scholarly journals Evaluation of the Magnetic Permeability for the Microstructural Characterization of a Duplex Stainless Steel

2014 ◽  
Vol 44 (3) ◽  
pp. 20130313 ◽  
Author(s):  
Edgard de Macedo Silva ◽  
Josinaldo P. Leite ◽  
Francisco A. de França Neto ◽  
João P. Leite ◽  
Walter M. L. Fialho ◽  
...  
Keyword(s):  
Stainless Steel ◽  
Duplex Stainless Steel ◽  
Magnetic Permeability ◽  
Microstructural Characterization

DETECTION OF THE SIGMA PHASE IN A DUPLEX STAINLESS STEEL THROUGH MEASUREMENTS OF MAGNETIC PERMEABILITY

2019 ◽  
Author(s):  
Edgard Silva ◽  
Francisco Eduardo Mendes da Silva ◽  
Amanda Medeiros ◽  
Ana Paula Alves Pacheco ◽  
IZAURA VIEGAS ◽  
...  
Keyword(s):  
Stainless Steel ◽  
Duplex Stainless Steel ◽  
Magnetic Permeability ◽  
Sigma Phase

METALLURGICAL AND CORROSION CHARACTERIZATION OF POST WELD HEAT TREATED DUPLEX STAINLESS STEEL (UNS S31803) JOINTS BY FRICTION WELDING PROCESS

2016 ◽  
Vol 23 (03) ◽  
pp. 1650013 ◽  
Author(s):  
MOHAMMED ASIF M. ◽  
KULKARNI ANUP SHRIKRISHNA ◽  
P. SATHIYA
Keyword(s):  
Stainless Steel ◽  
Duplex Stainless Steel ◽  
Friction Welding ◽  
Volume Fraction ◽  
Welding Process ◽  
Equilibrium Temperature ◽  
Weld Interface ◽  
Heat Treated ◽  
Weld Heat

The present study focuses on the metallurgical and corrosion characterization of post weld heat treated duplex stainless steel joints. After friction welding, it was confirmed that there is an increase in ferrite content at weld interface due to dynamic recrystallization. This caused the weldments prone to pitting corrosion attack. Hence the post weld heat treatments were performed at three temperatures 1080[Formula: see text]C, 1150[Formula: see text]C and 1200[Formula: see text]C with 15[Formula: see text]min of aging time. This was followed by water and oil quenching. The volume fraction of ferrite to austenite ratio was balanced and highest pit nucleation resistance were achieved after PWHT at 1080[Formula: see text]C followed by water quench and at 1150[Formula: see text]C followed by oil quench. This had happened exactly at parameter set containing heating pressure (HP):40 heating time (HT):4 upsetting pressure (UP):80 upsetting time (UP):2 (experiment no. 5). Dual phase presence and absence of precipitates were conformed through TEM which follow Kurdjumov–Sachs relationship. PREN of ferrite was decreasing with increase in temperature and that of austenite increased. The equilibrium temperature for water quenching was around 1100[Formula: see text]C and that for oil quenching was around 1140[Formula: see text]C. The pit depths were found to be in the range of 100[Formula: see text]nm and width of 1.5–2[Formula: see text][Formula: see text]m.

scholarly journals Characterization of Impact Deformation Behavior of a Thermally Aged Duplex Stainless Steel by EBSD

2018 ◽  
Vol 31 (8) ◽  
pp. 798-806 ◽  
Author(s):  
Gang Liu ◽  
Shi-Lei Li ◽  
Hai-Long Zhang ◽  
Xi-Tao Wang ◽  
Yan-Li Wang
Keyword(s):  
Stainless Steel ◽  
Duplex Stainless Steel ◽  
Deformation Behavior ◽  
Impact Deformation
Sign in / Sign up

Export Citation Format

Share Document