A Serviceability Approach for Carbon Steel Piping to Intermittent High Temperatures

1996 ◽  
Vol 118 (4) ◽  
pp. 496-501 ◽  
Author(s):  
M. D. Ratiu ◽  
N. T. Moisidis
Keyword(s):  
Carbon Steel ◽  
Gas Flow ◽  
Elevated Temperatures ◽  
Industrial Applications ◽  
Diesel Generator ◽  
Operating Life ◽  
Permissible Stress ◽  
Design Qualification ◽  
Creep Fatigue ◽  
Steel Piping

Carbon steel piping (e.g., ASME SA-106, SA-53), is installed in many industrial applications (i.e., diesel generator exhaust manifold) where the internal gas flow subjects the piping to successive short time exposures at elevated temperatures up to 1100°F. A typical design of this piping without consideration for creep-fatigue cumulative damage is at least incomplete if not inappropriate. Also, a design for creep-fatigue, usually employed for long-term exposure to elevated temperatures, would be too conservative and will impose replacement of the carbon steel piping with heat-resistant CrMo steel piping. The existing ASME Standard procedures do not explicitly provide acceptance criteria for the design qualification to withstand these intermittent exposures to elevated temperatures. The serviceability qualification proposed is based on the evaluation of equivalent full temperature cycles which are presumed/expected to be experienced by the exhaust piping during the design operating life of the diesel engine. The proposed serviceability analysis consists of: (a) determination of the permissible stress at elevated temperatures, and (b) estimation of creep-fatigue damage for the total expected cycles of elevated temperature exposures following the procedure provided in ASME Code Cases N-253-6 and N-47-28.

Qualification of Diesel Generator Exhaust Carbon Steel Piping to Intermittent Elevated Temperatures

1996 ◽  
Vol 118 (1) ◽  
pp. 42-47
Author(s):  
M. D. Ratiu ◽  
N. T. Mosidis
Keyword(s):  
Carbon Steel ◽  
Elevated Temperatures ◽  
Diesel Generator ◽  
Operating Life ◽  
Permissible Stress ◽  
Design Qualification ◽  
Creep Fatigue ◽  
Asme Code ◽  
Full Temperature ◽  
Steel Piping

The diesel generator exhaust piping, usually made up of carbon steel piping (e.g., ASME SA-106, SA-53), is subjected to successive short time exposures at elevated temperatures up to 1000° F (538°C). A typical design of this piping, without consideration for creep-fatigue cumulative damage, is at least incomplete, if not inappropriate. Also, a design for creep-fatigue, usually employed for long-term exposure to elevated temperatures, would be too conservative and will impose replacement of the carbon steel piping with heat-resistant CrMo alloy piping. The existing ASME standard procedures do not explicitly provide acceptance criteria for the design qualification to withstand these intermittent exposures to elevated temperatures. The serviceability qualification proposed is based on the evaluation of equivalent full temperature cycles which are presumed/expected to be experienced by the exhaust piping during the design operating life of the diesel engine. The proposed serviceability analysis consists of: (a) determination of the permissible stress at elevated temperatures, and (b) estimation of creep-fatigue damage for the total expected cycles of elevated temperature exposures following the procedure provided in ASME Code Cases N-253-6 and N-47-28.

Low cycle fatigue and ductile fracture for Japanese carbon steel piping under dynamic loadings

1994 ◽  
Vol 153 (1) ◽  
pp. 57-69 ◽  
Author(s):  
Naoki Miura ◽  
Terutaka Fujioka ◽  
Koichi Kashima ◽  
Satoshi Kanno ◽  
Makoto Hayashi ◽  
...  
Keyword(s):  
Carbon Steel ◽  
Ductile Fracture ◽  
Low Cycle Fatigue ◽  
Cycle Fatigue ◽  
Dynamic Loadings ◽  
Steel Piping

Improvement of Integrity Concepts for NPP Primary Circuit Piping

2008 ◽  
Author(s):  
Alexey Arzhaev ◽  
Sergey Butorin
Keyword(s):  
Carbon Steel ◽  
General Scheme ◽  
Primary Circuit ◽  
Feed Water ◽  
Outer Diameter ◽  
Intergranular Stress Corrosion ◽  
Methodology Development ◽  
Integrity Assessment ◽  
Piping Systems ◽  
Steel Piping

Operating NPPs license extension activities in Russia produced strong demand for safety improvement of plants build according to earlier standards. Installation of additional supports as pipe whip restraints is one of requirement in acting regulatory documentation which should be followed or compensated by appropriate measures like Leak Before Break (LBB) analyses and improvement of In-Service Inspection (ISI) and Leak Detecting System (LDS). Basic document for LBB concept application to Russian NPP piping is RD 95 10547-99. Its requirements correspond to classical LBB principles used in many countries in Europe, USA and Japan. In many real cases requirements of RD 95 10547-99 could not be applied to safety important NPP piping systems due to the presence of specific features of operational degradation due to some corrosion mechanisms: for example, erosion-corrosion (E-C) for carbon steel piping and intergranular stress corrosion cracking (IGSSC) for heat affected zones of austenitic piping weldments. For special case of RBMK piping with outer diameter 325 mm (potentially susceptible to IGSCC) special Break Preclusion Concept has been developed in Russia after IAEA Extrabudgetary Program in 2000–2002. Contrary to LBB Concept demanding for all four basic principles to be completely fulfilled BP Concept accepts some principles to be fulfilled in a balanced way with demonstration of monitored degradation effectively achieved in operation. Special BP Concept is being developed now to support integrity assessment of RBMK carbon steel steam and feed water piping potentially susceptible to E-C which requires another set of measures to demonstrate principle of controlled degradation in operation then in case of austenitic steel piping. General scheme of piping integrity analyses according to LBB and BP Concepts is discussed and examples of specific approaches to achieve controlled degradation are illustrated in paper. As result of LBB and BP Concepts application it is possible to substantiate reject of additional piping whip restraints implementation on-site. Examples of similar safety methodology development in other countries have been reported at IAEA Specialists Meeting on LBB in Kiev, Ukraine in November 2006.

Numerical Study on the Removal of Hydrogen and Nitrogen from the Melt of Medium Carbon Steel in Vacuum Tank Degasser

2013 ◽  
Vol 762 ◽  
pp. 253-260 ◽  
Author(s):  
Shan Yu ◽  
Jyrki Miettinen ◽  
Seppo Louhenkilpi
Keyword(s):  
Carbon Steel ◽  
Liquid Steel ◽  
Gas Flow ◽  
Numerical Study ◽  
Vacuum Treatment ◽  
Medium Carbon Steel ◽  
Transfer Coefficients ◽  
Ansys Fluent ◽  
Medium Carbon ◽  
Cell Expression

The steelmaking field has been seeing an increased demand of reducing hydrogen and nitrogen in liquid steel before casting. This is often accomplished by vacuum treatment. This paper focuses on developing a numerical model to investigate the removal of hydrogen and nitrogen from the melt of medium carbon steel in a commercial vacuum tank degasser. An activity coefficient model and the eddy-cell expression are implemented in the ANSYS FLUENT code to compute the activities of related elements and mass transfer coefficients of hydrogen and nitrogen in liquid steel. Several cases are simulated to assess the effect of gas flow rate and initial nitrogen content in liquid steel on degassing process and the calculated results are compared with industrial measured data.

Behavior of Radial Incompressible Flow in Pneumatic Dimensional Control Systems

2003 ◽  
Vol 125 (5) ◽  
pp. 843-850 ◽  
Author(s):  
G. Roy ◽  
D. Vo-Ngoc ◽  
D. N. Nguyen ◽  
P. Florent
Keyword(s):  
Gas Flow ◽  
Flow Behavior ◽  
Pressure Gauge ◽  
Axisymmetric Flow ◽  
Low Pressure ◽  
Industrial Applications ◽  
Nozzle Geometry ◽  
Machined Surface ◽  
Flow Area ◽  
Simpler Algorithm

The application of pneumatic metrology to control dimensional accuracy on machined parts is based on the measurement of gas flow resistance through a restricted section formed by a jet orifice placed at a small distance away from a machined surface. The backpressure, which is sensed and indicated by a pressure gauge, is calibrated to measure dimensional variations. It has been found that in some typical industrial applications, the nozzles are subject to fouling, e.g., dirt and oil deposits accumulate on their frontal areas, thus requiring more frequent calibration of the apparatus for reliable service. In this paper, a numerical and experimental analysis of the flow behavior in the region between an injection nozzle and a flat surface is presented. The analysis is based on the steady-state axisymmetric flow of an incompressible fluid. The governing equations, coupled with the appropriate boundary conditions, are solved using the SIMPLER algorithm. Results have shown that for the standard nozzle geometry used in industrial applications, an annular low-pressure separated flow area was found to exist near the frontal surface of the nozzle. The existence of this area is believed to be the cause of the nozzle fouling problem. A study of various alternate nozzle geometries has shown that this low-pressure recirculation area can be eliminated quite readily. Well-designed chamfered, rounded, and reduced frontal area nozzles have all reduced or eliminated the separated recirculation flow area. It has been noted, however, that rounded nozzles may adversely cause a reduction in apparatus sensitivity.

Design and Remnant Life Analysis of a Carbon Steel Containment Jacket Operating in the Creep Range

2004 ◽  
Author(s):  
David Mair
Keyword(s):  
Elevated Temperature ◽  
Carbon Steel ◽  
Creep Behaviour ◽  
Operating Life ◽  
Probabilistic Technique ◽  
History Of ◽  
Routine Inspection ◽  
Life Analysis ◽  
Steam System ◽  
Operating History

During routine inspection of a 35 year old steam generating plant, a large surface crack was found at a critical tee intersection. With the crack appearing to be close to a condition of sudden rupture, a probabilistic technique was used to assist in determining the likelihood of failure. This paper describes this technique and the design of a carbon steel containment jacket used to enclose the cracked area. The design of the jacket had to take into account its creep behaviour at elevated temperature. The advantage of this repair method was that it was able to be installed quickly and without having to completely de-pressure the steam system. It was later decided that the operating life of the jacket should be extended to defer a planned shutdown. A simplified remnant life analysis was then undertaken as detailed in this paper. Taking into account the operating history of the jacket, it demonstrated that the life of the jacket could be safely extended as required.

scholarly journals A Concise Binomial Model for Nonlinear Creep-Fatigue Crack Growth Behavior at Elevated Temperatures

Materials ◽  
2022 ◽  
Vol 15 (2) ◽  
pp. 651
Author(s):  
Jianxing Mao ◽  
Zhixing Xiao ◽  
Dianyin Hu ◽  
Xiaojun Guo ◽  
Rongqiao Wang
Keyword(s):  
Fatigue Crack ◽  
Fatigue Crack Growth ◽  
Crack Growth ◽  
Dwell Time ◽  
Elevated Temperatures ◽  
Nonlinear Creep ◽  
Nickel Based Superalloy ◽  
Proposed Model ◽  
Creep Fatigue ◽  
Creep Fatigue Crack

The creep-fatigue crack growth problem remains challenging since materials exhibit different linear and nonlinear behaviors depending on the environmental and loading conditions. In this paper, we systematically carried out a series of creep-fatigue crack growth experiments to evaluate the influence from temperature, stress ratio, and dwell time for the nickel-based superalloy GH4720Li. A transition from coupled fatigue-dominated fracture to creep-dominated fracture was observed with the increase of dwell time at 600 °C, while only the creep-dominated fracture existed at 700 °C, regardless of the dwell time. A concise binomial crack growth model was constructed on the basis of existing phenomenal models, where the linear terms are included to express the behavior under pure creep loading, and the nonlinear terms were introduced to represent the behavior near the fracture toughness and during the creep-fatigue interaction. Through the model implementation and validation of the proposed model, the correlation coefficient is higher than 0.9 on ten out of twelve sets of experimental data, revealing the accuracy of the proposed model. This work contributes to an enrichment of creep-fatigue crack growth data in the typical nickel-based superalloy at elevated temperatures and could be referable in the modeling for damage tolerance assessment of turbine disks.

Load Factor for Evaluating Non-Planar Flaws in Carbon Steel Piping Using Limit Load Methodology

2016 ◽  
Author(s):  
Phuong H. Hoang
Keyword(s):  
Carbon Steel ◽  
Nuclear Power ◽  
Power Plants ◽  
Pipe Wall ◽  
Local Strain ◽  
Limit Load ◽  
Evaluation Methodology ◽  
Load Factor ◽  
Wall Thinning ◽  
Steel Piping

Non-planar flaw such as local wall thinning flaw is a major piping degradation in nuclear power plants. Hundreds of piping components are inspected and evaluated for pipe wall loss due to flow accelerated corrosion and microbiological corrosion during a typical scheduled refueling outage. The evaluation is typically based on the original code rules for design and construction, and so often that uniformly thin pipe cross section is conservatively assumed. Code Case N-597-2 of ASME B&PV, Section XI Code provides a simplified methodology for local pipe wall thinning evaluation to meet the construction Code requirements for pressure and moment loading. However, it is desirable to develop a methodology for evaluating non-planar flaws that consistent with the Section XI flaw evaluation methodology for operating plants. From the results of recent studies and experimental data, it is reasonable to suggest that the Section XI, Appendix C net section collapse load approach can be used for non-planar flaws in carbon steel piping with an appropriate load multiplier factor. Local strain at non-planar flaws in carbon steel piping may reach a strain instability prior to net section collapse. As load increase, necking starting at onset strain instability leads to crack initiation, coalescence and fracture. Thus, by limiting local strain to material onset strain instability, a load multiplier factor can be developed for evaluating non-planar flaws in carbon steel piping using limit load methodology. In this paper, onset strain instability, which is material strain at the ultimate stress from available tensile test data, is correlated with the material minimum specified elongation for developing a load factor of non-planar flaws in various carbon steel piping subjected to multiaxial loading.

Sign in / Sign up

Export Citation Format

Share Document