Chloride-Induced Stress Corrosion Cracking of Austenitic Stainless Steel Used for Dry Storage of Spent Nuclear Fuel

2013 ◽  
Vol 50 (31) ◽  
pp. 211-226
Author(s):  
T. M. Ahn ◽  
G. Oberson ◽  
S. DePaula
Keyword(s):  
Stainless Steel ◽  
Austenitic Stainless Steel ◽  
Stress Corrosion ◽  
Nuclear Fuel ◽  
Stress Corrosion Cracking ◽  
Spent Nuclear Fuel ◽  
Corrosion Cracking ◽  
Dry Storage ◽  
Induced Stress

scholarly journals Preventing Stress Corrosion Cracking of Spent Nuclear Fuel Dry Storage Canisters

2019 ◽  
Vol 19 ◽  
pp. 346-361 ◽  
Author(s):  
Lloyd Hackel ◽  
Jon Rankin ◽  
Matt Walter ◽  
C Brent Dane ◽  
William Neuman ◽  
...  
Keyword(s):  
Stress Corrosion ◽  
Nuclear Fuel ◽  
Stress Corrosion Cracking ◽  
Spent Nuclear Fuel ◽  
Corrosion Cracking ◽  
Dry Storage

scholarly journals Detecting and imaging stress corrosion cracking in stainless steel, with application to inspecting storage canisters for spent nuclear fuel

2020 ◽  
Vol 109 ◽  
pp. 102180 ◽  
Author(s):  
Marcel C. Remillieux ◽  
Djamel Kaoumi ◽  
Yoshikazu Ohara ◽  
Marcie A. Stuber Geesey ◽  
Li Xi ◽  
...  
Keyword(s):  
Stainless Steel ◽  
Stress Corrosion ◽  
Nuclear Fuel ◽  
Stress Corrosion Cracking ◽  
Spent Nuclear Fuel ◽  
Corrosion Cracking

Spent Fuel Canister Probabilistic Confinement Integrity Assessment

2017 ◽  
Author(s):  
John E. Broussard ◽  
Shannon Chu ◽  
Kevin Fuhr
Keyword(s):  
Stainless Steel ◽  
Austenitic Stainless Steel ◽  
Stress Corrosion ◽  
Stress Corrosion Cracking ◽  
Probabilistic Model ◽  
Population Based ◽  
Corrosion Cracking ◽  
Spent Fuel ◽  
Integrity Assessment ◽  
Induced Stress

A probabilistic model was developed that considers the likelihood of through-wall penetration of chloride-induced stress corrosion cracking (CISCC) in austenitic stainless steel canisters and compares different population-based sample inspection regimes. This paper describes the inputs and methods used to simulate multiple canisters with a range of susceptibilities. This paper also summarizes results of key illustrative cases.

Crack Growth Rate Testing and Large Plate Demonstration Under Chloride-Induced Stress Corrosion Cracking Conditions in Stainless Steel Canisters for Storage of Spent Nuclear Fuel

2019 ◽  
Author(s):  
Poh-Sang Lam ◽  
Andrew J. Duncan ◽  
Lisa N. Ward ◽  
Robert L. Sindelar ◽  
Yun-Jae Kim ◽  
...  
Keyword(s):  
Growth Rate ◽  
Stainless Steel ◽  
Crack Growth Rate ◽  
Stress Corrosion ◽  
Crack Growth ◽  
Nuclear Fuel ◽  
Stress Corrosion Cracking ◽  
Spent Nuclear Fuel ◽  
Compact Tension ◽  
Corrosion Cracking

Abstract Stress corrosion cracking may occur when chloride-bearing salts deposit and deliquesce on the external surface of stainless steel spent nuclear fuel storage canisters at weld regions with high residual stresses. Although it has not yet been observed, this phenomenon leads to a confinement concern for these canisters due to its potential for radioactive materials breaching through the containment system boundary provided by the canister wall during extended storage. The tests for crack growth rate have been conducted on bolt-load compact tension specimens in a setup designed to allow initially dried salt deposits to deliquesce and infuse to the crack front under conditions relevant to the canister storage environments (e.g., temperature and humidity). The test and characterization protocols are performed to provide bounding conditions in which cracking will occur. The results after 2- and 6-month exposure are examined in relation to previous studies in condensed brine and compared with other experimental data in the open literature. The knowledge gained from bolt-load compact tension testing is being applied to a large plate cut from a mockup commercial spent nuclear fuel canister to demonstrate the crack growth behavior induced from starter cracks machined in regions where the welding residual stress is expected. All these tests are conducted to support the technical basis for ASME Boiler and Pressure Vessel Section XI Code Case N-860.