scholarly journals Study of Structure and Magnetic Properties of SmCo10 Alloy Prepared by Different Methods

2018 ◽  
Vol 2018 ◽  
pp. 1-10
Author(s):  
Xiang Chi ◽  
Ying Li ◽  
De-quan Er ◽  
Xu-hao Han ◽  
Xiu-li Duan ◽  
...  
Keyword(s):  
Grain Size ◽  
Magnetic Properties ◽  
Grain Boundaries ◽  
Melt Spinning ◽  
Phase Distribution ◽  
Cast Alloy ◽  
Structural Parameters ◽  
Homogeneous Distribution ◽  
Annealed Alloy ◽  
Average Grain Size

In this paper, the phase compositions, microstructures, atomic structures, and magnetic properties of Co-rich SmCo10 alloys prepared by arc-melting, annealing, and melt-spinning were studied. It was found that as-cast alloy is composed of Th2Zn17-type Sm2Co17 matrix with an average grain size of ∼45 μm accompanied by lamellar eutecticum (consisting of α-Co and Th2Zn17-type Sm2Co17) distributed at grain boundaries. The annealed alloy has the same phase composition and phase distribution as the as-cast alloy except that the average grain size decreases to ∼35 μm, and the eutecticum has more homogeneous distribution on the matrix. Simultaneously, the atomic structure of Sm2Co17 is unchanged with only a decrease in structural disorder after annealing. The as-spun ribbons are composed of ∼95.5 vol.% TbCu7-type Sm2Co17 and the rest α-Co. The short rod-shaped α-Co grains are intermittently distributed at the grain boundaries of equiaxed Sm2Co17 grains. The as-spun ribbons show a higher coercivity, and the annealed alloy shows maximum magnetization. The structural parameters were calculated by Extended X-ray Absorption Fine Structure (EXAFS), and the relationship between structure and magnetic properties was discussed in detail.

scholarly journals Structure and Properties of Nd-Fe-B Alloy Subjected to HDDR Process

2016 ◽  
Vol 61 (1) ◽  
pp. 217-220 ◽  
Author(s):  
M. Szymański ◽  
B. Michalski ◽  
M. Leonowicz ◽  
Z. Miazga
Keyword(s):  
Grain Size ◽  
Magnetic Properties ◽  
Phase Transformation ◽  
Grain Boundaries ◽  
Master Alloy ◽  
Structure And Properties ◽  
Rich Phase ◽  
Average Grain Size ◽  
Reversal Phase ◽  
Neodymium Magnets

In this paper the Hydrogenation, Disproportionation, Desorption and Recombination (HDDR) route was tested, for the Nd-Fe-B master alloy, as a prospective procedure for recycling of sintered scrap neodymium magnets. The HDDR method is based on the hydrogen induced reversal phase transformation of Nd-Fe-B alloy: Nd2Fe14B + (2±x) H2 = 2NdH2±x + Fe2B + 12Fe. Microstructural observations (SEM), phase constitution studies (XRD) and measurement of magnetic properties (VSM) were done to investigate the HDDR transformation progress. It was observed that disproportionation reaction starts at the grain boundaries, where the Nd-rich phase is located. Average grain size was reduced and coercive material was produced as a result of the HDDR process. Obtained results are similar to literature data.

A Study on The Phase Transformation and Exchange-Coupling of (Nd0 95La0 05)9 5FebalCo5Nb2B10.5 Nanocomposites

1999 ◽  
Vol 577 ◽  
Author(s):  
Q. Chen ◽  
B. M. Ma ◽  
B. Lu ◽  
M. Q. Huang ◽  
D. E. Laughlin
Keyword(s):  
Grain Size ◽  
Magnetic Properties ◽  
Phase Transformation ◽  
Thermal Treatment ◽  
Grain Growth ◽  
Exchange Coupling ◽  
Phase Distribution ◽  
Maximum Energy ◽  
Treatment Temperature ◽  
Phase Identification

ABSTRACTThe phase transformation and the exchange coupling in (Ndo095Lao005)9.5FebaICOsNb 2BI05 have been investigated. Nanocomposites were obtained by treating amorphous precursors at temperatures ranging from 650TC to 9500C for 10 minutes. The magnetic properties were characterized via the vibrating sample magnetometer (VSM). X-ray diffraction (XRD), thermomagnetic analysis (TMA), and transmission electron microscopy (TEM) were used to perform phase identification, measure grain size, and analyze phase distribution. The strength of the exchange coupling between the magnetically hard and soft phases in the corresponding nanocomposite was analyzed via the AM-versus-H plot. It was found that the remanence (Br), coercivity (Hci), and maximum energy product (BHmax) obtained were affected by the magnetic phases present as well as the grain size of constituent phases and their distribution. The optimal magnetic performance, BHm, occurred between 700°C to 750°C, where the crystallization has completed without excessive grain growth. TMA and TEM indicated that the system was composed of three phases at this point, Nd2(Fe Co) 14B, ca-Fe, and Fe3B. The exchange coupling interaction among these phases was consistently described via the AM-versus-H plot up to 750°C. The Br, Hci, and BHmax degraded severely when the thermal treatment temperature increased from 750°C. This degradation may be attributed to the grain growth of the main phases, from 45 to 68nm, and the development of precipitates, which grew from 5nm at 750°C to 12nm at 850°C. Moreover, the amount of the precipitates was found to increase with the thermal treatment temperatures. The precipitates, presumably borides, may cause a decrease in the amount of the a-Fe and Fe 3B and result in a redistribution of the Co in the nanocomposites. The increase of the Co content in the Nd 2(Fe Co) 14B may explain the increase of its Curie temperature with the thermal treatment temperatures. In this paper, we examine the impacts of these factors on the magnetic properties of (Ndo 95Lao 05)9 5FebaICosNb2B10.5 nanocomposite.

scholarly journals The Influence of Annealing Temperature on the Structure and Magnetic Properties of Nanocrystalline BiFeO3 Prepared by Sol–Gel Method

2021 ◽  
Author(s):  
T. Pikula ◽  
T. Szumiata ◽  
K. Siedliska ◽  
V. I. Mitsiuk ◽  
R. Panek ◽  
...  
Keyword(s):  
Grain Size ◽  
Magnetic Properties ◽  
Annealing Temperature ◽  
Sol Gel ◽  
Weak Ferromagnetism ◽  
X Ray Diffraction ◽  
Gel Method ◽  
Sol Gel Method ◽  
Average Grain Size ◽  
Spin Cycloid

AbstractIn this work, BiFeO3 powders were synthesized by a sol–gel method. The influence of annealing temperature on the structure and magnetic properties of the samples has been discussed. X-ray diffraction studies showed that the purest phase was formed in the temperature range of 400 °C to 550 °C and the samples annealed at a temperature below 550 °C were of nanocrystalline character. Mössbauer spectroscopy and magnetization measurements were used as complementary methods to investigate the magnetic state of the samples. In particular, the appearance of weak ferromagnetic properties, significant growth of magnetization, and spin-glass-like behavior were observed along with the drop of average grain size. Mössbauer spectra were fitted by the model assuming cycloidal modulation of spins arrangement and properties of the spin cycloid were determined and analyzed. Most importantly, it was proved that the spin cycloid does not disappear even in the case of the samples with a particle size well below the cycloid modulation period λ = 62 nm. Furthermore, the cycloid becomes more anharmonic as the grain size decreases. The possible origination of weak ferromagnetism of the nanocrystalline samples has also been discussed.

MICROSTRUCTURE AND MAGNETIC PROPERTIES OF NANOSTRUCTURED Al2O3-20vol%Fe70Co30 COMPOSITE PREPARED BY HIGH ENERGY MECHANICAL MILLING

2009 ◽  
Vol 23 (06n07) ◽  
pp. 1383-1388 ◽  
Author(s):  
MASLEEYATI YUSOP ◽  
DELIANG ZHANG ◽  
MARCUS WILSON ◽  
NICK STRICKLAND
Keyword(s):  
Grain Size ◽  
Magnetic Properties ◽  
Alloy Powder ◽  
Milling Time ◽  
High Energy ◽  
Composite Powders ◽  
Nanostructured Composite ◽  
Alloy Particles ◽  
Average Grain Size ◽  
Microstructure And Magnetic Properties

Al 2 O 3-20 vol % Fe 70 Co 30 composite powders have been prepared by high energy ball milling a mixture of Al 2 O 3 powder and Fe 70 Co 30 alloy powder. The Fe 70 Co 30 alloy powder was also prepared by mechanical alloying of Fe and Co powders using the same process. The effects of milling duration from 8 to 48 hours on microstructure and magnetic properties of the nanostructured composite powders have been studied by means of X-ray Diffractometry (XRD), scanning electron microscopy (SEM) and vibrating sample magnetometry (VSM). It was found that the nanostructured composite powder particles with irregular shapes and Fe 70 Co 30 alloy particles being embedded in them formed after 8 hours of milling. The average grain size of the Al 2 O 3 matrix reduced drastically to less than 18nm after 16 hours of milling. On the other hand, the embedded alloy particles demonstrated almost unchanged average grain size in the range of 14-15nm. Magnetic properties of the powder compacts at room temperature were measured from hysteresis curves, and show strong dependence of the milling time, with the coercivity increasing from 67.1 up to 127.9kOe with increasing the milling time from 8 to 48 hours. The possible microstructural reasons for this dependence are discussed.

Effect of Mo doping on the microstructure and properties of an Fe36Ni Invar alloy

2020 ◽  
Vol 34 (31) ◽  
pp. 2050297
Author(s):  
Liming Dong ◽  
Zhaopeng Yu ◽  
Xianjun Hu ◽  
Fang Feng
Keyword(s):  
Grain Size ◽  
Thermal Expansion ◽  
Grain Boundaries ◽  
Coefficient Of Thermal Expansion ◽  
Solution Temperature ◽  
Microstructure And Properties ◽  
Invar Alloys ◽  
Average Grain Size ◽  
Mo Content ◽  
Hot Rolled

The effects of doping with different Mo contents on the microstructure and properties of Fe36Ni Invar alloys were investigated. The results show that when 0.9 wt.% Mo and 1.8 wt.% Mo were added to Fe36Ni, the tensile strengths of the hot rolled alloys were 46 and 61 MPa higher than that of the 0 wt.% Mo sample, respectively. With an increase in Mo content from 0.9 to 1.8 wt.%, the solution temperature of the highest hardness after heat treatment increased from 800[Formula: see text]C to 850[Formula: see text]C, respectively. The addition of 0.9 wt.% Mo refined the average grain size from 37 to 15 [Formula: see text]m, and an excessive amount of Mo (1.8 wt.%) did not refine the grains further. After Mo was added, the precipitates on the original grain boundaries changed into nanoprecipitates dispersed in the grain boundaries and inside the grains. Mo was present in the alloy in the form of a carbide and in solid solution, which affected the magnetic lattice effect and increased the thermal expansion coefficient of the alloy. However, upon comparing the samples doped with 0 wt.% Mo, 0.9 wt.% Mo and 1.8 wt.% Mo, it was found that the addition of 0.9 wt.% Mo not only refined the grain size and improved the mechanical properties of the alloy but also led to a low coefficient of thermal expansion (CTE) over the range from 20[Formula: see text]C to 300[Formula: see text]C.

scholarly journals Microstructure and Mechanical Properties of 4Al Alumina-Forming Austenitic Steel after Cold-Rolling Deformation and Annealing

Materials ◽  
2020 ◽  
Vol 13 (12) ◽  
pp. 2767 ◽  
Author(s):  
Chenchen Jiang ◽  
Qiuzhi Gao ◽  
Hailian Zhang ◽  
Ziyun Liu ◽  
Huijun Li
Keyword(s):  
Grain Size ◽  
Cold Rolling ◽  
Grain Boundaries ◽  
Austenitic Steel ◽  
Rolling Reduction ◽  
X Ray Diffraction ◽  
Transmission Electron ◽  
Cold Rolling Reduction ◽  
Average Grain Size ◽  
Cold Rolled

Microstructural evolutions of the 4Al alumina-forming austenitic steel after cold rolling with different reductions from 5% to 30% and then annealing were investigated using electron backscattering diffraction (EBSD), X-ray diffraction (XRD) and transmission electron microscopy (TEM). Tensile properties and hardness were also measured. The results show that the average grain size gradually decreases with an increase in the cold-rolling reduction. The low angle grain boundaries (LAGBs) are dominant in the cold-rolled samples, but high angle grain boundaries (HAGBs) form in the annealed samples, indicating that the grains are refined under the action of dislocations. During cold rolling, high-density dislocations are initially introduced in the samples, which contributes to a large number of dislocations remaining after annealing. With the sustaining increase in cold-rolled deformation, the samples exhibit more excellent tensile strength and hardness due to the decrease in grain size and increase in dislocation density, especially for the samples subjected to 30% cold-rolling reduction. The contribution of dislocations on yield strength is more than 60%.

Characterization of Zinalco Alloy Superplastically Deformed Using Orientation Imaging Microscopy

2009 ◽  
Vol 1242 ◽  
Author(s):  
Ramos A. Mitsuo ◽  
Martínez F. Elizabeth ◽  
Negrete S. Jesús ◽  
Torres-Villaseñor G.
Keyword(s):  
Grain Size ◽  
Grain Boundary ◽  
Grain Boundaries ◽  
Superplastic Deformation ◽  
Orientation Imaging Microscopy ◽  
Grain Boundary Sliding ◽  
Boundary Misorientation ◽  
Average Grain Size ◽  
Grain Boundary Misorientation ◽  
Misorientation Angles

ABSTRACTZinalco alloy (Zn-21mass%Al-2mass%Cu) specimens were deformed superplastically with a strain rate (ε) of 1×10-3 s-1 at homologous temperature (TH) of 0.68 (5 ). It was observed neck formation that indicate nonhomegeneus deformation. Grain size and grain boundaries misorientation changes, due superplastic deformation, were characterized by Orientation Imagining Microscopy (OIM) technique. It was studied three regions in deformed specimens and the results were compared with the results for a specimen without deformation. Average grain size of 1 mm was observed in non-deformed specimen and a fraction of 82% for grain boundary misorientation angles with a grain boundaries angles between 15° and 55° was found. For deformed specimen, the fraction of angles between 15° and 55° was decreced to average value of 75% and fractions of low angle (<5°) and high angle (>55°) misorientations were 10% and 15% respectively. The grain size and high fraction of grain boundary misorientation angles between 15° and 55° observed in the alloy without deformation, are favorable for grain rotation and grain boundary sliding (GBS) procces. The changes observed in the fraction of favorable grain boundary angles during superplastic deformation, shown that the superplastic capacity of Zinalco was reduced with the deformation.

Grain Size Dependent Magnetic Properties of Nanocrystalline Sm [BE]Co [BD][BJ]/Cu

2001 ◽  
Vol 703 ◽  
Author(s):  
L. Bessais ◽  
C. Djéga-Mariadassou ◽  
J. Zhang ◽  
V. Lalanne ◽  
A. Percheron-Guégan
Keyword(s):  
Grain Size ◽  
Magnetic Properties ◽  
Rietveld Method ◽  
X Ray Diffraction ◽  
X Ray ◽  
Size Dependent ◽  
Transmission Electron ◽  
Average Grain Size ◽  
Magnetic Metal ◽  
Chemical Distribution

ABSTRACTThe evolution of both micro structural and magnetic properties of the Sm[BE]Co[BD][BJ] Cu powder, is studied as a function of soft co-milling time. The average grain size in the range 20 - 50 nm was determined by transmission electron microscopy coupled with x-ray diffraction using the Rietveld method. The particle shape and chemical distribution were investigated by elemental mapping, using wavelength dispersive x-ray analysis with electron microprobe analysis. The coercivity evolution shows that an optimum value of 6 kOe is obtained after 5 h co-milling. The microstructure analysis indicates that both materials are well mixed in nanometer scale. This technique appears as a potential route to synthesize nanocrystalline Sm[BE]Co[BD][BJ] isolated by non-magnetic metal Cu.