The shear bond strength of resin-based composite to white mineral trioxide aggregate

2012 ◽  
Vol 143 (8) ◽  
pp. e40-e45 ◽  
Author(s):  
Prasanna Neelakantan ◽  
Deeksha Grotra ◽  
Chandragiri Venkata Subbarao ◽  
Franklin Garcia-Godoy
Keyword(s):  
Bond Strength ◽  
Shear Bond Strength ◽  
Mineral Trioxide Aggregate ◽  
White Mineral

scholarly journals Shear bond strength of novel calcium aluminate-based cement (EndoBinder) to root dentine

2014 ◽  
Vol 08 (04) ◽  
pp. 498-503 ◽  
Author(s):  
Lucas da Fonseca Roberti Garcia ◽  
Hebert Luis Rossetto ◽  
Fernanda de Carvalho Panzeri Pires-de-Souza
Keyword(s):  
Bond Strength ◽  
Calcium Aluminate ◽  
Shear Bond Strength ◽  
Testing Machine ◽  
Mineral Trioxide Aggregate ◽  
Acrylic Resin ◽  
Promising Alternative ◽  
Mean Values ◽  
Significant Difference ◽  
Molar Teeth

ABSTRACT Objective: To evaluate the shear bond strength of a novel calcium aluminate-based cement, EndoBinder (EB), to dentine in comparison with Grey and White Mineral Trioxide Aggregate (MTA). Materials and Methods: Root canal hemi-sections obtained from 30 extracted molar teeth were embedded in self-polymerized acrylic resin and were grounded wet in order to obtain a flat dentine surface. Next, the roots were randomly assigned into three groups (n = 10), according to the cement used, as follows: EB: EndoBinder; WMTA: White MTA and GMTA: Grey MTA. The shear bond strength test was performed using a Universal Testing Machine (0.5 mm/min) and the data were submitted to statistical analysis (1-way ANOVA and Tukey tests, P < 0.05). Results: EB presented the highest shear bond strength values; however, there was no statistically significant difference in comparison with GMTA (P > 0.05). WMTA presented the lowest mean values, which were significant in comparison with EB (P < 0.05). Conclusions: The novel calcium aluminate-based cement presented higher shear bond strength than WMTA, and should be considered as a promising alternative in endodontic therapy.

scholarly journals Does Delayed Restoration Improve Shear Bond Strength of Different Restorative Protocols to Calcium Silicate-Based Cements?

Materials ◽  
2018 ◽  
Vol 11 (11) ◽  
pp. 2216 ◽  
Author(s):  
Paulo Palma ◽  
Joana Marques ◽  
Rui Falacho ◽  
Alexandra Vinagre ◽  
João Santos ◽  
...  
Keyword(s):  
Bond Strength ◽  
Calcium Silicate ◽  
Shear Bond Strength ◽  
Proper Time ◽  
Testing Machine ◽  
Glass Ionomer Cement ◽  
Mineral Trioxide Aggregate ◽  
Bonding System ◽  
Post Hoc ◽  
Ionomer Cement

The purpose of the present study was to assess the proper time to perform a restoration (immediately or delayed) after placement of two calcium silicate-based cements (CSCs) and to test the performance of two different restorative protocols regarding shear bond strength (SBS). Seventy-five acrylic blocks were randomly divided into five groups (n = 15). Specimens were filled with either ProRoot MTA (Dentsply Tulsa Dental) or Biodentine (Septodont). The restoration was performed at an immediate (12 min) or delayed (seven days) timeframe, using a resin-based flowable composite (SDR) (bonded to the CSC using a universal bonding system) or glass ionomer cement (GIC) as restorative materials. SBS was measured using a universal testing machine. Fractured surfaces were evaluated, and the pattern was registered. Statistical analysis was performed using the Dunn–Sidak post hoc test (P < 0.05). Biodentine/immediate SDR showed the highest mean SBS value (4.44 MPa), with statistically significant differences when compared to mineral trioxide aggregate (MTA)/GIC (1.14 MPa) and MTA/immediate SDR (1.33 MPa). MTA/GIC and MTA/immediate SDR did not present significant differences regarding SBS. No statistical differences were verified concerning mean SBS between both CSCs within the 7 day groups. MTA/delayed SDR (3.86 MPa) presented statistical differences compared to MTA/immediate SDR, whereas no differences were observed regarding Biodentine performance (Biodentine/immediate SDR and Biodentine/delayed SDR (3.09 MPa)). Bonding procedures directly on top of MTA might be preferably performed at a delayed timeframe, whereas Biodentine might allow for immediate restoration.

scholarly journals Removal of White Mineral Trioxide Aggregate Cement: A Promising Approach

2013 ◽  
Vol 2013 ◽  
pp. 1-7 ◽  
Author(s):  
Mohammad Ali Saghiri ◽  
Franklin Garcia-Godoy ◽  
James L. Gutmann ◽  
Nader Sheibani ◽  
Armen Asatourian ◽  
...  
Keyword(s):  
Hydrochloric Acid ◽  
Bond Strength ◽  
Testing Machine ◽  
Mineral Trioxide Aggregate ◽  
Sem Analysis ◽  
The Other ◽  
Effective Solution ◽  
Glass Tubes ◽  
Push Out ◽  
White Mineral

Removal of MTA from dentin by applying 37% hydrochloric acid (HCl) to reduce microhardness and push-out bond strength. Forty dentin slices were filled with WMTA and divided into two groups (n=20). Ten slices remained untreated while others were exposed to either HCl or phosphate buffer saline (PBS) and all samples were subjected to pushout test. The mode of bond failures was determined by SEM analysis. Later, twenty glass tubes were filled with WMTA and divided into two groups (n=10). One side of tube was exposed to HCl or PBS while the other side remained untreated and the microhardness was analyzed by testing machine. HCl showed significantly lower pushout strength and microhardness values (P=0.0001), (P=0.0001). HCl treated samples showed mixed bond failures dominantly, while PBS samples mostly showed adhesive failures. The results of this study can suggest the 37% HCl as an effective solution to aid the removal of MTA from the dentin surfaces.

Sign in / Sign up

Export Citation Format

Share Document