Evaluation of a Proposed Standard Method of Testing for Susceptibility to Stress-Corrosion Cracking of High-Strength 7XXX Series Aluminum Alloy Products

Stress Corrosion—New Approaches ◽

10.1520/stp28667s ◽

2009 ◽

pp. 3-3-29 ◽

Cited By ~ 2

Author(s):

DO Sprowls ◽

TJ Summerson ◽

GM Ugiansky ◽

SG Epstein ◽

HL Craig

Keyword(s):

Aluminum Alloy ◽

Stress Corrosion ◽

Standard Method ◽

Stress Corrosion Cracking ◽

High Strength ◽

Corrosion Cracking ◽

Series Aluminum Alloy

Download Full-text

Macroscopic Segregation and Stress Corrosion Cracking in 7xxx Series Aluminum Alloy Arc Welds

Metallurgical and Materials Transactions A ◽

10.1007/s11661-015-2796-5 ◽

2015 ◽

Vol 46 (5) ◽

pp. 1827-1833 ◽

Cited By ~ 5

Author(s):

Tyler E. Borchers ◽

Donald P. McAllister ◽

Wei Zhang

Keyword(s):

Aluminum Alloy ◽

Stress Corrosion ◽

Stress Corrosion Cracking ◽

Corrosion Cracking ◽

Series Aluminum Alloy

Download Full-text

Effect of Corrosion Atmosphere and Strain Rate on the Stress Corrosion Cracking of High Strength 7xxx Aluminum Alloy

Journal of the Korean institute of surface engineering ◽

10.5695/jkise.2008.41.3.121 ◽

2008 ◽

Vol 41 (3) ◽

pp. 121-128

Author(s):

Yeo-Wan Yun ◽

Sang-Ha Kim

Keyword(s):

Aluminum Alloy ◽

Strain Rate ◽

Stress Corrosion ◽

Stress Corrosion Cracking ◽

High Strength ◽

Corrosion Cracking

Download Full-text

Model experiments concerning the contribution of hydrogen embrittlement on stress corrosion cracking of high strength aluminum alloy.

Journal of Japan Institute of Light Metals ◽

10.2464/jilm.42.21 ◽

1992 ◽

Vol 42 (1) ◽

pp. 21-26 ◽

Cited By ~ 3

Author(s):

Tadakazu OHNISHI

Keyword(s):

Aluminum Alloy ◽

Hydrogen Embrittlement ◽

Stress Corrosion ◽

Stress Corrosion Cracking ◽

High Strength ◽

Corrosion Cracking ◽

Model Experiments ◽

High Strength Aluminum Alloy

Download Full-text

Stress Corrosion Cracking of High Strength Al-Zn-Mg-Cu Aluminum Alloy with Different Compositions

Journal of the Korean institute of surface engineering ◽

10.5695/jkise.2008.41.3.109 ◽

2008 ◽

Vol 41 (3) ◽

pp. 109-113 ◽

Cited By ~ 1

Author(s):

Jun-Tak Kim ◽

Sang-Ho Kim

Keyword(s):

Aluminum Alloy ◽

Stress Corrosion ◽

Stress Corrosion Cracking ◽

High Strength ◽

Corrosion Cracking

Download Full-text

In-Situ Nanoscopic Visualization of Stress Corrosion Cracking of High-Strength Aluminum Alloy by Scanning Atomic Force Microscopy

Journal de Physique IV (Proceedings) ◽

10.1051/jp4:1996641 ◽

1996 ◽

Vol 06 (C6) ◽

pp. C6-413-C6-420 ◽

Cited By ~ 3

Author(s):

K. Komai ◽

K. Minoshima ◽

T. Miyawaki

Keyword(s):

Atomic Force Microscopy ◽

Aluminum Alloy ◽

Stress Corrosion ◽

Stress Corrosion Cracking ◽

High Strength ◽

Corrosion Cracking ◽

Force Microscopy ◽

High Strength Aluminum Alloy ◽

Atomic Force

Download Full-text

Minimizing Stress-Corrosion Cracking in Wrought High-Strength Aluminum Alloy Products

10.4271/arp823f ◽

2019 ◽

Author(s):

Keyword(s):

Aluminum Alloy ◽

Stress Corrosion ◽

Stress Corrosion Cracking ◽

High Strength ◽

Corrosion Cracking ◽

High Strength Aluminum Alloy

Download Full-text

Stress Corrosion Cracking of High Strength Skills. Abstract Only

10.21236/ada367777 ◽

1999 ◽

Author(s):

Eun Lee ◽

Henry Sanders ◽

Bhaskar Sarkar

Keyword(s):

Stress Corrosion ◽

Stress Corrosion Cracking ◽

High Strength ◽

Corrosion Cracking

Download Full-text

Stress Corrosion Cracking of High Strength Steels

10.21236/ada375902 ◽

1995 ◽

Author(s):

Eun U. Lee ◽

Henry Sanders ◽

Bhaskar Sarkar

Keyword(s):

Stress Corrosion ◽

Stress Corrosion Cracking ◽

High Strength Steels ◽

High Strength ◽

Corrosion Cracking

Download Full-text

Effects of high temperature austenitization on fracture, fatigue and stress corrosion cracking behavior of cast and forged high strength steels I: Monotonic fracture behavior

Materials Science and Engineering A ◽

10.1016/0921-5093(89)90166-4 ◽

1989 ◽

Vol 110 ◽

pp. 151-164 ◽

Cited By ~ 2

Author(s):

Wei-Di Cao ◽

Xiao-Ping Lu

Keyword(s):

High Temperature ◽

Stress Corrosion ◽

Stress Corrosion Cracking ◽

Fracture Behavior ◽

High Strength Steels ◽

High Strength ◽

Corrosion Cracking ◽

Cracking Behavior

Download Full-text

Effect of sulfate-reducing bacteria on hydrogen permeation and stress corrosion cracking behavior of 980 high-strength steel in seawater

Journal of Material Science and Technology ◽

10.1016/j.jmst.2021.02.039 ◽

2021 ◽

Author(s):

Meiying Lv ◽

Xuchao Chen ◽

Zhenxin Li ◽

Min Du

Keyword(s):

Stress Corrosion ◽

Stress Corrosion Cracking ◽

High Strength Steel ◽

Hydrogen Permeation ◽

High Strength ◽

Sulfate Reducing Bacteria ◽

Corrosion Cracking ◽

Cracking Behavior ◽

Sulfate Reducing ◽

Reducing Bacteria

Download Full-text