Rietveld refinement of transition metal doped ZnO

2008 ◽  
Vol 23 (S1) ◽  
pp. S36-S41 ◽  
Author(s):  
D. A. A. Santos ◽  
A. D. P. Rocha ◽  
M. A. Macêdo
Keyword(s):  
Transition Metal ◽  
Rietveld Refinement ◽  
Sol Gel ◽  
Hexagonal Wurtzite Structure ◽  
X Ray Diffraction ◽  
Ionic Radii ◽  
X Ray ◽  
Sol Gel Process ◽  
Doped Zno ◽  
Metal Doped

Nanocrystals of Zn1−xMxO (M=Mn, Co, or Ni) were grown using proteic sol-gel process, and the crystalline phases were identified by X-ray diffraction and Rietveld refinement. The nanocrystals have hexagonal wurtzite structure, with space group P63mc. The insertion of Mn2+ in the place of Zn2+ provoked an increase in the size of the nanocrystals, and the insertion of Co2+ or Ni2+ caused a reduction in the sizes of the nanocrystals, as compared to pure ZnO. This occurred because these three transition metals have very different ionic radii (Co2+=0.58 A˚, Mn2+=0.66 A˚, Ni2+=0.55 A˚, and Zn2+=0.60 A˚).

Investigation on Nano-Sized ZnO Powder Doped with Al3+ Prepared by Sol-Gel Method

2012 ◽  
Vol 621 ◽  
pp. 3-7
Author(s):  
Yu Xiong ◽  
Ji Zheng ◽  
Song Lin Li ◽  
Xue Jia Liu ◽  
Lu Liang
Keyword(s):  
Electron Microscope ◽  
Sol Gel ◽  
X Ray Diffraction ◽  
X Ray ◽  
Nano Powder ◽  
Transmission Electron ◽  
Sol Gel Process ◽  
Doped Zno ◽  
Zno Powder ◽  
Tin Tetrachloride

Al3+-doped ZnO nano-powder was prepared by sol-gel process, using tin tetrachloride and titanium tetrachloride as starting materials. The crystallinity and purity of the powder were analyzed by X-ray diffraction spectrometer (XRD). And the size and distribution of Al3+-doped ZnO grains were studied using transmission electron microscope (TEM) and scanning electron microscope (SEM). The results showed that the Al3+ was successfully doped into the crystal lattice of tin oxide and that the electric conductivity of Al3+-doped ZnO sample was improved significantly.

Photocatalytic Properties of the Transition Metal Doped TiO2 Powder Prepared by Sol-Gel Process

2007 ◽  
Vol 280-283 ◽  
pp. 647-650 ◽  
Author(s):  
Chin Myung Whang ◽  
J.G. Kim ◽  
Hae Jin Hwang
Keyword(s):  
Photocatalytic Activity ◽  
Transition Metal ◽  
Surface Area ◽  
Sol Gel ◽  
Doped Tio2 ◽  
X Ray ◽  
Undoped Tio2 ◽  
Sol Gel Process ◽  
Uv Visible ◽  
Metal Doped

Transition metal-doped TiO2 powders as a photocatalyst were prepared by sol-gel process and Sb, Bi and Nb were introduced into them as dopants. The photocatalytic behaviors of the doped TiO2 powder were studied as a function of dopant, doping concentration and preparation conditions. X-ray diffraction, FT-Raman, B.E.T. and scanning electron microscopy were applied for structural and microstructural studies. Optical properties of the doped TiO2 powders were studied by UV-Visible Spectrometer and photocatalytic activity of the doped TiO2 was characterized in terms of the degradation of 1,4-dichlorobenzene. X-ray difraction analysis showed that doping with a transition metal ion suppresses anatase-to-rutile phase transition compared with the pure TiO2. The Sb and Nb-doped TiO2 powders did not exhibit any other diffraction peaks except those belonging to TiO2. On the other hand, a diffraction peak of Bi4Ti3O12 appears for 5 at.% Bi-doped samples. All of the doped TiO2 powders had higher specific surface area than undoped TiO2. Surface area increased with increasing dopant concentration depending on the dopant, from 33.9 m2/g to 55.4m2/g. The UV-visible absorption spectra of doped samples were red-shifted by 20~50nm according to the doping level. Also transition metal doped TiO2 powders exhibited better photocatalytic activity than the undoped TiO2. The increase in photoactivity is probably due to the increase in the interfacial electron transfer, red shifts, and better crystallinity.

Luminescent Properties of Zn2SiO4:Eu3+,Dy3+ Phosphors via Sol-Gel Process

2012 ◽  
Vol 217-219 ◽  
pp. 733-736
Author(s):  
Xiu Mei Han ◽  
Shu Ai Hao ◽  
Ying Ling Wang ◽  
Gui Fang Sun ◽  
Xi Wei Qi
Keyword(s):  
Thermal Analysis ◽  
Ir Spectra ◽  
Sol Gel ◽  
Luminescent Properties ◽  
Photoluminescence Spectra ◽  
X Ray Diffraction ◽  
X Ray ◽  
Sol Gel Process ◽  
Ft Ir

Zn2SiO4:Eu3+, Dy3+ phosphors have been prepared through the sol-gel process. X-ray diffraction (XRD), thermogravimetric and ddifferential thermal analysis (TG-DTA), FT-IR spectra and photoluminescence spectra were used to characterize the resulting phosphors. The results of XRD indicated that the phosphors crystallized completely at 1000oC. In Zn2SiO4:Eu3+,Dy3+ phosphors, the Eu3+ and Dy3+ show their characteristic red(613nm, 5D0-7F2), blue (481nm, 4F9/2–6H15/2) and yellow (577nm, 4F9/2–6H13/2) emissions.

The Preparation and Photocatalytic Activity of SWNTs Doped ZnO/TiO2 Compound Films

2010 ◽  
Vol 97-101 ◽  
pp. 1611-1615 ◽  
Author(s):  
Qing Wang ◽  
Xin Li Li ◽  
Wei Nie ◽  
Yong Mei Xia ◽  
Jian Feng Dai
Keyword(s):  
Photocatalytic Activity ◽  
Absorption Spectra ◽  
Sol Gel ◽  
Composite Films ◽  
Wavelength Region ◽  
Tio2 Films ◽  
X Ray Diffraction ◽  
Sol Gel Process ◽  
Doped Zno ◽  
Walled Carbon Nanotubes

The ZnO/TiO2 composite films were deposited over glass using spin coating technique by sol-gel process. Single-walled carbon nanotubes (SWNTs) were used to modify the ZnO/TiO2 films successfully in this paper. The structure and composition of the ZnO/TiO2 composite and SWNTs doped ZnO/TiO2 composite were characterized by X-ray diffraction (XRD). The morphology of samples was characterized by scanning electron microscopy (SEM). The photocatalytic activity was investigated by photocatalytic degradation of aqueous methyl orange under ultraviolet (UV) radiation. The UV-vis absorption spectra of the ZnO/TiO2 films and SWNTs doped ZnO/TiO2 films in the wavelength region 200~800 nm were obtained. The results indicate that the SWNTs addition can decrease the grain size of ZnO/TiO2, which can enhance the photocatalytic activity. UV-vis absorption spectra of SWNTs-ZnO/TiO2 showed obvious blue shifts compared with ZnO/TiO2. The optimal amount of doping SWNTs is 1% according to this research. The enhanced mechanism of the SWNTs for the photocatalytic activity in ZnO/TiO2 films was analyzed in this article.

Magnetic Properties of Bulk Zn0.95-XMnXFe0.05O2 Prepared by Sol-Gel Method and Subsequent Hot Pressing

2011 ◽  
Vol 268-270 ◽  
pp. 356-359 ◽  
Author(s):  
Wen Song Lin ◽  
C. H. Wen ◽  
Liang He
Keyword(s):  
Magnetic Properties ◽  
Photoelectron Spectroscopy ◽  
Raw Materials ◽  
Sol Gel ◽  
Secondary Phase ◽  
X Ray Diffraction ◽  
Gel Method ◽  
X Ray ◽  
Sol Gel Method ◽  
Doped Zno

Mn, Fe doped ZnO powders (Zn0.95-xMnxFe0.05O2, x≤0.05) were synthesized by an ameliorated sol-gel method, using Zn(CH3COO)2, Mn(CH3COO)2and FeCl2as the raw materials, with the addition of vitamin C as a kind of chemical reducer. The resulting powder was subsequently compacted under pressure of 10 MPa at the temperature of 873K in vacuum. The crystal structure and magnetic properties of Zn0.95-xMnxFe0.05O2powder and bulk samples have been investigated by X-ray diffraction (XRD) and vibrating sample magnetometer (VSM). X-ray photoelectron spectroscopy (XPS) was used to study chemical valence of manganese, iron and zinc in the samples. The x-ray diffraction (XRD) results showed that Zn0.95-xMnxFe0.05O (x≤0.05) samples were single phase with the ZnO-like wurtzite structure. No secondary phase was found in the XRD spectrum. X-ray photoelectron spectroscopy (XPS) showed that Fe and Mn existed in Zn0.95-xMnxFe0.05O2samples in Fe2+and Mn2+states. The results of VSM experiment proved the room temperature ferromagnetic properties (RTFP) of Mn, Fe co-doped ZnO samples.

Sol-Gel derived Bi4-xNdxTi3O12 Thin Films and Their Characterization

2002 ◽  
Vol 737 ◽  
Author(s):  
R.E. Melgarejo ◽  
M.S. Tomar ◽  
A. Hidalgo ◽  
R.S. Katiyar
Keyword(s):  
Thin Films ◽  
Spin Coating ◽  
Bismuth Titanate ◽  
Sol Gel ◽  
X Ray Diffraction ◽  
X Ray ◽  
Complete Solid Solution ◽  
Sol Gel Process ◽  
Ferroelectric Memory ◽  
Initial Results

ABSTRACTNd substituted bismuth titanate Bi4-xNdxTi3O12 were synthesized by sol-gel process and thin films were deposited on Pt substrate (Pt/TiO2/SiO2/Si) by spin coating. Thin films, characterized by X-ray diffraction and Raman spectroscopy, shows complete solid solution up to the composition x < 1. Initial results indicate that the ferroelectric polarization increases with increasing Nd content in the film with 2Pr = 50μC/cm2 for x = 0.46, which may have application in non-volatile ferroelectric memory devices.

Characterization of bulk crystals of transition metal doped ZnO for spintronic applications

2003 ◽  
Vol 799 ◽  
Author(s):  
M. H. Kane ◽  
R. Varatharajan ◽  
Z. C. Feng ◽  
S. Kandoor ◽  
J. Nause ◽  
...  
Keyword(s):  
Transition Metal ◽  
Lattice Parameter ◽  
X Ray Diffraction ◽  
Absorption Bands ◽  
Growth Technique ◽  
Undoped Material ◽  
Doped Zno ◽  
Metal Doped ◽  
The Individual

ABSTRACTIn this work, we report on the material properties of ZnO doped with Mn, Co, and Fe grown by a modified melt growth technique. X-ray diffraction measurements show that transition metals can be incorporated on Zn sites; an increase in the lattice parameter is apparent with increasing doping level. UV-visible transmission and reflectance measurements have also been performed. Absorption bands in the visible regime are distinctive to the individual transition metal dopants. A noticeable shift in the optical band edge has been observed from these Mn/Co/Fe-doped ZnO crystals in comparison with the undoped material. ZnO may also provide a suitable platform for the incorporation of transition metal elements through high temperature near equilibrium growth processes; however, further work is required in order to employ these materials for spintronic applications.

Synthesis and Characterizations of Strontium Substituted Hydroxyapatite Thin Films

2010 ◽  
Vol 93-94 ◽  
pp. 231-234
Author(s):  
B. Hongthong ◽  
Satreerat K. Hodak ◽  
Sukkaneste Tungasmita
Keyword(s):  
Thin Film ◽  
Thin Films ◽  
Chemical Composition ◽  
Spin Coating ◽  
Phase Structure ◽  
Sol Gel ◽  
Cross Linking ◽  
X Ray Diffraction ◽  
X Ray ◽  
Sol Gel Process

Strontium substituted hydroxyapatite(SrHAp) were fabricated both in the form of powder as reference and thin film by using inorganic precursor reaction. The sol-gel process has been used for the deposition of SrHAp layer on stainless steal 316L substrate by spin coating technique, after that the films were annealed in air at various temperatures. The chemical composition of SrHAp is represented (SrxCa1-x)5(PO4)3OH, where x is equal to 0, 0.5 and 1.0. Investigations of the phase structure of SrHAp were carried out by using X-ray diffraction technique (XRD). The results showed that strontium is incorporated into hydroxyapatite where its substitution for calcium increases in the lattice parameters, and Sr3(PO4)2 can be detected at 900°C. The SEM micrographs showed that SrHAp films exhibited porous structure before develop to a cross-linking structure.

Low-Temperature Synthesis of Nano-Crystalline ZnTiO3 Powders by Aqueous Sol-Gel Process

2014 ◽  
Vol 543-547 ◽  
pp. 3741-3744
Author(s):  
Quan Jing Mei ◽  
Cong Ying Li ◽  
Jing Dong Guo ◽  
Gui Wang ◽  
Hai Tao Wu
Keyword(s):  
Sol Gel ◽  
Zinc Nitrate ◽  
X Ray Diffraction ◽  
Low Temperature Synthesis ◽  
Temperature Synthesis ◽  
Calcination Process ◽  
X Ray ◽  
Nano Crystalline ◽  
Transmission Electron ◽  
Sol Gel Process

The ecandrewsite-type ZnTiO3was successfully synthesized by the aqueous sol-gel method using TiO2dioxide and zinc nitrate as starting materials instead of expensive organic solvent and metal alkoxides. The as-prepared nanopowders were characterized by X-ray diffraction (XRD), differential thermal analysis (DTA) and transmission electron microscopy (TEM), respectively. The results showed that the calcination process of gel consisted of a series of oxidation and combustion reactions, accompanied by significantly exothermal effects. Highly reactive nanosized ZnTiO3powders were successfully obtained at 850 °C with particle size ~50 nm. By comparison, the aqueous sol-gel process was the most effective and least expensive technique used for the preparation of ZnTiO3nanopowders.

Preparation of YBCO Superconducting Films by Sol-Gel Process

2007 ◽  
Vol 546-549 ◽  
pp. 2007-2010
Author(s):  
Gao Yang Zhao ◽  
Huang Li Zhang ◽  
Ren Zhong Xue ◽  
Yuan Qing Chen ◽  
Li Lei
Keyword(s):  
Sol Gel ◽  
Precursor Solution ◽  
Superconducting Films ◽  
Superconducting Transition ◽  
X Ray Diffraction ◽  
Organic Salts ◽  
Ybco Films ◽  
X Ray ◽  
Sol Gel Process ◽  
Ybco Superconducting Films

precursor solution was prepared using barium trifluoroacetae (Ba-TFA) and non-fluorine yttrium (Y) and copper (Cu) organic salts. The precursor solution was modified by benzalacetone (BzAcH), in which the Cu2+ were chelated with BzAcH, which preventing the loss of Cu in the pyrolysis process. Dense YBCO superconducting films with smooth surface, which confirmed by scanning electron microscopy (SEM), were repeatedly obtained through sol-gel process. X-ray diffraction (XRD) 2θ scanning and φ scanning indicated that the as-prepared YBCO films had good c-axis texture. YBCO films with superconducting transition temperature (TC) above 89K were obtained.

Sign in / Sign up

Export Citation Format

Share Document