Elevated Temperature Properties of Maraging Steel Plates and Welds

1971 ◽  
Vol 93 (2) ◽  
pp. 218-224
Author(s):  
N. Kenyon ◽  
E. P. Sadowski ◽  
P. P. Hydrean
Keyword(s):  
Elevated Temperature ◽  
Maraging Steel ◽  
Elevated Temperatures ◽  
High Strength Steels ◽  
High Strength ◽  
Steel Plates ◽  
Maraging Steels ◽  
Gas Tungsten Arc ◽  
Temperature Exposure ◽  
Rupture Behavior

The creep rupture behavior, and the effects of elevated temperature exposure in air and hydrogen on the subsequent room temperature properties of a 12 percent Ni-5 percent Cr-3 percent Mo maraging steel are described. Tests have been made on several heats of plate and on gas tungsten-arc, gas metal-arc, and electroslag welds. On the basis of the results obtained, maraging steels offer promise as high-strength steels for service at elevated temperatures.

scholarly journals RESIDUAL STRENGTH OF STRUCTURAL STEELS: SN400, SM520 AND SM570

2016 ◽  
Author(s):  
In-Rak Choi ◽  
Kyung-Soo Chung
Keyword(s):  
Mechanical Properties ◽  
Elevated Temperatures ◽  
High Strength Steels ◽  
High Strength ◽  
Building Construction ◽  
Steel Plates ◽  
Seismic Resistance ◽  
Building Structures ◽  
Reliable Performance ◽  
Strength And Stiffness

<p>This paper presents post-fire mechanical properties of mild to high-strength steels commonly used in building structures in Korea. Steel is one of the main materials for building construction due to fast construction, light weight, and high seismic resistance. However, steel usually loses its strength and stiffness at elevated temperatures, especially over 600°C. But steel can regain some of its original mechanical properties after cooling down from the fire. Therefore, it is important to accurately evaluate the reliable performance of steel to reuse or repair the structures. For this reason, an experimental study was performed to examine the post-fire mechanical properties of steel plates SN400, SM520 and SM570 after cooling down from elevated temperatures up to 900°C. The post-fire stress-strain curves, elastic modulus, yield and ultimate strengths and residual factors were obtained and discussed.</p>

Microstructure of resistance spot welding of maraging steels

1990 ◽  
Vol 48 (4) ◽  
pp. 900-901
Author(s):  
I. Neuman ◽  
S.F. Dirnfeld ◽  
I. Minkoff
Keyword(s):  
Maraging Steel ◽  
Spot Welding ◽  
Lath Martensite ◽  
Base Material ◽  
Aging Treatment ◽  
High Strength ◽  
Maraging Steels ◽  
Heat Treated ◽  
Current Cycle ◽  
Welding Processes

Experimental work on the spot welding of Maraging Steels revealed a surprisingly low level of strength - both in the as welded and in aged conditions. This appeared unusual since in the welding of these materials by other welding processes (TIG,MIG) the strength level is almost that of the base material. The maraging steel C250 investigated had the composition: 18wt%Ni, 8wt%Co, 5wt%Mo and additions of Al and Ti. It has a nominal tensile strength of 250 KSI. The heat treated structure of maraging steel is lath martensite the final high strength is reached by aging treatment at 485°C for 3-4 hours. During the aging process precipitation takes place of Ni3Mo and Ni3Ti and an ordered solid solution containing Co is formed.Three types of spot welding cycles were investigated: multi-pulse current cycle, bi-pulse cycle and single pulsle cycle. TIG welded samples were also tested for comparison.The microstructure investigations were carried out by SEM and EDS as well as by fractography. For multicycle spot welded maraging C250 (without aging), the dendrites start from the fusion line towards the nugget centre with an epitaxial growth region of various widths, as seen in Figure 1.

Investigation of EN AW 5754 Aluminum Alloy’s Formability at Elevated Temperatures

2017 ◽  
Vol 885 ◽  
pp. 98-103 ◽  
Author(s):  
Dávid Budai ◽  
Miklós Tisza ◽  
Péter Zoltán Kovács
Keyword(s):  
Elevated Temperatures ◽  
High Strength Steels ◽  
High Strength ◽  
Carbon Composite ◽  
Alloy Sheet ◽  
High Mass ◽  
Mass Reduction ◽  
Forming Process ◽  
Forming Temperature ◽  
Operating Distance

Nowadays, mass reduction is the most often used term in the automotive industry. Car manufacturers are continuously working on getting ever lighter models than the previous ones, because of the global competition and the rigorous emission rules. A light car has many advantages: lower consumption, better handling, longer operating distance, etc. The emission rules forced the car brands to start new researches to find new solutions for mass reduction. The formula is relatively simple, using lighter or less materials or both and the car will be lighter. In the recent solutions there are three different ways: application of high strength steels, aluminum alloys, and carbon-composite elements. Our investigations are focusing mainly on aluminum, because of its high mass reduction potential. The biggest problem with the aluminum is its low formability. The formability of aluminum is lower than the steel, and it causes problems for the manufacturers. To increase the formability of the aluminum is a hot topic in the research and development area. Forming at elevated temperatures is one of the best solutions to increase the formability of aluminum. The relation between the formability and the forming temperature is not linear, furthermore beyond the optimum forming temperature the formability decreases. We need dozens of investigations to describe the perfect relation, but sometimes a good approximation is enough to form sheet products safely. In our work we investigated the EN AW 5754 aluminum alloy sheet at room temperature, 130°C, 200°C and 260°C. From these tests we could obtain FLC curves of the alloy at different temperatures. Using these curves, the process engineers could find the optimum parameters of their forming process.

scholarly journals Influence of Elevated Temperatures on the High-Strength X3NiCoMoTi 18-9-5 Maraging Steel Behavior

2020 ◽  
Vol 20 (5) ◽  
pp. 684-689
Author(s):  
Angelina Strakosova ◽  
Alena Michalcová ◽  
Zdeněk Kačenka ◽  
Filip Průša ◽  
Dalibor Vojtěch
Keyword(s):  
Maraging Steel ◽  
Elevated Temperatures ◽  
High Strength

scholarly journals Post-fire mechanical properties of high strength steels

2018 ◽  
Author(s):  
Ben Young ◽  
Hai-Ting Li
Keyword(s):  
Mechanical Properties ◽  
Experimental Investigation ◽  
Ambient Temperature ◽  
High Strength Steel ◽  
Elevated Temperatures ◽  
Weight Ratio ◽  
High Strength Steels ◽  
High Strength ◽  
Predictive Equations ◽  
Retention Factors

High strength steels are becoming increasingly attractive for structural and architectural applications due to their superior strength-to-weight ratio which could lead to lighter and elegant structures. The stiffness and strength of high strength steels may reduce after exposure to fire. The post-fire mechanical properties of high strength steels have a crucial role in evaluating the residual strengths of these materials. This paper presents an experimental investigation on post-fire mechanical properties of cold-formed high strength steels. A series of tensile coupon tests has been carried out. The coupon specimens were extracted from cold-formed square hollow sections with nominal yield stresses of 700 and 900 MPa at ambient temperature. The specimens were exposed to various elevated temperatures ranged from 200 to 1000 °C and then cooled down to ambient temperature before tested to failure. Stress-strain curves were obtained and the mechanical properties, namely, Young’s modulus, yield stress (0.2% proof stress) and ultimate strength, of the cold-formed high strength steel materials after exposure to elevated temperatures were derived. The post-fire retention factors that obtained from the experimental investigation were compared with existing predictive equations in the literature. New predictive equations are proposed to determine the residual mechanical properties of high strength steels after exposure to fire. It is shown that the proposed predictive equations are suitable for both cold-formed and hot-rolled high strength steel materials with nominal yield stresses ranged from 690 to 960 MPa.

scholarly journals Study on Tensile Properties of CFRP Plates under Elevated Temperature Exposure

Materials ◽  
2019 ◽  
Vol 12 (12) ◽  
pp. 1995 ◽  
Author(s):  
Yongxin Yang ◽  
Yanju Jiang ◽  
Hongjun Liang ◽  
Xiaosan Yin ◽  
Yue Huang
Keyword(s):  
Tensile Strength ◽  
Elastic Modulus ◽  
Elevated Temperature ◽  
Tensile Properties ◽  
Failure Mode ◽  
Elevated Temperatures ◽  
Strain Curve ◽  
Effect Of Temperature ◽  
Temperature Exposure ◽  
The Impact

Elevated temperature exposure has a negative effect on the performance of the matrix resin in Carbon Fiber Reinforced Plastics (CFRP) plates, whereas limited quantitative research focuses on the deteriorations. Therefore, 30 CFRP specimens were designed and tested under elevated temperatures (10, 30, 50, 70, and 90 °C) to explore the degradations in tensile properties. The effect of temperature on the failure mode, stress-strain curve, tensile strength, elastic modulus and elongation of CFRP plates were investigated. The results showed that elevated temperature exposure significantly changed the failure characteristics. When the exposed temperature increased from 10 °C to 90 °C, the failure mode changed from the global factures in the whole CFRP plate to the successive fractures in carbon fibers. Moreover, with temperatures increasing, tensile strength and elongation of CFRP plates decreases gradually while the elastic modulus shows negligible change. Finally, the results of One-Way Analysis of Variance (ANOVA) show that the degradation of the tensile strength of CFRP plates was due to the impact of elevated temperature exposure, rather than the test error.

Sign in / Sign up

Export Citation Format

Share Document