Fire and thermal resistance properties of chemically treated ligno-cellulosic coconut fabric–reinforced polymer eco-nanocomposites

2016 ◽  
Vol 47 (1) ◽  
pp. 104-124 ◽  
Author(s):  
N Rajini ◽  
JT Winowlin Jappes ◽  
I Siva ◽  
A Varada Rajulu ◽  
S Rajakarunakaran
Keyword(s):  
Electron Microscopy ◽  
Morphological Changes ◽  
Mass Loss Rate ◽  
Fiber Surface ◽  
Reinforced Polymer ◽  
Transmission Electron ◽  
Hybridization Effect ◽  
Flammability Characteristics ◽  
Polyester Matrix ◽  
Thermal Stability Of

The present work was aimed to develop naturally woven coconut sheath/polyester biocomposites. In these composites, montmorillonite nanoclay (5 wt%) was used as a second filler. The heat releasing rate and other flammability properties were studied using cone calorimeter. The coconut sheath reinforcement in polyester matrix significantly decreased the heat releasing rate when compared to that of the pristine polyester. However, the time to ignite the composite material was shorter than that of the pure polyester. The morphological changes on the fiber surface by the chemical modification significantly influenced the heat-releasing rate and other flammability characteristics due to better interfacial bonding. The hybridization effect of 5 wt% of nanoclay could greatly decrease the heat release rate and the mass loss rate of the composites by char formation mechanism. The characterization techniques such as the scanning electron microscopy and the transmission electron microscopy were used to study the morphological state of the fiber surface and dispersion of clay in the polyester nanocomposites. The thermogravimetric analysis was also carried out to study the effect of the nanoclay on the thermal stability of the coconut sheath/polyester composites at higher temperatures.

Ultrastructural Study of Rat Colon Following Psyllium Ingestion

1985 ◽  
Vol 43 ◽  
pp. 580-581
Author(s):  
F.G. Lightfoot ◽  
L.E. Grau ◽  
M.M. Cassidy ◽  
G.R. Tadvalkar ◽  
G.V. Vahouny
Keyword(s):  
Electron Microscopy ◽  
Morphological Changes ◽  
Large Population ◽  
Rat Colon ◽  
Gastrointestinal Disorders ◽  
Luminal Surface ◽  
Fecal Material ◽  
Transmission Electron ◽  
Morphologic Analysis ◽  
Irritable Bowel

Psyllium hydrophillic mucilloid is a natural gelling fiber consumed by a large population of our society. It is used as a bulk-producing laxative and in the treatment of gastrointestinal disorders such as “Irritable Bowel Syndrome”. The literature pertaining to the ultrastructural effects of this agent is sparse.This study documents morphological changes induced by psyllium. Animals fed a diet containing 2% psyllium for four weeks were subsequently sacrificed and processed for scanning and transmission electron microscopy. The colon contained fecal material combined with psyllium which conformed to the contour of the luminal surface. This mixture formed surface replicas of the intestinal mucosa. These replicas and their related colonic sites were processed for morphologic analysis.

Correlation Between Cellular Functions and Morphological Changes of Human Trophoblast in Vitro

1975 ◽  
Vol 33 ◽  
pp. 600-601
Author(s):  
John C. Garancis ◽  
Robert O. Hussa ◽  
Michael T. Story ◽  
Donald Yorde ◽  
Roland A. Pattillo
Keyword(s):  
Electron Microscopy ◽  
Cellular Proliferation ◽  
Morphological Changes ◽  
Culture Fluid ◽  
Cellular Functions ◽  
Human Trophoblast ◽  
Transmission Electron ◽  
Marked Activity ◽  
Malignant Trophoblast

Human malignant trophoblast cells in continuous culture were incubated for 3 days in medium containing 1 mM N6-O2'-dibutyryl cyclic adenosine 3':5'-monophosphate (dibutyryl cyclic AMP) and 1 mM theophylline. The culture fluid was replenished daily. Stimulated cultures secreted many times more chorionic gonadotropin and estrogens than did control cultures in the absence of increased cellular proliferation. Scanning electron microscopy revealed remarkable surface changes of stimulated cells. Control cells (not stimulated) were smooth or provided with varying numbers of microvilli (Fig. 1). The latter, usually, were short and thin. The surface features of stimulated cells were considerably different. There was marked increase of microvilli which appeared elongated and thick. Many cells were covered with confluent polypoid projections (Fig. 2). Transmission electron microscopy demonstrated marked activity of cytoplasmic organelles. Mitochondria were increased in number and size; some giant forms with numerous cristae were observed.

scholarly journals Zinc Oxide and Silver Nanoparticle Effects on Intestinal Bacteria

Materials ◽  
2021 ◽  
Vol 14 (10) ◽  
pp. 2489
Author(s):  
Ami Yoo ◽  
Mengshi Lin ◽  
Azlin Mustapha
Keyword(s):  
Electron Microscopy ◽  
Zinc Oxide ◽  
Morphological Changes ◽  
Intestinal Bacteria ◽  
Bacterial Cells ◽  
Ag Nps ◽  
Zno Nps ◽  
Bifidobacterium Animalis ◽  
Transmission Electron

The application of nanoparticles (NPs) for food safety is increasingly being explored. Zinc oxide (ZnO) and silver (Ag) NPs are inorganic chemicals with antimicrobial and bioactive characteristics and have been widely used in the food industry. However, not much is known about the behavior of these NPs upon ingestion and whether they inhibit natural gut microflora. The objective of this study was to investigate the effects of ZnO and Ag NPs on the intestinal bacteria, namely Escherichia coli, Lactobacillus acidophilus, and Bifidobacterium animalis. Cells were inoculated into tryptic soy broth or Lactobacilli MRS broth containing 1% of NP-free solution, 0, 12, 16, 20 mM of ZnO NPs or 0, 1.8, 2.7, 4.6 mM Ag NPs, and incubated at 37 °C for 24 h. The presence and characterization of the NPs on bacterial cells were investigated by scanning electron microscopy (SEM), transmission electron microscopy (TEM), and energy-dispersive X-ray spectroscopy (EDS). Membrane leakage and cell viability were assessed using a UV-visible spectrophotometer and confocal electron microscope, respectively. Numbers of treated cells were within 1 log CFU/mL less than those of the controls for up to 12 h of incubation. Cellular morphological changes were observed, but many cells remained in normal shapes. Only a small amount of internal cellular contents was leaked due to the NP treatments, and more live than dead cells were observed after exposure to the NPs. Based on these results, we conclude that ZnO and Ag NPs have mild inhibitory effects on intestinal bacteria.

scholarly journals Human serum activates the tegument of female schistosomes and supports recovery from Praziquantel

2020 ◽  
Author(s):  
Franziska Winkelmann ◽  
Marcus Frank ◽  
Anne Rabes ◽  
Nicole Koslowski ◽  
Cindy Schulz ◽  
...  
Keyword(s):  
Electron Microscopy ◽  
Human Serum ◽  
Immune Reaction ◽  
Morphological Changes ◽  
Expression Profiles ◽  
Female Worm ◽  
Male Worm ◽  
Transmission Electron ◽  
Gene Expression Analyses ◽  
Males And Females

AbstractSchistosomiasis is one of the most devastating parasitic disease in the world. Schistosoma spp. survive for decades within the vasculature of their human hosts. They have evolved a vast array of mechanisms to avoid the immune reaction of the host. Due to their sexual dimorphism, with the female worm lying within the gynecophoric canal of the male worm, it is the male that is exposed to the immediate environment and the soluble parts of the host’s immune response. To understand how the worms are so successful in fending off the immune attacks of the host, comparative analyses of both worm sexes in human serum (with or without Praziquantel) were performed using scanning electron microscopy, transmission electron microscopy, and immunohistochemistry. Further, gene expression analyses of tegument-specific genes were performed. Following the incubation in human serum, males and females out of pairs show morphological changes such as an altered structure of the pits below the surface and an increased number of pits per area. In addition, female schistosomes presented a marked tuft-like repulsion of their opsonized surface. The observed resistance of females to Praziquantel seemed to depend on active proteins in the human serum. Moreover, different expression profiles of tegument-specific genes indicate different functions of female_single and male_single teguments in response to human serum. Our results indicate that female schistosomes developed different evasion strategies toward the host’s immune system in comparison to males that might lead to more robustness and has to be taken into account for the development of new anti-schistosomal drugs.

scholarly journals Cytochemical localization of calcium and Ca2+,Mg2(+)-adenosine triphosphatase in colchicine-altered rat incisor ameloblasts.

1990 ◽  
Vol 38 (10) ◽  
pp. 1469-1478 ◽  
Author(s):  
D R Eisenmann ◽  
A H Salama ◽  
A M Zaki ◽  
S H Ashrafi
Keyword(s):  
Electron Microscopy ◽  
Transmission Electron Microscopy ◽  
Adenosine Triphosphatase ◽  
Morphological Changes ◽  
Rat Incisor ◽  
Cytochemical Localization ◽  
Early Maturation ◽  
Transmission Electron ◽  
Maturation Stages ◽  
Secretory Transport

Colchicine is known to affect secretory, transport, and degradative functions of ameloblasts. The effects of colchicine on membrane-associated calcium and Ca2+,Mg2(+)-ATPase in secretory and maturation ameloblasts were investigated cytochemically. The pyroantimonate (PPA) method was used for localizing calcium and a modified Wachstein-Meisel medium was used to localize Ca2+,Mg2(+)-ATPase. Sections representing secretory and early maturation stages were examined by transmission electron microscopy. Morphological changes induced by colchicine included dislocated organelles and other well-established reactions to such anti-microtubule drugs. Calcium pyroantimonate (Ca-PA) deposits in most ameloblast types were markedly reduced, with the greater reduction occurring in those cells more severely altered morphologically. However, the cell membranes of both control and experimental smooth-ended maturation ameloblasts were essentially devoid of Ca-PA. The normal distribution and intensity of Ca2+,Mg2(+)-ATPase was not affected by colchicine. Because the observed reduction of membrane-associated calcium is apparently not mediated by Ca2+,Mg2(+)-ATPase in this case, other aspects of the calcium regulating system of ameloblasts are apparently targeted by colchicine.

Mechanical Properties and Microstructure Evolution of Typical Over-Aging State Al-Zn-Mg-Cu Alloy during Thermal Exposure

2021 ◽  
Vol 1026 ◽  
pp. 84-92
Author(s):  
Tao Qian Cheng ◽  
Zhi Hui Li
Keyword(s):  
Electron Microscopy ◽  
Mechanical Properties ◽  
Mechanical Property ◽  
Electrical Conductivity ◽  
Transmission Electron Microscopy ◽  
Tensile Strength ◽  
Thermal Exposure ◽  
Cu Alloy ◽  
Transmission Electron ◽  
Thermal Stability Of

Al-Zn-Mg-Cu alloy have been widely used in aerospace industry. However, there is still a lack of research on thermal stability of Al-Zn-Mg-Cu alloy products. In the present work, an Al-Zn-Mg-Cu alloy with T79 and T74 states was placed in the corresponding environment for thermal exposure experiments. Performance was measured by tensile strength, hardness and electrical conductivity. In this paper, precipitation observation was analyzed by transmission electron microscopy (TEM) and high-resolution transmission electron microscopy (HREM). The precipitations of T79 state alloy were GPⅡ zone, η' phase and η phase while the ultimate tensile strength, hardness and electrical conductivity were 571MPa, 188.2HV and 22.2MS×m-1, respectively. The mechanical property of T79 state alloy decreased to 530MPa and 168.5HV after thermal exposure. The diameter of precipitate increased and the precipitations become η' and η phase at the same time. During the entire thermal exposure, T74 state alloy had the same mechanical property trend as T79 state alloy. The precipitate diameter also increased while the types of precipitate did not change under thermal exposure. The size of precipitates affected the choice of dislocation passing through the particles to affect the mechanical properties.

scholarly journals Morphological changes and bioaccumulation in response to cadmium exposure in Morchella spongiola, a fungus with potential for detoxification

2021 ◽  
Author(s):  
Hongyan Xu ◽  
Jing Guo ◽  
Qing Meng ◽  
Zhanling Xie
Keyword(s):  
Electron Microscopy ◽  
Morphological Changes ◽  
Intracellular Accumulation ◽  
Tolerance Mechanism ◽  
Edible Fungi ◽  
Transmission Electron Microscopy Analysis ◽  
Transmission Electron ◽  
Electron Microscopy Analysis ◽  
Microscopy Analysis ◽  
Micro Morphology

<i>Morchella</i> is a genus of edible fungi with strong resistance to Cd and the ability to accumulate it in the mycelium. However, the mechanisms conferring Cd resistance in <i>Morchella</i> are unknown. In the present study, morphological and physiological responses to Cd were evaluated in the mycelia of <i>Morchella spongiola</i>. Variations in hyphal micro-morphology including twisting, folding and kinking in mycelia exposed to different Cd concentrations (0.15, 0.9, 1.5, 2.4, 5.0 mg/L) were observed using scanning electron microscopy. Deposition of Cd precipitates on cell surfaces (at Cd concentrations > 2.4 mg/L) was shown by SEM-EDS. Transmission electron microscopy analysis of cells exposed to different concentrations of Cd revealed the loss of intracellular structures and the localization of Cd depositions inside/outside the cell. FTIR analysis showed that functional groups such as C=O, -OH, -NH and -CH could be responsible for Cd binding on the cell surface of <i>M. spongiola</i>. In addition, intracellular accumulation was observed in cultures at low Cd concentrations (< 0.9 mg/L), while extracellular adsorption occurred at higher concentrations. These results provide valuable information on the Cd tolerance mechanism in <i>M. spongiola</i> and constitute a robust foundation for further studies on fungal bioremediation strategies.

Sign in / Sign up

Export Citation Format

Share Document