Failure assessment of the first stage high-pressure turbine blades in an aero-engine turbine

2017 ◽  
Vol 40 (12) ◽  
pp. 2092-2106 ◽  
Author(s):  
D. Shi ◽  
C. Wang ◽  
X. Yang ◽  
S. Li
Keyword(s):  
High Pressure ◽  
Turbine Blades ◽  
High Pressure Turbine ◽  
Failure Assessment ◽  
Aero Engine

Failure Assessment of the First Stage High Pressure Turbine Blades

2016 ◽  
Vol 853 ◽  
pp. 498-502 ◽  
Author(s):  
Chan Wang ◽  
Duo Qi Shi ◽  
Xiao Guang Yang
Keyword(s):  
High Pressure ◽  
Low Cycle Fatigue ◽  
Turbine Blades ◽  
Microstructural Characterization ◽  
Damage Mechanism ◽  
High Pressure Turbine ◽  
Element Analysis ◽  
Failure Assessment ◽  
Creep Fatigue ◽  
Simulation And Experiment

Ni-based superalloys are used as turbine blade material in which creep-fatigue is an important damage mechanism. Simulation and experiment methods are used to investigate and predicte the failure mechanism of the first stage high pressure turbine blades of an aeroengine after 600 hours service. The high pressure turbine blades were made of Ni-base superalloy DZ4, fabricated by DS investment casting. The largest stress point was obtained by finite element analysis. During the fatigue test, the high temperature and low cycle fatigue/creep load simulating the real working condition were applied on the blades until they fractured. And then several examinations were carried out to identify the fracture’s main cause, such as visual examination, SEM fractography and microstructural characterization. In conclusion, the fracture of the high pressure turbine blades was mainly caused by the interaction of the fatigue and creep. Besides, the oxidation accelerated the blades fracture.

Aerothermal Effect of Cavity Welding Beads on a Transonic Squealer Tip

2020 ◽  
Author(s):  
Joao Vieira ◽  
John Coull ◽  
Peter Ireland ◽  
Eduardo Romero
Keyword(s):  
High Pressure ◽  
Film Cooling ◽  
Turbine Blades ◽  
Reynolds Numbers ◽  
High Pressure Turbine ◽  
Cooling Effectiveness ◽  
Film Cooling Effectiveness ◽  
Aerodynamic Loss ◽  
Blade Tip ◽  
Mass Flow Rates

Abstract High pressure turbine blade tips are critical for gas turbine performance and are sensitive to small geometric variations. For this reason, it is increasingly important for experiments and simulations to consider real geometry features. One commonly absent detail is the presence of welding beads on the cavity of the blade tip, which are an inherent by-product of the blade manufacturing process. This paper therefore investigates how such welds affect the Nusselt number, film cooling effectiveness and aerodynamic performance. Measurements are performed on a linear cascade of high pressure turbine blades at engine realistic Mach and Reynolds numbers. Two cooled blade tip geometries were tested: a baseline squealer geometry without welding beads, and a case with representative welding beads added to the tip cavity. Combinations of two tip gaps and several coolant mass flow rates were analysed. Pressure sensitive paint was used to measure the adiabatic film cooling effectiveness on the tip, which is supplemented by heat transfer coefficient measurements obtained via infrared thermography. Drawing from all of this data, it is shown that the weld beads have a generally detrimental impact on thermal performance, but with local variations. Aerodynamic loss measured downstream of the cascade is shown to be largely insensitive to the weld beads.

scholarly journals Evaluation of High Pressure Turbine Blade Coatings on an LM2500 Rainbow Rotor

1995 ◽  
Author(s):  
B. Nagaraj ◽  
G. Katz ◽  
A. F. Maricocchi ◽  
M. Rosenzweig
Keyword(s):  
High Pressure ◽  
Turbine Blades ◽  
Leading Edge ◽  
Service Evaluation ◽  
High Pressure Turbine ◽  
Barrier Coating ◽  
Marine Propulsion ◽  
Corrosion Resistant Coatings ◽  
Stage 1 ◽  
Plasma Sprayed

Two LM2500 rainbow rotors with repaired stage 1 and stage 2 high pressure turbine blades are being assembled for marine propulsion service evaluation by the US Navy. The blades have seen between 5,000 and 15,000 hours of service in the Navy’s Fleets. A number of corrosion resistant coatings including plasma sprayed CoCrAlHf (bill of material), composite plated CoCrAlHf, platinum aluminide, aluminum silicide, and physical vapor deposited yttria stabilized zirconia thermal barrier coating (PVD TBC) will be evaluated in the rainbow rotor. This paper will discuss the advantages and microstructures of the various coatings. Composite plated CoCrAlHf, and PVD TBCs were recently service evaluated in an industrial LM2500 rainbow rotor for 10,500 hours. Both these coatings performed well, although the PVD TBC had local spallation at the leading edge. This paper will review the details of performance of these two coatings in the industrial LM2500 application.

Using CFD to Reduce Resonant Stresses on a Single-Stage, High-Pressure Turbine Blade

2002 ◽  
Author(s):  
J. P. Clark ◽  
A. S. Aggarwala ◽  
M. A. Velonis ◽  
R. E. Gacek ◽  
S. S. Magge ◽  
...  
Keyword(s):  
High Pressure ◽  
Turbine Blade ◽  
Guide Vane ◽  
Turbine Blades ◽  
Suction Side ◽  
Lessons Learned ◽  
Single Stage ◽  
Navier Stokes ◽  
High Pressure Turbine ◽  
Time Resolved

The ability to predict levels of unsteady forcing on high-pressure turbine blades is critical to avoid high-cycle fatigue failures. In this study, 3D time-resolved computational fluid dynamics is used within the design cycle to predict accurately the levels of unsteady forcing on a single-stage high-pressure turbine blade. Further, nozzle-guide-vane geometry changes including asymmetric circumferential spacing and suction-side modification are considered and rigorously analyzed to reduce levels of unsteady blade forcing. The latter is ultimately implemented in a development engine, and it is shown successfully to reduce resonant stresses on the blade. This investigation builds upon data that was recently obtained in a full-scale, transonic turbine rig to validate a Reynolds-Averaged Navier-Stokes (RANS) flow solver for the prediction of both the magnitude and phase of unsteady forcing in a single-stage HPT and the lessons learned in that study.

Investigation of Combustor-Turbine-Interaction in a Rotating Cooled Transonic High-Pressure Turbine Test Rig: Part 2 — Numerical Modelling and Simulation

2019 ◽  
Author(s):  
Simon Gövert ◽  
Federica Ferraro ◽  
Alexander Krumme ◽  
Clemens Buske ◽  
Marc Tegeler ◽  
...  
Keyword(s):  
High Pressure ◽  
Flame Stabilization ◽  
Test Facility ◽  
Test Rig ◽  
High Pressure Turbine ◽  
Lean Burn ◽  
Turbine Inlet ◽  
Measurement Results ◽  
Aero Engine ◽  
Inlet Conditions

Abstract Reducing the uncertainties in the prediction of turbine inlet conditions is a crucial aspect to improve aero engine designs and further increase engine efficiencies. To meet constantly stricter emission regulations, lean burn combustion could play a key role for future engine designs. However, these combustion systems are characterized by significant swirl for flame stabilization and reduced cooling air mass flows. As a result, substantial spatial and transient variations of the turbine inlet conditions are encountered. To investigate the effect of the combustor on the high pressure turbine, a rotating cooled transonic high-pressure configuration has been designed and investigated experimentally at the DLR turbine test facility ‘NG-Turb’ in Göttingen, Germany. It is a rotating full annular 1.5 stage turbine configuration which is coupled to a combustor simulator. The combustor simulator is designed to create turbine inlet conditions which are hydrodynamically representative for a lean-burn aero engine. A detailed description of the test rig and its instrumentation as well as a discussion of the measurement results is presented in part I of this paper. Part II focuses on numerical modeling of the test rig to further extend the understanding of the measurement results. Integrated simulations of the configuration including combustor simulator and nozzle guide vanes are performed for leading edge and passage clocking position and the effect on the hot streak migration is discussed. The simulation and experimental results at the combustor-turbine interface are compared showing a good overall agreement. The relevant flow features are correctly predicted in the simulations, proving the suitability of the numerical model for application to integrated combustor-turbine interaction analysis.

Sign in / Sign up

Export Citation Format

Share Document