Durability Analysis of SnAgCu Solder Joints for an Aerospace Application

2008 ◽  
Author(s):  
Amir M. Lajimi ◽  
Joel Cugnoni ◽  
John Botsis
Keyword(s):  
Solder Joints ◽  
Snagcu Solder ◽  
Aerospace Application ◽  
Durability Analysis

Effect of thermal aging on the interfacial structure of SnAgCu solder joints on Cu

2007 ◽  
Vol 47 (12) ◽  
pp. 2161-2168 ◽  
Author(s):  
Weiqun Peng ◽  
Eduardo Monlevade ◽  
Marco E. Marques
Keyword(s):  
Thermal Aging ◽  
Solder Joints ◽  
Interfacial Structure ◽  
Snagcu Solder

A competition between stress triaxiality and joule heating on microstructure evolution and degradation of SnAgCu solder joints

2020 ◽  
Vol 54 ◽  
pp. 221-227
Author(s):  
Waluyo Adi Siswanto ◽  
M. Arun ◽  
Irina V. Krasnopevtseva ◽  
A. Surendar ◽  
Andino Maseleno
Keyword(s):  
Joule Heating ◽  
Microstructure Evolution ◽  
Solder Joints ◽  
Stress Triaxiality ◽  
Snagcu Solder

scholarly journals Mechanical Behaviour of Grains in SnAgCu Solder Joints

2006 ◽  
Author(s):  
Jicheng Gong ◽  
Changqing Liu ◽  
Paul P. Conway ◽  
Vadim V. Silberschmidt
Keyword(s):  
Mechanical Behaviour ◽  
Solder Joints ◽  
Snagcu Solder

scholarly journals A Mechanistic Thermal Fatigue Model for SnAgCu Solder Joints

2018 ◽  
Vol 47 (5) ◽  
pp. 2526-2544 ◽  
Author(s):  
Peter Borgesen ◽  
Luke Wentlent ◽  
Sa’d Hamasha ◽  
Saif Khasawneh ◽  
Sam Shirazi ◽  
...  
Keyword(s):  
Thermal Fatigue ◽  
Solder Joints ◽  
Snagcu Solder ◽  
Fatigue Model

Measurement of impact toughness of eutectic SnPb and SnAgCu solder joints in ball grid array by mini-impact tester

2008 ◽  
Vol 23 (5) ◽  
pp. 1482-1487 ◽  
Author(s):  
Yuhuan Xu ◽  
Shengquan Ou ◽  
K.N. Tu ◽  
Kejun Zeng ◽  
Rajiv Dunne
Keyword(s):  
Impact Toughness ◽  
High Speed ◽  
Solder Joints ◽  
Ball Grid Array ◽  
Snagcu Solder ◽  
Snpb Solder ◽  
Impact Tester ◽  
Pull Tests ◽  
The Impact ◽  
Eutectic Snpb

The most frequent cause of failure for wireless, handheld, and portable consumer electronic products is an accidental drop to the ground. The impact may cause interfacial fracture of ball-grid-array solder joints. Existing metrology, such as ball shear and ball pull tests, cannot characterize the impact-induced high speed fracture failure. In this study, a mini-impact tester was utilized to measure the impact toughness and to characterize the impact reliability of both eutectic SnPb and SnAgCu solder joints. The annealing effect at 150 °C on the impact toughness was investigated, and the fractured surfaces were examined. The impact toughness of SnAgCu solder joints with the plating of electroless Ni/immersion Au (ENIG) became worse after annealing, decreasing from 10 or 11 mJ to 7 mJ. On the other hand, an improvement of the impact toughness of eutectic SnPb solder joints with ENIG was recorded after annealing, increasing from 6 or 10 to 15 mJ. Annealing has softened the bulk SnPb solder so that more plastic deformation can occur to absorb the impact energy.

Effect of RE on Creep Rupture Life of SnAgCu Solder Joints

2011 ◽  
Vol 687 ◽  
pp. 39-43
Author(s):  
Yao Li Wang ◽  
Gai Hong Dong ◽  
Chen Yang Li ◽  
Zhi Wei Wu ◽  
Jing Sun
Keyword(s):  
Rare Earth ◽  
Solder Alloy ◽  
Interfacial Layer ◽  
Solder Joints ◽  
Rupture Life ◽  
Creep Property ◽  
Creep Rupture ◽  
Sectional Area ◽  
Cross Sectional ◽  
Snagcu Solder

Creep property is one of the most important factors to affect the reliability of soldered joints. The effect of rare earth(RE) on the creep rupture life of Sn2.5Ag0.7Cu solder joints were investigated under constant temperature and stress using creep specimens with a 1mm2cross sectional area. The results show that adding tiny RE in Sn2.5Ag0.7Cu solder alloy can effectually affect the size and configuration of the intermetallic compound (IMC) of interfacial layer. The IMC of Sn2.5Ag0.7Cu interfacial layer is thinner and its thickness is homogeneous with adding 0.1% RE, and the creep rupture life of solder joints is longest, which is apparently superior to that of Sn2.5Ag0.7Cu and commercial used Sn3.8Ag0.7Cu solder alloy.