Practice for Evaluating Stress-Corrosion-Cracking Resistance of Metals and Alloys in a Boiling Magnesium Chloride Solution

1994 ◽  
Author(s):  
Keyword(s):  
Stress Corrosion ◽  
Stress Corrosion Cracking ◽  
Magnesium Chloride ◽  
Chloride Solution ◽  
Corrosion Cracking ◽  
Metals And Alloys ◽  
Cracking Resistance ◽  
Magnesium Chloride Solution

Effects of Composition on the Stress Corrosion Cracking of Ferritic Stainless Steels

CORROSION ◽  
1968 ◽  
Vol 24 (10) ◽  
pp. 344-352 ◽  
Author(s):  
A. P. BOND ◽  
H. J. DUNDAS
Keyword(s):  
Stress Corrosion ◽  
Stress Corrosion Cracking ◽  
Stainless Steels ◽  
Magnesium Chloride ◽  
Chloride Solution ◽  
Corrosion Cracking ◽  
Type Specimens ◽  
Magnesium Chloride Solution ◽  
Ferritic Stainless Steels ◽  
Molybdenum Alloys

Abstract U-bend and axially loaded tensile-type specimens were used in stress corrosion tests performed in boiling 140 C (284 F) magnesium chloride solution. The experimental ferritic alloys tested contained 17 to 25% chromium, 0 to 4% nickel, 0 to 2% copper, and 0 to 5% molybdenum. Alloys essentially free of nickel and copper did not undergo stress corrosion cracking. (Tests on Types 430 and 434 stainless steels confirmed this behavior.) However, alloys containing more than 1% nickel or 0.5% copper were subject to transgi anular stress corrosion cracking in boiling magnesium chloride solution. Critical concentrations of copper and nickel that produce susceptibility to cracking were determined at various chromium and molybdenum levels. Experiments at controlled potentials indicated that cracking in boiling magnesium chloride was not the result of hydrogen embrittlement.