scholarly journals Mechanical Properties of Steel Fiber-Reinforced Concrete by Vibratory Mixing Technology

2018 ◽  
Vol 2018 ◽  
pp. 1-11 ◽  
Author(s):  
Yuanxun Zheng ◽  
Xiaolong Wu ◽  
Guangxian He ◽  
Qingfang Shang ◽  
Jianguo Xu ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Reinforced Concrete ◽  
Steel Fiber ◽  
Fiber Reinforced Concrete ◽  
Bending Test ◽  
Fiber Reinforced ◽  
Steel Fiber Reinforced Concrete ◽  
Steel Fiber Concrete ◽  
Mixing Method ◽  
Splitting Tensile Test

As a kind of important engineering material, steel fiber-reinforced concrete was used widely in civil engineering. Up to now, steel fiber-reinforced concrete was usually produced by the traditional mixing method. For the reason of uniform distribution of fiber, the reinforcement of mechanical properties of concrete was inadequately performed. In this paper, C50 steel fiber-reinforced concrete and C60 steel fiber-reinforced concrete were manufactured by traditional mixing and vibratory mixing methods, respectively, and then, the cube compression test, flexural test, splitting tensile test, and the bending test were carried out. The reinforcement effects of mechanical properties were analyzed by comparing the traditional mixing and vibratory mixing methods. The results show that vibratory mixing can effectively improve the distribution of steel fibers in concrete and can increase the density of steel fiber concrete, and therefore, it effectively improves the mechanical properties of steel fiber-reinforced concrete when compared to the traditional mixing method.

scholarly journals The Effect of Vibration Mixing on the Mechanical Properties of Steel Fiber Concrete with Different Mix Ratios

Materials ◽  
2021 ◽  
Vol 14 (13) ◽  
pp. 3669
Author(s):  
Chunyu Zhang ◽  
Yikai Sun ◽  
Jianguo Xu ◽  
Bo Wang
Keyword(s):  
Mechanical Properties ◽  
Reinforced Concrete ◽  
Steel Fiber ◽  
Volume Ratio ◽  
Fiber Reinforced Concrete ◽  
Fiber Reinforced ◽  
Steel Fiber Reinforced Concrete ◽  
Fiber Volume ◽  
Fiber Concrete ◽  
Steel Fiber Concrete

This work addresses how vibration stirring, steel-fiber volume ratio, and matrix strength affect the mechanical properties of steel-fiber-reinforced concrete. The goal of the work is to improve the homogeneity of steel-fiber-reinforced concrete, which is done by comparing the mechanical properties of steel-fiber-reinforced concrete fabricated by ordinary stirring with that fabricated by vibration stirring. The results show that the mechanical properties of steel-fiber-reinforced concrete produced by vibration mixing are better than those produced by ordinary mixing. The general trend is that the mechanical properties of steel-fiber concrete have a linear relationship with the matrix strength and the volume ratio of steel fiber. The best mechanical properties are obtained for a steel-fiber volume ratio of less than 1%. We have also established calculation models for the mechanical performance index of vibration, mixing steel-fiber concrete based on the test results. Microscopic studies show that vibration stirring optimizes the microstructure of the transition zone between the concrete interface and the slurry, and improves the homogeneity of the steel-fiber-reinforced concrete, and enhances the adhesion between the mixture components.

Study on Retrofitting and Strengthening of Reinforced Concrete Beams Using Fibrous Concrete

2021 ◽  
Vol 9 (8) ◽  
pp. 1676-1684
Author(s):  
Natalia Sharma
Keyword(s):  
Mechanical Properties ◽  
Reinforced Concrete ◽  
Steel Fiber ◽  
Concrete Beams ◽  
Fiber Reinforced Concrete ◽  
Steel Fibers ◽  
Reinforced Concrete Beams ◽  
Cement Matrix ◽  
Fiber Reinforced ◽  
Steel Fiber Reinforced Concrete

Abstract: Reinforced concrete structures are frequently in need of repair and strengthening as a result of numerous environmental causes, ageing, or material damage under intense stress conditions, as well as mistakes made during the construction process. RC structures are repaired using a variety of approaches nowadays. The usage of FRC is one of the retrofitting strategies. Steel fiber reinforced concrete (SFRC) was used in this investigation because it contains randomly dispersed short discrete steel fibers that operate as internal reinforcement to improve the cementitious composite's characteristics (concrete). The main rationale for integrating small discrete fibers into a cement matrix is to reduce the amount of cement used. The principal reason for incorporating short discrete fibers into a cement matrix is to reduce cracking in the elastic range, increase the tensile strength and deformation capacity and increase the toughness of the resultant composite. These properties of SFRC primarily depend upon length and volume of Steel fibers used in the concrete mixture. In India, the steel fiber reinforced concrete (SFRC) has seen limited applications in several structures due to the lack of awareness, design guidelines and construction specifications. Therefore, there is a need to develop information on the role of steel fibers in the concrete mixture. The experimental work reported in this study includes the mechanical properties of concrete at different volume fractions of steel fibers. These mechanical properties include compressive strength, split tensile strength and flexural strength and to study the effect of volume fraction and aspect ratio of steel fibers on these mechanical properties. However, main aim of the study was significance of reinforced concrete beams strengthened with fiber reinforced concrete layer and to investigate how these beams deflect under strain. The objective of the investigation was finding that applying FRC to strengthen beams enhanced structural performance in terms of ultimate load carrying capacity, fracture pattern deflection, and mode of failure or not.

scholarly journals Failure mode in shear of steel fiber reinforced concrete beams

2018 ◽  
Vol 163 ◽  
pp. 02003 ◽  
Author(s):  
Julita Krassowska ◽  
Marta Kosior-Kazberuk
Keyword(s):  
Reinforced Concrete ◽  
Steel Fiber ◽  
Concrete Beams ◽  
Fiber Reinforced Concrete ◽  
Reinforced Concrete Beams ◽  
Bending Test ◽  
Fibre Reinforced Concrete ◽  
Fiber Reinforced ◽  
Steel Fiber Reinforced Concrete ◽  
Steel Fibres

Experimental tests were carried out to assess the failure model of steel fiber reinforced concrete beams. Experimental research was focused on observing changes in the behavior of the tested elements depending on the amount of shear reinforcement and the fiber. Model two-span beams with a cross-section of 80x180 mm and a length of 2000 mm were tested. The beams had varied stirrup spacing. The following amounts of steel fibres in concrete were used: 78.5 kg/m3 (1.0%) i 118 kg/m3 (1.5%). Concrete beams without fibres were examined at the same time. The beams were loaded in a five-point bending test until they were destroyed. Shear or bending capacity of the element was observed. Fibre reinforced concrete beams were not destroyed rapidly, but they kept their shape consistent under load. Larger number of diagonal cracks with a smaller width were observed in fibre reinforced concrete beams. Failure of concrete beams without fibres was rapid, with a characteristic brittle cracking. Steel fibres revealed the ability to transfer significant shear stress after cracking in comparison to plain concrete.

scholarly journals The change in impermeability of steel fiber reinforced concrete with high strength cement-sand matrix at heating

2020 ◽  
Vol 17 (1) ◽  
pp. 150-155
Author(s):  
V. A. Dorf ◽  
◽  
R. O. Krasnovskij ◽  
D. E. Kapustin ◽  
P. S. Sultygova ◽  
...  
Keyword(s):  
Reinforced Concrete ◽  
Steel Fiber ◽  
Heating Temperature ◽  
High Strength ◽  
Fiber Reinforced Concrete ◽  
Fiber Reinforced ◽  
Steel Fiber Reinforced Concrete ◽  
Fiber Concrete ◽  
The Matrix ◽  
Steel Fiber Concrete

The paper considers the effects of high temperatures in case of fire on the change in impermeability of steel fiber reinforced concrete having a high-strength cement-sand matrix and various content of fiber of different types, sizes, and strength. It is shown that in the temperature range from 20° to 1100° C in the diagram “Heating temperature - impermeability class», the matrix and steel fiber concrete(SFC) have a S-shaped character, and in case of heating temperature of over 100 °C, there comes a distinct decrease in impermeability.

Sign in / Sign up

Export Citation Format

Share Document