Interfacial Reaction Mechanism between Molten Ag-Cu-Based Active Brazing Alloys and Untreated or Pre-Oxidized PLS-SiC

ABSTRACTBased on wettability and reaction interfaces previously reported, as well as on thermodynamic considerations, a likely mechanism has been proposed for the chemical interaction taking place at the metal/ceramic interface during wettability experiments carried out by the so-called “sessile drop” method. The experiments involved three Ag-Cu-based brazing alloys [Cusil (Ag-28wt.%Cu), Cusil-ABA (Ag-34.6wt.%Cu-1.58wt.%Ti) and Incusil-ABA (Ag-26.6wt.%Cu-12.4wt.%In-0.89wt.%Ti)] and as polished and pre-oxidized pressure-less sintered silicon carbide (PLS-SiC), with a total holding time of 90 minutes at 850 °C, under a Zr sponge-gettered vacuum of 10-4/10-5 Torr.