ABSTRACTCopper-doped carbon aerogels, which were prepared by sol-gel polymerization of a mixture of resorcinol, formaldehyde and copper ions, followed by supercritical drying with liquid CO2 and carbonization at different temperatures under a N2 atmosphere, were characterized by magnetic susceptibility and temperature-dependent conductivity measurements. The experimental results show that the magnetic susceptibilities (χ) of all the copper-doped carbon aerogels are larger than that of the blank carbon aerogel. The temperature-dependent magnetic susceptibilities of the copper-doped carbon aerogels are well fit to a Curie function in the low temperature region (below 45 K). According to the Curie constant obtained, the spin concentration (N) of the copper-doped carbon aerogels was calculated and the results show that the spin concentration of doped samples increases at first with an increase in the copper concentration used in doping, and then drops from the maximum in N and χ when the copper concentration is further increased above 0.1 wt%. Magnetic susceptibility results suggest that copper-doped carbon aerogels carbonized at 800 °C are more disordered than those carbonized at 1000 °C. The conductivity of these copper-doped carbon aerogels is apparently higher than that of the blank carbon aerogel, especially at low temperature (T < 45 K). The temperature-dependent resistivities of both the copper-doped and the blank carbon aerogels follow a linear functional form log ρ(T) ∼ (1/T)1/2 with two distinct regions below and above 45 K, indicating that the conduction of both the copper-doped and the blank carbon aerogels obey a tunneling and/or a hopping mechanism.
Carbon Aerogels Prepared Based on Sol-Gel Reaction of Cellulose Colloid with AEP and Its Adsorption of Copper Ions in Aqueous Solution