Failure analysis of high power GaAs-based lasers using electron beam induced current analysis and transmission electron microscopy

1998 ◽  
Vol 16 (2) ◽  
pp. 825-829 ◽  
Author(s):  
R. E. Mallard ◽  
R. Clayton ◽  
D. Mayer ◽  
L. Hobbs
Keyword(s):  
Electron Microscopy ◽  
Transmission Electron Microscopy ◽  
Electron Beam ◽  
Failure Analysis ◽  
High Power ◽  
Induced Current ◽  
Current Analysis ◽  
Transmission Electron ◽  
Electron Beam Induced Current

Techniques for Transmission Electron Microscopy of Fiber-Matrix Interfaces in Aluminum Alloy-Boron Composites by Ion Erosio

1971 ◽  
Vol 29 ◽  
pp. 204-205
Author(s):  
G. G. Shaw
Keyword(s):  
Electron Microscopy ◽  
Transmission Electron Microscopy ◽  
Aluminum Alloy ◽  
Electron Beam ◽  
Pure Aluminum ◽  
Ion Milling ◽  
Transmission Electron ◽  
Fiber Matrix ◽  
Ion Erosion ◽  
Row Of Fibers

The morphology and composition of the fiber-matrix interface can best be studied by transmission electron microscopy and electron diffraction. For some composites satisfactory samples can be prepared by electropolishing. For others such as aluminum alloy-boron composites ion erosion is necessary.When one wishes to examine a specimen with the electron beam perpendicular to the fiber, preparation is as follows: A 1/8 in. disk is cut from the sample with a cylindrical tool by spark machining. Thin slices, 5 mils thick, containing one row of fibers, are then, spark-machined from the disk. After spark machining, the slice is carefully polished with diamond paste until the row of fibers is exposed on each side, as shown in Figure 1.In the case where examination is desired with the electron beam parallel to the fiber, preparation is as follows: Experimental composites are usually 50 mils or less in thickness so an auxiliary holder is necessary during ion milling and for easy transfer to the electron microscope. This holder is pure aluminum sheet, 3 mils thick.

Effects of High-Energy Ions on Synthetic Quartz

1972 ◽  
Vol 30 ◽  
pp. 544-545
Author(s):  
Joseph J. Comer ◽  
Charles Bergeron ◽  
Lester F. Lowe
Keyword(s):  
Electron Microscopy ◽  
Transmission Electron Microscopy ◽  
Electron Beam ◽  
High Energy ◽  
Transmission Electron ◽  
Kikuchi Lines ◽  
High Energy Ions ◽  
Diffraction Patterns ◽  
Dauphiné Twinning ◽  
Beam Damage

Using a Van De Graaff Accelerator thinned specimens were subjected to bombardment by 3 MeV N+ ions to fluences ranging from 4x1013 to 2x1016 ions/cm2. They were then examined by transmission electron microscopy and reflection electron diffraction using a 100 KV electron beam.At the lowest fluence of 4x1013 ions/cm2 diffraction patterns of the specimens contained Kikuchi lines which appeared somewhat broader and more diffuse than those obtained on unirradiated material. No damage could be detected by transmission electron microscopy in unannealed specimens. However, Dauphiné twinning was particularly pronounced after heating to 665°C for one hour and cooling to room temperature. The twins, seen in Fig. 1, were often less than .25 μm in size, smaller than those formed in unirradiated material and present in greater number. The results are in agreement with earlier observations on the effect of electron beam damage on Dauphiné twinning.