scholarly journals Nanograin layer formation at crack initiation region for very-high-cycle fatigue of a Ti-6Al-4V alloy

2016 ◽  
Vol 40 (6) ◽  
pp. 979-993 ◽  
Author(s):  
H. Su ◽  
X. Liu ◽  
C. Sun ◽  
Y. Hong
Keyword(s):  
Crack Initiation ◽  
High Cycle Fatigue ◽  
Cycle Fatigue ◽  
Layer Formation ◽  
Very High Cycle Fatigue ◽  
Very High

scholarly journals Recent Advances in Very High Cycle Fatigue Behavior of Metals and Alloys—A Review

Metals ◽  
2020 ◽  
Vol 10 (9) ◽  
pp. 1200
Author(s):  
Ashutosh Sharma ◽  
Min Chul Oh ◽  
Byungmin Ahn
Keyword(s):  
Crack Initiation ◽  
High Cycle Fatigue ◽  
Fatigue Testing ◽  
Fatigue Behavior ◽  
Simulation Studies ◽  
Cycle Fatigue ◽  
Future Directions ◽  
Very High Cycle Fatigue ◽  
Ultrasonic Fatigue ◽  
Very High

We reviewed the research and developments in the field of fatigue failure, focusing on very-high cycle fatigue (VHCF) of metals, alloys, and steels. We also discussed ultrasonic fatigue testing, historical relevance, major testing principles, and equipment. The VHCF behavior of Al, Mg, Ni, Ti, and various types of steels were analyzed. Furthermore, we highlighted the major defects, crack initiation sites, fatigue models, and simulation studies to understand the crack development in VHCF regimes. Finally, we reviewed the details regarding various issues and challenges in the field of VHCF for engineering metals and identified future directions in this area.

scholarly journals Properties of the Fine Granular Area and Postulated Models for Its Formation during Very High Cycle Fatigue—A Review

2020 ◽  
Vol 10 (23) ◽  
pp. 8475
Author(s):  
Jan Patrick Sippel ◽  
Eberhard Kerscher
Keyword(s):  
Fatigue Strength ◽  
Crack Initiation ◽  
Crack Growth ◽  
High Performance ◽  
High Cycle Fatigue ◽  
The Other ◽  
Cycle Fatigue ◽  
Very High Cycle Fatigue ◽  
Open Questions ◽  
Very High

Understanding the mechanisms leading to very high cycle fatigue is necessary to make predictions about the behavior under various conditions and to ensure safe design over the whole lifetime of high-performance components. It is further vital for the development of possible measures to increase the very high cycle fatigue strength. This review therefore intends to give an overview of the properties of the fine granular area that have been observed so far. Furthermore, the existing models to describe the early crack initiation and crack growth within the very high cycle fatigue regime are outlined and the models are evaluated on the basis of the identified fine granular area properties. The aim is to provide an overview of the models that can already be considered refuted and to specify the respective open questions regarding the other individual models.

Effect of shot peening on very high cycle fatigue of 2024-T351 aluminium alloy

2020 ◽  
Vol 10 (7) ◽  
pp. 1032-1039
Author(s):  
Renhui Tian ◽  
Jiangfeng Dong ◽  
Yongjie Liu ◽  
Qingyuan Wang ◽  
Yunrong Luo
Keyword(s):  
Fracture Surface ◽  
Crack Initiation ◽  
Shot Peening ◽  
High Cycle Fatigue ◽  
Fatigue Tests ◽  
Cycle Fatigue ◽  
Very High Cycle Fatigue ◽  
Fatigue Strength Improvement ◽  
Ultrasonic Fatigue ◽  
Very High

To investigate the influence of shot peening (SP) on very high cycle fatigue (VHCF) performance of 2024-T351, the specimens with three surface conditions were performed under ultrasonic fatigue tests: mechanicallypolished without peening (NP), ceramic shot peening (SP1), steel and glass mixed shot peening (SP2). The roughness, microhardness, residual stress, fractography measurement and scanning electron microscopy (SEM) were applied before fatigue test to characterize the effective layer induced by the peening treatment. For the failed specimens, the fracture surface were analysed using SEM to study the mechanisms of fatigue crack propagation. In addition, the fatigue life curve in ultra-high cycle region continuously decreased in the three series of specimens. However, the experimental results revealed that fatigue strength improvement resulting from shot peening treatment was negligible in very high cycle regime. Furthermore, the stress intensity factor for the surface crack initiation (SCI) and interior crack initiation (ICI) was discussed based on quantitative analysis on the fracture surface. The average values of ΔKfish-eye for NP, SP1 and SP2 specimens are about 2.22, 1.48 and 1.61 MPa · m1/2, respectively.