scholarly journals Effect of Traverse Speed on the Defect Characteristic, Microstructure, and Mechanical Property of Friction Stir Welded T-Joints of Dissimilar Mg/Al Alloy

2020 ◽  
Vol 2020 ◽  
pp. 1-15
Author(s):  
Sun Tao ◽  
Wu Siyu ◽  
Yifu Shen ◽  
Jin Jiayi ◽  
Lu Jiazhu ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Traverse Speed ◽  
Optical Microscope ◽  
Welding Parameters ◽  
Al Alloy ◽  
Lap Joint ◽  
T Joints ◽  
Friction Stir ◽  
Metallurgical Structure ◽  
Characteristic Microstructure

The AZ31 B/2024-T4 T-lap-joint was successfully fabricated by friction stir welding (FSW) with different welding parameters. The defect characteristics and metallurgical structure were observed and analyzed using optical microscope (OM) and scanning electron microscopy (SEM). Besides, the effects of defects and welding parameters on mechanical properties were investigated. The results show that an effective metallurgical reaction zone can be formed between Mg and Al (Mg-Al MRZ) and the island structures and lamellar structures appeared in the Mg-Al MRZ. The T-joints without tunnel defects can be obtained and the excellent mechanical properties of the T-joint were achieved using the welding speed of 50 mm/min. The tensile strength along the skin and the stringer was mainly affected by the kiss bonding defects.

scholarly journals Effect of Stirring Pin Rotation Speed on Microstructure and Mechanical Properties of 2A14-T4 Alloy T-Joints Produced by Stationary Shoulder Friction Stir Welding

Materials ◽  
2021 ◽  
Vol 14 (8) ◽  
pp. 1938
Author(s):  
Haifeng Yang ◽  
Hongyun Zhao ◽  
Xinxin Xu ◽  
Li Zhou ◽  
Huihui Zhao ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Friction Stir Welding ◽  
Rotation Speed ◽  
Weld Nugget ◽  
Al Alloy ◽  
Nugget Zone ◽  
T Joints ◽  
Friction Stir ◽  
Stationary Shoulder ◽  
Microstructure And Mechanical Properties

In this study, 2A14-T4 Al-alloy T-joints were prepared via stationary shoulder friction stir welding (SSFSW) technology where the stirring pin’s rotation speed was set as different values. In combination with the numerical simulation results, the macro-forming, microstructure, and mechanical properties of the joints under different welding conditions were analyzed. The results show that the thermal cycle curves in the SSFSW process are featured by a steep climb and slow decreasing variation trends. As the stirring pin’s rotation speed increased, the grooves on the weld surface became more obvious. The base and rib plates exhibit W- or N-shaped hardness distribution patterns. The hardness of the weld nugget zone (WNZ) was high but was lower than that of the base material. The second weld’s annealing effect contributed to the precipitation and coarsening of the precipitated phase in the first weld nugget zone (WNZ1). The hardness of the heat affect zone (HAZ) in the vicinity of the thermo-mechanically affected zone (TMAZ) dropped to the minimum. As the stirring pin's rotation speed increased, the tensile strengths of the base and rib plates first increased and then dropped. The base and rib plates exhibited ductile and brittle/ductile fracture patterns, respectively.

scholarly journals Effect of Friction Stir Welding Parameters on the Microstructure and Mechanical Properties of AA2024-T4 Aluminum Alloy

2018 ◽  
Vol 8 (1) ◽  
pp. 2493-2498 ◽  
Author(s):  
A. W. El-Morsy ◽  
M. Ghanem ◽  
H. Bahaitham
Keyword(s):  
Mechanical Properties ◽  
Aluminum Alloy ◽  
Friction Stir Welding ◽  
Cross Section ◽  
High Performance ◽  
Traverse Speed ◽  
Butt Joint ◽  
Welding Parameters ◽  
Friction Stir

In this work, the effects of rotational and traverse speeds on the 1.5 mm butt joint performance of friction stir welded 2024-T4 aluminum alloy sheets have been investigated. Five rotational speeds ranging from 560 to 1800 rpm and five traverse speeds ranging from 11 to 45 mm/min have been employed. The characterization of microstructure and the mechanical properties (tensile, microhardness, and bending) of the welded sheets have been studied. The results reveal that by varying the welding parameters, almost sound joints and high performance welded joints can be successfully produced at the rotational speeds of 900 rpm and 700 rpm and the traverse speed of 35 mm/min. The maximum welding performance of joints is found to be 86.3% with 900 rpm rotational speed and 35 mm/min traverse speed. The microhardness values along the cross-section of the joints show a dramatic drop in the stir zone where the lowest value reached is about 63% of the base metal due to the softening of the welded zone caused by the heat input during joining.

Effects of bottom plate in friction stir welding of AA6061-T6

2020 ◽  
Vol 118 (1) ◽  
pp. 108
Author(s):  
M.A. Vinayagamoorthi ◽  
M. Prince ◽  
S. Balasubramanian
Keyword(s):  
Mechanical Properties ◽  
Axial Load ◽  
Weld Zone ◽  
Welding Process ◽  
Bottom Plate ◽  
Welding Parameters ◽  
Nugget Zone ◽  
Friction Stir ◽  
Weld Joints ◽  
Fine Grain

The effects of 40 mm width bottom plates on the microstructural modifications and the mechanical properties of a 6 mm thick FSW AA6061-T6 joint have been investigated. The bottom plates are placed partially at the weld zone to absorb and dissipate heat during the welding process. An axial load of 5 to 7 kN, a rotational speed of 500 rpm, and a welding speed of 50 mm/min are employed as welding parameters. The size of the nugget zone (NZ) and heat-affected zone (HAZ) in the weld joints obtained from AISI 1040 steel bottom plate is more significant than that of weld joints obtained using copper bottom plate due to lower thermal conductivity of steel. Also, the weld joints obtained using copper bottom plate have fine grain microstructure due to the dynamic recrystallization. The friction stir welded joints obtained with copper bottom plate have exhibited higher ductility of 8.9% and higher tensile strength of 172 MPa as compared to the joints obtained using a steel bottom plate.

scholarly journals Thermo-mechanical analysis of linear welding stage in friction stir welding - influence of welding parameters

2021 ◽  
pp. 186-186
Author(s):  
Darko Veljic ◽  
Marko Rakin ◽  
Aleksandar Sedmak ◽  
Nenad Radovic ◽  
Bojan Medjo ◽  
...  
Keyword(s):  
Friction Stir Welding ◽  
Heat Generation ◽  
Welding Speed ◽  
Reaction Force ◽  
Material Model ◽  
Element Model ◽  
Welding Parameters ◽  
Al Alloy ◽  
Friction Stir ◽  
Fsw Parameters

The influence of friction stir welding (FSW) parameters on thermo-mechanical behaviour of the material during welding is analysed. An aluminium alloy is considered (Al 2024 T351), and different rotating speed and welding speed are applied. Finite element model consists of the plate (Al alloy), backing plate and welding tool, and it is formed and solved in software package Simulia Abaqus. The influence of the welding conditions on material behaviour is taken into account by application of the Johnson-Cook material model. The rotation of the tool affects the results: if increased, it contributes to an increase of friction-generated heat intensity. The other component of the generated heat, the plastic deformation of the material, is negligibly changed. When the welding speed is increased, the intensity of friction-generated heat decreases, while the heat generation due to plastic deforming increases. Combined, these two effects cause small change of the total heat generation. For the same welded joint length, the plate welded by lower speed will be heated more intensively. The changes of the heat generation influence both the temperature field and reaction force, which are also considered.

Sign in / Sign up

Export Citation Format

Share Document