of a new phase are present. This new phase is identified as TiC both from high-resolution electron microscopy after heat treatment and electron diffraction collected during in situ heating experiments. Video images of the particle motion in situ show the nanoparticles diffusing and interacting with the underlying grid material as the reaction from TiO2 to TiC proceeds.