Fatigue Behavior and Microstructure of Neutron Irradiated Thin Section Type 304 Stainless Steel at Elevated Temperatures

2009 ◽  
pp. 156-156-16
Author(s):  
DJ Michel ◽  
HH Smith
Keyword(s):  
Stainless Steel ◽  
Thin Section ◽  
Elevated Temperatures ◽  
Fatigue Behavior ◽  
304 Stainless Steel ◽  
Section Type ◽  
Type 304 ◽  
Type 304 Stainless Steel

416 Fatigue Behavior of Zirconia-Coated Type 304 Stainless Steel Under Heat Cycle Condition

2001 ◽  
Vol 2001.76 (0) ◽  
pp. _4-33_-_4-34_
Author(s):  
Keiji OGURA ◽  
Izuru NISHIKAWA ◽  
Hiroyuki WAKI ◽  
Hirotaka NAGANUMA
Keyword(s):  
Stainless Steel ◽  
Fatigue Behavior ◽  
304 Stainless Steel ◽  
Heat Cycle ◽  
Cycle Condition ◽  
Type 304 ◽  
Type 304 Stainless Steel

High-Cycle Fatigue Behavior of Solution-Annealed and Thermally-Aged Type 304 Stainless Steel

1980 ◽  
Vol 102 (1) ◽  
pp. 141-146 ◽  
Author(s):  
P. Soo ◽  
J. G. Y. Chow
Keyword(s):  
Stainless Steel ◽  
High Cycle Fatigue ◽  
Fatigue Behavior ◽  
Cyclic Stress ◽  
304 Stainless Steel ◽  
Strain History ◽  
Cycle Fatigue ◽  
Stress Strain ◽  
Type 304 ◽  
Type 304 Stainless Steel

High-cycle, load-controlled fatigue data have been obtained for solution-annealed and thermally-aged Type 304 stainless steel, for temperatures between 22 and 593°C (72-1100°F) at a cycling rate of 40 Hz. Although these data are principally used to assess fatigue failure in components subjected to rapid stress cycling, it has been shown that they may be correlated with available low-cycle data if cyclic stress-strain curves are used for converting the high-cycle stresses to effective strains. Differences in initial stress-strain history and cycling rates for the high- and low-cycle data evaluated are found to be unimportant. For the thermally-aged material there is an initial enhancement of the high-cycle-fatigue strength but, after long aging times, the strength decreases to a value close to that for unaged material. The carbide precipitates formed during aging appear to influence fatigue life through changes they impart in the cyclic work-hardening rates.

An assessment of cold work effects on strain-controlled low-cycle fatigue behavior of type 304 stainless steel

1993 ◽  
Vol 24 (4) ◽  
pp. 913-924 ◽  
Author(s):  
K. Bhanu Sankara Rao ◽  
M. Valsan ◽  
R. Sandhya ◽  
S. L. Mannan ◽  
P. Rodriguez
Keyword(s):  
Stainless Steel ◽  
Low Cycle Fatigue ◽  
Fatigue Behavior ◽  
Cold Work ◽  
304 Stainless Steel ◽  
Cycle Fatigue ◽  
Type 304 ◽  
Type 304 Stainless Steel
Sign in / Sign up

Export Citation Format

Share Document