Estimation of Suppressing Warpage for Heterogeneous Integration of Packaging Framework by Utilizing Equivalent Material Simulated Technique

2021 ◽  
Author(s):  
Chang-Chun Lee ◽  
Chi-Wei Wang ◽  
Te-Pei Hsiang
Keyword(s):  
Heterogeneous Integration ◽  
Equivalent Material

scholarly journals Ductile failure analysis of epoxy resin plates containing multiple circular arc cracks by means of the equivalent material concept

2021 ◽  
Vol 16 (1) ◽  
Author(s):  
M. Pourseifi ◽  
A. S. Rahimi
Keyword(s):  
Ductile Failure ◽  
Equivalent Material ◽  
Circular Arc ◽  
Equivalent Material Concept ◽  
Crack Tips ◽  
Fracture Tests ◽  
Polymeric Samples ◽  
Cracked Specimens ◽  
Brittle Fracture Criterion ◽  
Material Concept

AbstractDuctile failure of polymeric samples weakened by circular arc cracks is studied theoretically and experimentally in this research. Various arrangements of cracks with different arc angles are considered in the specimens such that crack tips experienced the mixed mode I/II loading conditions. Fracture tests are conducted on the multi-cracked specimens and their fracture loads are achieved. To provide the results, the equivalent material concept (EMC) is used in conjunction of dislocation method and a brittle fracture criterion such that there is no necessity for performing complex and time-consuming elastic-plastic damage analyses. Theoretical and experimental stress intensity factors are computed and compared with each other by employing the fracture curves which demonstrate the appropriate efficiency of proposed method to predict the tests results.