Facile surface hydrophobization of medium-density fiberboard (MDF) by silver deposition

Holzforschung ◽  
2017 ◽  
Vol 71 (4) ◽  
pp. 337-340 ◽  
Author(s):  
Xiaodi Ji ◽  
Minghui Guo
Keyword(s):  
Crystal Structure ◽  
Surface Coating ◽  
Medium Density Fiberboard ◽  
Water Repellent ◽  
Medium Density ◽  
X Ray Diffraction ◽  
Silver Deposition ◽  
X Ray ◽  
Ag Particles ◽  
Scanning Electron

Abstract A facile and effective method for the surface hydrophobization of medium-density fiberboards (MDFs) via the silver (Ag) mirror reaction has been investigated. The pristine MDF surface was treated with silver nitrate (AgNO3) and subsequently with glucose to reduce Ag ions into Ag particles, which led to dual-size surface roughness. The roughness and morphology of the Ag-coated MDF surface were characterized by scanning electron microscopy (SEM), and the elemental composition and the crystal structure of the surface were determined via energy-dispersive X-ray spectroscopy (EDXS) and X-ray diffraction (XRD) analyses. The wettability of the MDF surface was measured by contact angle (CA) measurements. The results indicated that pure Ag particles were successfully deposited onto the MDF surface without any impurities. The Ag surface coating was water repellent as indicated by a CA of 136°, which slightly decreased with time. The hydrophobicity was derived from the air trapped in the surface cavities and the dual-size roughness.

X-ray powder diffraction data of LaNi0.5Ti0.45Co0.05O3, LaNi0.45Co0.05Ti0.5O3, and LaNi0.5Ti0.5O3 perovskites

2021 ◽  
pp. 1-6
Author(s):  
Mariana M. V. M. Souza ◽  
Alex Maza ◽  
Pablo V. Tuza
Keyword(s):  
Crystal Structure ◽  
Rietveld Method ◽  
Pechini Method ◽  
Powder Diffraction Data ◽  
X Ray Diffraction ◽  
Unit Cell Parameters ◽  
X Ray ◽  
Cell Parameters ◽  
Modified Pechini Method ◽  
Scanning Electron

In the present work, LaNi0.5Ti0.45Co0.05O3, LaNi0.45Co0.05Ti0.5O3, and LaNi0.5Ti0.5O3 perovskites were synthesized by the modified Pechini method. These materials were characterized using X-ray fluorescence, scanning electron microscopy, and powder X-ray diffraction coupled to the Rietveld method. The crystal structure of these materials is orthorhombic, with space group Pbnm (No 62). The unit-cell parameters are a = 5.535(5) Å, b = 5.527(3) Å, c = 7.819(7) Å, V = 239.2(3) Å3, for the LaNi0.5Ti0.45Co0.05O3, a = 5.538(6) Å, b = 5.528(4) Å, c = 7.825(10) Å, V = 239.5(4) Å3, for the LaNi0.45Co0.05Ti0.5O3, and a = 5.540(2) Å, b = 5.5334(15) Å, c = 7.834(3) Å, V = 240.2(1) Å3, for the LaNi0.5Ti0.5O3.

Study on the Properties of Doped La in BaBi4Ti4O15 Ceramic

2007 ◽  
Vol 26-28 ◽  
pp. 243-246
Author(s):  
Xing Hua Yang ◽  
Jin Liang Huang ◽  
Xiao Wang ◽  
Chun Wei Cui
Keyword(s):  
Crystal Structure ◽  
Grain Size ◽  
Electron Microscope ◽  
Scanning Electron Microscope ◽  
Sintering Temperature ◽  
Solid Phase ◽  
X Ray Diffraction ◽  
X Ray ◽  
Lanthanum Content ◽  
Scanning Electron

BaBi4-xLaxTi4O15 (BBLT) ceramics were prepared by conventional solid phase sintering ceramics processing technology. The crystal structure and the microstructure were detected by X-ray diffraction (XRD) and scanning electron microscope (SEM). The XRD analyses show that La3+ ions doping did not change the crystal structure of BBT ceramics. The sintering temperature increased from 1120°C to 1150°C with increasing Lanthanum content from 0 to 0.5, but it widened the sintering temperature range from 20°C to 50°C and refined the grain size of the BBT ceramic. Additionally, polarization treatment was performed and finally piezoelectric property was measured. As a result, the piezoelectric constant d33 of the 0.1at.% doped BBLT ceramics reached its highest value about 22pc/N at polarizing electric field of 8kV/mm and polarizing temperature of 120°C for 30min.

High-performance electrical properties of La-based perovskite ceramics for the functional phase of thick film resistors

2020 ◽  
Author(s):  
Yongcheng Lu ◽  
Yuanxun Li ◽  
Daming Chen ◽  
Rui Peng ◽  
Qinghui Yang ◽  
...  
Keyword(s):  
Crystal Structure ◽  
Electrical Properties ◽  
Thick Film ◽  
High Performance ◽  
Composite Ceramics ◽  
X Ray Diffraction ◽  
X Ray ◽  
Alternative Material ◽  
Perovskite Ceramics ◽  
Scanning Electron

Abstract In order to explore an economical functional phase alternative material for thick film resistors, the crystal structure, microstructure, and electrical properties of (1-x)LSCN + xLCNZ (x = 0.0–1.0) composite ceramics were studied through solid-state reaction experiments. The composite ceramics were characterized by x–ray diffraction, scanning electron microscopy, energy dispersive x–ray spectroscopy, and DC four–probe method. Results suggested that the main phases of LSCN and LCNZ were formed, along with a small part of impurity phases. The addition of LCNZ to LSCN decreased the electrical conductivity and changed the TCR from positive to negative. Zero TCR could be achieved around 0.6 < x < 0.8 and relatively low absolute TCR values could be obtained for the samples of 0.4 ≤ x ≤ 0.8. The ceramic of 0.6LSCN + 0.4LCNZ showed the optimal performances of conductivity = 1923 S/cm, TCR = 379.54 ppm/℃, and relative density = 95.05%.

Nanocrystalline Barium Zirconium Titanate Synthesized by the Sonochemical Process

2013 ◽  
Vol 802 ◽  
pp. 119-123
Author(s):  
Supamas Wirunchit ◽  
Rangson Muanghlua ◽  
Supamas Wirunchit ◽  
Wanwilai Vittayakorn ◽  
Naratip Vittayakorn
Keyword(s):  
Crystal Structure ◽  
Electron Microscopy ◽  
Reaction Time ◽  
Single Phase ◽  
Zirconium Titanate ◽  
X Ray Diffraction ◽  
X Ray ◽  
Large Particles ◽  
Barium Zirconium Titanate ◽  
Scanning Electron

Nanocrystalline barium zirconium titanate, BaZr0.4Ti0.6O3, was synthesized successfully via the sonochemical process. The effects of reaction time on the precipitation of Ba(Zr,Ti)O3 particles were investigated briefly. The crystal structure as well as molecular vibrations and morphology were investigated. X-ray diffraction indicated that the powders exhibited a single phase perovskite structure, without the presence of pyrochlore or unwanted phases at the reaction time of 60 min. Nanocrystals were formed before being oriented and aggregated into large particles in aqueous solution under ultrasonic irradiation. A scanning electron microscopy (SEM) photograph showed the BZT powder as spherical in shape with uniform nanosized features.

scholarly journals Phase Equilibria in the Nb-Rich Region of Al-Nb-Sn at 900 and 1200 °C

Materials ◽  
2019 ◽  
Vol 12 (17) ◽  
pp. 2759 ◽  
Author(s):  
Ioannis Papadimitriou ◽  
Claire Utton ◽  
Panos Tsakiropoulos
Keyword(s):  
Crystal Structure ◽  
Phase Equilibria ◽  
Ternary Phase ◽  
X Ray Diffraction ◽  
High Solubility ◽  
Rich Region ◽  
X Ray ◽  
Heat Treated ◽  
Aero Engine ◽  
Scanning Electron

The Al-Nb-Sn phase diagram was studied experimentally in the Nb-rich region to provide important phase equilibria information for alloy design of Nb-silicide based materials for aero engine applications. Three alloys were produced: Nb-17Al-17Sn, Nb-33Al-13Sn and Nb-16Al-20Sn (at.%). As-cast and heat-treated alloys (900 and 1200 °C) were analysed using XRD (X-ray diffraction) and SEM/EDS (scanning electron microscopy/ electron dispersive x-ray spectroscopy). Tin showed a high solubility in Nb2Al, reaching up to 21 at.% in the Sn-rich areas, substituting for Al atoms. Tin and Al also substituted for each other in the A15 phases (Nb3Al and Nb3Sn). Tin showed limited solubility in NbAl3, not exceeding 3.6 at.% as it substituted Al atoms. The solubility of Al in NbSn2 varied from 4.8 to 6.8 at.%. A ternary phase, Nb5Sn2Al with the tI32 W5Si3 crystal structure, was found to be stable. This phase was observed in the 900 °C heat-treated samples, but not in the 1200 °C heated samples.

The Effect of Water Content on the Formation of TiO2 Nanotubes in Ethylene Glycol

2010 ◽  
Vol 173 ◽  
pp. 102-105 ◽  
Author(s):  
Khairul Arifah Saharudin ◽  
Srimala Sreekantan
Keyword(s):  
Crystal Structure ◽  
Aspect Ratio ◽  
Ethylene Glycol ◽  
Water Content ◽  
Anatase Phase ◽  
Xrd Analysis ◽  
X Ray Diffraction ◽  
X Ray ◽  
Degradation Of Methyl Orange ◽  
Scanning Electron

In this paper, anodization of Ti foil was carried out in ethylene glycol (EG) containing 5 wt% NH4F solution and 0 to 1.5 wt% of water at 50 V for 60 min. The pH of the bath was kept constant at ~pH7. The crystal structure was studied by X-Ray Diffraction (XRD) analysis, and the morphology was observed via field emission scanning electron microscopy (FESEM). TiO2 nanotube with aspect ratio of 100 was obtained in EG containing less than 1wt % water. The nanotubes wall was very smooth. Increasing the water content > 1wt % results in short nanotubes of approximately 6.2μm with aspect ratio of 62. As anodized, nanotubes were amorphous and annealed at 400 °C promote 100 % anatase phase. Photocatalytic activity of the nanotubes produced at different water content was also evaluated by the degradation of methyl orange and the detail of the observation was discussed thoroughly in this paper.

Crystal Structure of BiFeO3 Synthesized Using the Hydrothermal Processing

2014 ◽  
Vol 602-603 ◽  
pp. 947-950
Author(s):  
Zhen Wang ◽  
Hai Yan Chen ◽  
Lin Qiang Gao ◽  
Xin Zou
Keyword(s):  
Crystal Structure ◽  
Electron Microscopy ◽  
Thermal Analysis ◽  
Scanning Electron Microscopy ◽  
Single Phase ◽  
Hydrothermal Processing ◽  
Optimal Conditions ◽  
X Ray Diffraction ◽  
X Ray ◽  
Scanning Electron

BiFeO3 nanoparticles were successfully synthesized by a hydrothermal method by a mineralizer (KNO3). Structural characterization was performed by thermal analysis, powder X-ray diffraction (XRD) and scanning electron microscopy (TEM).The results showed that the products were perovskite structure BiFeO3 powders. Optimal conditions for the synthesis of single-phase BiFeO3 ceramics were obtained.

FABRICATION AND CHARACTERISTICS OF ALN NANOWIRES

2001 ◽  
Vol 15 (30) ◽  
pp. 1455-1458 ◽  
Author(s):  
H. CHEN ◽  
X. K. LU ◽  
S. Q. ZHOU ◽  
X. H. HAO ◽  
Z. X. WANG
Keyword(s):  
Crystal Structure ◽  
Electron Microscopy ◽  
Transmission Electron Microscopy ◽  
Single Phase ◽  
X Ray Diffraction ◽  
X Ray ◽  
Selected Area Electron Diffraction ◽  
Transmission Electron ◽  
Sublimation Method ◽  
Scanning Electron

Single phase AlN nanowires are fabricated by a sublimation method. They were characterized by means of X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), typical selected area electron diffraction (SAED) and high-resolution transmission electron microscopy (HRTEM). The SEM and TEM images show that most of the nanowires have diameters of about 10–60 nm. The crystal structure of AlN nanowires revealed by XRD, SAED and HRTEM shows the AlN nanowires have a wurtzite structure.

scholarly journals Synthesis and Catalase Mimic Activity of MnO2 Nano Powder Prepared by Hydrothermal Process

2019 ◽  
Vol 27 (2) ◽  
pp. 228-237 ◽  
Author(s):  
Rashed T. Rasheed ◽  
Sariya D. Al-Algawi ◽  
Rosul M. N.
Keyword(s):  
Crystal Structure ◽  
Electron Microscopy ◽  
Annealing Temperature ◽  
Hydrothermal Process ◽  
X Ray Diffraction ◽  
X Ray ◽  
Nano Powder ◽  
Atomic Force ◽  
Different Temperatures ◽  
Scanning Electron

Manganese dioxide (MnO2) nanopowder has been synthesized by hydrothermal method. MnO2 was annealed at different temperatures (250, 400, 550, 700˚C). The crystal structure and surface morphology of these nanostructures were characterized by X-ray diffraction (XRD), Atomic Force Microscope (AFM) and Scanning Electron Microscopy (SEM). The catalase mimic activity (catalytic activity) of MnO2 against hydrogen peroxide (H2O2) was studied by using the new method and found that 400˚C is the best annealing temperature.

scholarly journals Characterization of K6Ta10.8O30 Microrods with Tetragonal Tungsten Bronze-Like Structure Obtained from Tailings from the Penouta Sn-Ta-Nb Deposit

Nanomaterials ◽  
2020 ◽  
Vol 10 (11) ◽  
pp. 2289
Author(s):  
Belén Sotillo ◽  
Lorena Alcaraz ◽  
Félix A. López ◽  
Paloma Fernández
Keyword(s):  
Crystal Structure ◽  
Tungsten Bronze ◽  
X Ray Diffraction ◽  
Tetragonal Tungsten Bronze ◽  
X Ray ◽  
The North ◽  
Recovered Material ◽  
North Of Spain ◽  
Scanning Electron

In this work, a deep characterization of the properties of K6Ta10.8O30 microrods has been performed. The starting material used to grow the microrods has been recovered from mining tailings coming from the Penouta Sn-Ta-Nb deposit, located in the north of Spain. The recovered material has been submitted to a thermal treatment to grow the microrods. Then, they have been characterized by scanning electron microscopy, X-ray diffraction, micro-Raman and micro-photoluminescence. The results of our study confirm that the K6Ta10.8O30 microrods have a tetragonal tungsten bronze-like crystal structure, which can be useful for ion-batteries and photocatalysis.

Sign in / Sign up

Export Citation Format

Share Document