Effect of Film Thickness and Voids in Mineral Aggregate in Basic Oxygen Furnace Slag Dense-Graded Asphalt Concrete

2014 ◽  
Vol 43 (2) ◽  
pp. 20140079 ◽  
Author(s):  
Shih-Huang Chen ◽  
Jyh-Dong Lin ◽  
Daud Huang ◽  
Ching-Tsung Hung
Keyword(s):  
Film Thickness ◽  
Asphalt Concrete ◽  
Basic Oxygen Furnace ◽  
Basic Oxygen ◽  
Mineral Aggregate ◽  
Basic Oxygen Furnace Slag ◽  
Furnace Slag

scholarly journals A Study on Radiation Cooling Effect on Asphalt Concrete Pavement Using Basic Oxygen Furnace Slag to Replace Partial Aggregates

2021 ◽  
Vol 13 (7) ◽  
pp. 3708 ◽  
Author(s):  
Yeou-Fong Li ◽  
Po-An Yang ◽  
Chia-Ho Wu ◽  
Ta-Wui Cheng ◽  
Chih-Hong Huang
Keyword(s):  
Mechanical Properties ◽  
Thermal Performance ◽  
Asphalt Concrete ◽  
Basic Oxygen Furnace ◽  
The Body ◽  
Basic Oxygen ◽  
Radiation Cooling ◽  
Basic Oxygen Furnace Slag ◽  
Furnace Slag ◽  
Indoor And Outdoor

In this study, aggregates in asphalt concrete were partially replaced by basic oxygen furnace slag (BOFS) in proportions of 45 wt.%, 55 wt.%, and 75 wt.%. The thermal performances of the specimens are discussed based on the thermal conductivity, emissivity, and the indoor and outdoor temperature measurements. Consequently, 75 wt.% of the specimen’s aggregates were replaced by BOFS, which had a high emissivity of 0.86 across the sky window. In the indoor and outdoor tests, the temperature change was recorded to estimate the thermal performance of specimens. According to the quantitative calculation, when the substitution of BOFS was higher than 55 wt.%, the specimens had a better radiation cooling ability. Among these specimens, the specimen with the BOFS substitution of 75 wt.% absorbed the most heat inside the body, contributing to less heat remaining in the environment. Furthermore, because Newton’s cooling energy accounted for about 90% of the stored energy within 7 h, the heat dissipation after the seventh hour was primarily radiation cooling, corresponding to the emission across the urban boundary layer. As for the mechanical properties, the stability value, indirect tensile strength, and British pendulum number (BPN) were in line with the specifications under the proper BOFS substitution. In conclusion, BOFS has great applicability in pavements due to its thermal performance and mechanical properties. It not only achieves the goal of urban heat island mitigation by radiation cooling, but also reflects the concept of resource sustainability.

scholarly journals Geotechnical Properties and Microstructure of Lime-Fly Ash-Phosphogypsum-Stabilized Soil

2018 ◽  
Vol 2018 ◽  
pp. 1-9 ◽  
Author(s):  
Tebogo Pilgrene Mashifana ◽  
Felix Ndubisi Okonta ◽  
Freeman Ntuli
Keyword(s):  
Fly Ash ◽  
Expansive Soil ◽  
Basic Oxygen Furnace ◽  
Geotechnical Properties ◽  
Magnesium Silicide ◽  
Engineering Properties ◽  
Basic Oxygen ◽  
Basic Oxygen Furnace Slag ◽  
Phosphogypsum Waste ◽  
Furnace Slag

The use of industrial waste as a potential stabilizer of marginal construction materials is cost effective. Phosphogypsum and fly ash are industrial wastes generated in very large quantities and readily available in South Africa. In order to explore the potential stabilization of vastly abundant expansive soil using larger quantity phosphogypsum waste as a potential modifier, composites with a mixture of lime-fly ash-phosphogypsum-basic oxygen furnace slag were developed. However because of the presence of radionuclide, it was necessary to treat the phosphogypsum waste with mild citric acid. The effect of the acid treatment on the geotechnical properties and microstructure of expansive soil stabilized with phosphogypsum-lime-fly ash-basic oxygen furnace slag (PG-LFA-BOF) paste was evaluated, in comparison with the untreated phosphogypsum. Expansive soil stabilized with acid-treated PG-LFA-BOF paste exhibited better geotechnical properties; in particular, the high strength mobilized was associated primarily with the formation of various calcium magnesium silicide and coating by calcium silicate hydrate and calcium aluminate hydrate. The soil microstructure was improved due to the formation of hydration products. The stabilized expansive soil met the specification for road subgrades and subbase. Stabilization of expansive soils with phosphogypsum, fly ash, and basic oxygen fly ash does not only improve engineering properties of soil but also provides a solution in relation to disposal and environmental pollution challenges.

Basic oxygen furnace slag: Review of current and potential uses

2020 ◽  
Vol 149 ◽  
pp. 106234 ◽  
Author(s):  
Tamlyn Sasha Naidu ◽  
Craig Michael Sheridan ◽  
Lizelle Doreen van Dyk
Keyword(s):  
Basic Oxygen Furnace ◽  
Basic Oxygen ◽  
Basic Oxygen Furnace Slag ◽  
Furnace Slag

scholarly journals Feasibility and Characterization Mortar Blended with High-Amount Basic Oxygen Furnace Slag

Materials ◽  
2018 ◽  
Vol 12 (1) ◽  
pp. 6 ◽  
Author(s):  
Wei-Ting Lin ◽  
Chia-Jung Tsai ◽  
Jie Chen ◽  
Weidong Liu
Keyword(s):  
Steel Industry ◽  
Setting Time ◽  
Basic Oxygen Furnace ◽  
Cementitious Material ◽  
Partial Replacement ◽  
Supplementary Cementitious Material ◽  
Basic Oxygen ◽  
Basic Oxygen Furnace Slag ◽  
Furnace Slag ◽  
Weight Proportion

Basic oxygen furnace slag (BOFS) was ground to three levels of fineness as a replacement for cement at weight proportions of 10, 30, 50, and 70 wt.%. Fineness and weight proportion were shown to have significant effects on the flowability and setting time of the mortars. The expansion of BOFS mortars increased with an increase in the proportion of cement replaced, thereby exacerbating the effects of cracking. Optimal mechanical properties were achieved when 10 wt.% of the cement was replaced using BOFS with fineness of 10,000 cm2/g. The compressive strength of BOFS mortar is similar to that of ordinary Portland mortar, which makes BOFS suitable for the partial replacement of cement as a supplementary cementitious material. Scanning electron microscopy results revealed that the reaction of CaO with H2O results in the formation of C–S–H colloids, whereas the reaction of SiO2 with Al2O3 produces C–A–S–H colloids. The use of BOFS as a partial replacement for Portland cement could make a tremendous contribution to the steel industry and help to lower CO2 emissions.