Non-destructive evaluation of fatigue damage and fatigue crack initiation in type 316 stainless steel by positron annihilation line-shape and lifetime analyses

2016 ◽  
Vol 40 (7) ◽  
pp. 1143-1153 ◽  
Author(s):  
Y Uematsu ◽  
T Kakiuchi ◽  
K Hattori ◽  
N Uesugi ◽  
F Nakao
Keyword(s):  
Stainless Steel ◽  
Fatigue Crack ◽  
Crack Initiation ◽  
Positron Annihilation ◽  
Fatigue Damage ◽  
Line Shape ◽  
Fatigue Crack Initiation ◽  
Annihilation Line ◽  
Non Destructive Evaluation ◽  
Non Destructive

Plastic Slip and Early Stage of Fatigue Damage in Polycrystals: Comparison between Experiments and Crystal Plasticity Finite Elements Simulations

2014 ◽  
Vol 891-892 ◽  
pp. 1711-1716 ◽  
Author(s):  
Loic Signor ◽  
Emmanuel Lacoste ◽  
Patrick Villechaise ◽  
Thomas Ghidossi ◽  
Stephan Courtin
Keyword(s):  
Fatigue Crack ◽  
Finite Elements ◽  
Crack Initiation ◽  
Fatigue Damage ◽  
Crystal Plasticity ◽  
Early Stage ◽  
Low Cycle Fatigue ◽  
Fatigue Cracks ◽  
Fatigue Crack Initiation ◽  
Plastic Slip

For conventional materials with solid solution, fatigue damage is often related to microplasticity and is largely sensitive to microstructure at different scales concerning dislocations, grains and textures. The present study focuses on slip bands activity and fatigue crack initiation with special attention on the influence of the size, the morphology and the crystal orientation of grains and their neighbours. The local configurations which favour - or prevent - crack initiation are not completely identified. In this work, the identification and the analysis of several crack initiation sites are performed using Scanning Electron Microscopy and Electron Back-Scattered Diffraction. Crystal plasticity finite elements simulation is employed to evaluate local microplasticity at the scale of the grains. One of the originality of this work is the creation of 3D meshes of polycrystalline aggregates corresponding to zones where fatigue cracks have been observed. 3D data obtained by serial-sectioning are used to reconstruct actual microstructure. The role of the plastic slip activity as a driving force for fatigue crack initiation is discussed according to the comparison between experimental observations and simulations. The approach is applied to 316L type austenitic stainless steels under low-cycle fatigue loading.

Modeling of Fatigue Crack Propagation

2004 ◽  
Vol 126 (1) ◽  
pp. 77-86 ◽  
Author(s):  
Yanyao Jiang ◽  
Miaolin Feng
Keyword(s):  
Fatigue Crack ◽  
Fatigue Crack Growth ◽  
Crack Initiation ◽  
Crack Propagation ◽  
Crack Growth ◽  
Fatigue Damage ◽  
Fatigue Crack Propagation ◽  
Fatigue Crack Initiation ◽  
Cyclic Plasticity ◽  
R Ratio

Fatigue crack propagation was modeled by using the cyclic plasticity material properties and fatigue constants for crack initiation. The cyclic elastic-plastic stress-strain field near the crack tip was analyzed using the finite element method with the implementation of a robust cyclic plasticity theory. An incremental multiaxial fatigue criterion was employed to determine the fatigue damage. A straightforward method was developed to determine the fatigue crack growth rate. Crack propagation behavior of a material was obtained without any additional assumptions or fitting. Benchmark Mode I fatigue crack growth experiments were conducted using 1070 steel at room temperature. The approach developed was able to quantitatively capture all the important fatigue crack propagation behaviors including the overload and the R-ratio effects on crack propagation and threshold. The models provide a new perspective for the R-ratio effects. The results support the notion that the fatigue crack initiation and propagation behaviors are governed by the same fatigue damage mechanisms. Crack growth can be treated as a process of continuous crack nucleation.

Creep-Fatigue Damage and Crack Initiation for a Mod 9Cr-1Mo Structure With Weldments

2007 ◽  
Author(s):  
Hyeong-Yeon Lee ◽  
Se-Hwan Lee ◽  
Jong-Bum Kim ◽  
Jae-Han Lee
Keyword(s):  
Fatigue Crack ◽  
Crack Initiation ◽  
Fatigue Damage ◽  
Hold Time ◽  
Fatigue Crack Initiation ◽  
Creep Damage ◽  
Steel Specimen ◽  
Structural Test ◽  
Creep Fatigue ◽  
Creep Fatigue Crack

A structural test and evaluation on creep-fatigue damage, and creep-fatigue crack initiation have been carried out for a Mod. 9Cr-1Mo steel structural specimen with weldments. The conservatisms of the design codes of ASME Section III subsection and NH and RCC-MR codes were quantified at the welded joints of Mod.9Cr-1Mo steel and 316L stainless steel with the observed images from the structural test. In creep damage evaluation using the RCC-MR code, isochronous curve has been used rather than directly using the creep law as the RCC-MR specifies. A y-shaped steel specimen of a diameter 500mm, height 440mm and thickness 6.35mm is subjected to creep-fatigue loads with two hours of a hold time at 600°C and a primary nominal stress of 30MPa. The defect assessment procedures of RCC-MR A16 guide do not provide a procedure for Mod.9Cr-1Mo steel yet. In this study application of σd method for the assessment of creep-fatigue crack initiation has been examined for a Mod. 9Cr-1Mo steel structure.