Reinforced concrete is the number one medium of construction. It is important to have good quality concrete and reinforcing bar (rebar). It is equally important to have competent bond between rebar and concrete. About six decades ago ribbed rebars of high strength steel started replacing plain round bars of mild steel, the use of which had made reinforced concrete constructions durable. It was overlooked that ribbed rebars of carbon steel would be highly susceptible to corrosion at accelerated rates. That would not only make reinforced concrete constructions reach states of distress early, that could also destroy or reduce bond between ribbed rebars and concrete. The continued use of ribbed rebars of high strength carbon steel demonstrates a widespread lack of understanding of the phenomenon of bond between rebars and concrete. This lack of understanding of bond has led to the introduction of epoxy coated ribbed rebars, ribbed stainless steel bars and glass fiber reinforced and granite reinforced polymer rebars, all of which permit reinforced concrete carry static loads because of engagement between such rebars and concrete. But the load-carrying capacity of reinforced concrete elements is impaired, and such elements become vulnerable to local or even total failure during vibratory loads. The use of PSWC-BAR, characterized by its plain surface and wave-type configuration, permits the use of medium strength and high strength steel. In the absence of ribs, the rate of corrosion is greatly reduced. The use of PSWC-BARs, at no added effort or cost, in lieu of conventional ribbed bars, leads to enhancement of effective bond or engagement between such rebars and concrete, thereby leading to increased load-carrying capacity, several-fold higher life span, ductility and energy-absorbing capacity, and great reduction in life cycle cost and adverse impact of construction on the environment and the global climate. In keeping with a lack of understanding of bond between rebars and concrete, there is arbitrariness in the selection of the required level of percent elongation and ductility of rebars.
Reduction of the Early Autogenous Shrinkage of High Strength Concrete