Dielectric and piezoelectric properties of PbFe1/2Nb1/2O3-PbTiO3 ceramics from the morphotropic phase boundary compositional range

2011 ◽  
Vol 58 (9) ◽  
pp. 1914-1919 ◽  
Author(s):  
E. I. Sitalo ◽  
I. P. Raevski ◽  
A. G. Lutokhin ◽  
A. V. Blazhevich ◽  
S. P. Kubrin ◽  
...  
Keyword(s):  
Phase Boundary ◽  
Morphotropic Phase Boundary ◽  
Piezoelectric Properties ◽  
Compositional Range ◽  
Pbtio3 Ceramics ◽  
Dielectric And Piezoelectric Properties

Investigation of the Morphotropic Phase Boundary (MPB) of (1-x-y)BaZrO3-x(K0.45Na0.5Li0.05)NbO3-yBi (Mg0.5Ti0.5)O3

2014 ◽  
Vol 787 ◽  
pp. 242-246
Author(s):  
Rui Lin Wu ◽  
Tomoaki Karaki ◽  
Jiang Tao Zeng ◽  
Liao Ying Zheng ◽  
Wei Ruan ◽  
...  
Keyword(s):  
Phase Boundary ◽  
Morphotropic Phase Boundary ◽  
Tetragonal Phase ◽  
Room Temperature ◽  
Piezoelectric Properties ◽  
Piezoelectric Ceramics ◽  
Solid State Reaction Method ◽  
Lead Free ◽  
Reaction Method ◽  
Dielectric And Piezoelectric Properties

Lead-based piezoelectric ceramics have excellent piezoelectric properties with the compositions near the rhombohedral-tetragonal morphotropic phase boundary (MPB)[1,2]. In these materials, the dielectric and piezoelectric properties show the maximal values at MPB. For lead-free piezoelectric ceramics, finding the MPB area is a promising way to improve their properties. In this paper, the (1-x-y)BaZrO3-x(K0.45Na0.5Li0.05)NbO3-yBi (Mg0.5Ti0.5)O3 lead-free piezoelectric ceramics were prepared by solid-state reaction method, and their piezoelectric properties and dielectric properties were investigated. With the increase of KNLN content, the crystal structure changed from rombohedral phase to tetragonal phase, thus existed a MPB[3,4] between rombohedral and tetragonal phase. At room temperature, the specimen with the composition at MPB (x=0.93, y=0.01) shows the optimal piezoelectric properties (d33=225pC/N and kp=45%), which indicates that this material is a potential lead-free piezoceramic.

Dielectric and Piezoelectric Properties of Gd-modified (1-x) BiFeO3-xPbTiO3 Ceramics with a Morphotropic Phase Boundary

2013 ◽  
Vol 1507 ◽  
Author(s):  
Dalei Wang ◽  
Shundong Bu ◽  
Guoxi Jin ◽  
RuiDai ◽  
Dengren Jin ◽  
...  
Keyword(s):  
Dielectric Constant ◽  
Phase Boundary ◽  
Morphotropic Phase Boundary ◽  
Composition Range ◽  
Piezoelectric Properties ◽  
X Ray Diffraction ◽  
Wide Composition Range ◽  
X Ray ◽  
Dielectric Constant And Loss ◽  
Dielectric And Piezoelectric Properties

ABSTRACT(1-x)(Bi0.8Gd0.2)FeO3-xPbTiO3 (BGF-PT) solid solutions ceramics of x=0.55,0.50,0.4975, 0.49 and 0.45 were prepared by the mixed oxide method. Gd3+ of 20 at% was introduced into the Bi3+ site to improve the dielectric and piezoelectric properties of BFPT without causing the significant reduction of Curie temperature (Tc). X-ray diffraction analysis shows a transformation from the tetragonal (T) to rhombohedral (R) phase with the increase of BGF content. The morphotropic phase boundary was determined by measuring the dielectric and piezoelectric properties of BGF-PT within a wide composition range. BGF-PT for x=0.4975 shows the coexistence of T and R phases with the dielectric constant and loss of about 895 and 0.031 respectively at the frequency of 102 Hz.