Assessment of the friction stir welding parameters effect on mechanical properties and defect formation in 10 mm thick AA5056 alloy welded joints

2020 ◽  
Author(s):  
T. A. Kalashnikova ◽  
V. A. Beloborodov
Keyword(s):  
Mechanical Properties ◽  
Friction Stir Welding ◽  
Welded Joints ◽  
Defect Formation ◽  
Welding Parameters ◽  
Friction Stir

scholarly journals The Effects of In-Process Cooling during Friction Stir Welding of 7475 Aluminium Alloy

2021 ◽  
Vol 50 (9) ◽  
pp. 2743-2754
Author(s):  
Ashish Jacob ◽  
Sachin Maheshwari ◽  
Arshad Noor Siddiquee ◽  
Abdulrahman Al-Ahmari ◽  
Mustufa Haider Abidi ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Friction Stir Welding ◽  
Welded Joints ◽  
Positive Impact ◽  
Welding Process ◽  
Fusion Welding ◽  
Friction Stir ◽  
Cooling Conditions ◽  
Zero Degree ◽  
Welding Technique

Certain age hardenable alloys such as AA7475 cannot be joined with perfection using fusion welding techniques. This requires non-conventional welding technique such as friction stir welding process to join these ‘difficult to weld’ alloys. In this study, three different cooling conditions i.e. cryogenic, sub-zero, and zero-degree Celsius temperature conditions have been analyzed to understand its impact on the welding process. In-process cooling was found to behave effectively and also enhanced the mechanical properties of the welded joints. A stable microstructure was clearly seen in the images observed under the metallurgical microscope. The weld efficiencies were found to be good in each of the samples which are indicative of a strong metallic joint. The effective cooling conditions employed had an overall positive impact on the joint.

A Study on Friction Stir Welding Process for AA2219/AA2195 Joints

2018 ◽  
Vol 762 ◽  
pp. 339-342
Author(s):  
Ho Sung Lee ◽  
Koo Kil No ◽  
Joon Tae Yoo ◽  
Jong Hoon Yoon
Keyword(s):  
Friction Stir Welding ◽  
Welded Joints ◽  
Rotation Speed ◽  
Microstructural Analysis ◽  
Frictional Heat ◽  
Welding Parameters ◽  
Manufacturing Cost ◽  
Significant Saving ◽  
Friction Stir ◽  
Rotation Direction

The object of this study was to study mechanical properties of friction stir welded joints of AA2219 and AA2195. AA2219 has been used as an aerospace materials for many years primarily due to its high weldability and high specific strength in addition to the excellent cryogenic property so to be successfully used for manufacturing of cryogenic fuel tank for space launcher. Relatively new Aluminum-Lithium alloy, AA2195 provides significant saving on weight and manufacturing cost with application of friction stir welding. Friction stir welding is a solid-state joining process, which use a spinning tool to produce frictional heat in the work piece. To investigate the effect of the rotation direction of the tool, the joining was performed by switching the positions of the two dissimilar alloys. The welding parameters include the travelling speed, rotation speed and rotation direction of the tool, and the experiment was conducted under the condition that the travelling speed of the tool was 120-300 mm/min and the rotation speed of the tool was 400-800 rpm. Tensile tests were conducted to study the strength of friction stir welded joints and microhardness were measured with microstructural analysis. The results indicate the failure occurred in the relatively weaker TMAZ/HAZ interface of AA2219. The optimum process condition was obtained at the rotation speed of 600-800 rpm and the travelling speed of 180-240 mm/min.

scholarly journals Research on the Friction Stir Welding of Sc-Modified AA2519 Extrusion

Metals ◽  
2019 ◽  
Vol 9 (10) ◽  
pp. 1024 ◽  
Author(s):  
Robert Kosturek ◽  
Lucjan Śnieżek ◽  
Janusz Torzewski ◽  
Marcin Wachowski
Keyword(s):  
Mechanical Properties ◽  
Friction Stir Welding ◽  
Base Material ◽  
Stir Zone ◽  
Welding Parameters ◽  
Friction Stir ◽  
Treated Condition ◽  
Heat Treated ◽  
Heat Treated Condition ◽  
Fsw Parameters

The aim of this research was to investigate the effect of friction stir welding (FSW) parameters on microstructure and mechanical properties of Sc-modified AA2519 extrusion joints. The workpiece was welded by FSW in non-heat-treated condition with seven different sets of welding parameters. For each obtained joint macrostructure and microstructure observations were performed. Mechanical properties of joints were investigated using tensile test together with localization of fracture location. Joint efficiencies were established by comparing measured joints tensile strength to the value for base material. The obtained results show that investigated FSW joints of Sc-modified AA2519 in the non-heat-treated condition have joint efficiency within the range 87–95%. In the joints obtained with the lowest ratio of the tool rotation speed to the tool traverse speed, the occurrence of imperfections (voids) localized in the stir zone was reported. Three selected samples were subjected to further investigations consisting microhardness distribution and scanning electron microscopy fractography analysis. As the result of dynamic recrystallization, the microhardness of the base material value of 86 HV0.1 increased to about 110–125 HV0.1 in the stir zone depending on the used welding parameters. Due to lack of the strengthening phase and low strain hardening of used alloy the lack of a significantly softened zone was reported by both microhardness analysis and investigation of the fractured samples.

scholarly journals Friction Stir Welding Parameters: Impact of Abnormal Grain Growth during Post-Weld Heat Treatment on Mechanical Properties of Al–Mg–Si Welded Joints

Metals ◽  
2020 ◽  
Vol 10 (12) ◽  
pp. 1607
Author(s):  
Amir Hossein Baghdadi ◽  
Zainuddin Sajuri ◽  
Mohd Zaidi Omar ◽  
Armin Rajabi
Keyword(s):  
Mechanical Properties ◽  
Heat Treatment ◽  
Friction Stir Welding ◽  
Grain Growth ◽  
Precipitation Hardening ◽  
Al Alloys ◽  
Abnormal Grain Growth ◽  
Post Weld Heat Treatment ◽  
Welding Parameters ◽  
Friction Stir

Friction stir welding (FSW) is an alternative method to join aluminum (Al) alloys in a solid-state condition. However, the coarsening or dissolution of precipitation hardening phases in the welding zone causes strength reduction or softening behavior in the welded area of age-hardened Al alloys. Therefore, this research aimed to improve the mechanical properties of an FSW Al–Mg–Si alloy via post-weld heat treatment (PWHT) and the possibility of controlling the abnormal grain growth (AGG) using different welding parameters. FSW was performed with different rotational and travel speeds, and T6 heat treatment was carried out on the FSW samples as the PWHT. The results showed a decrease in the strength of the FSW samples compared with that of the base material (BM) due to the dissolution of precipitation hardening particles in the heat-affected zone. However, the emergence of AGG in the microstructure after the T6-PWHT was identified as the potential event in the microstructure of the PWHT samples. It is found that the AGG of the microstructure in similar joints of Al6061(T6) was governed by the welding parameters. The results proved that PWHT was able to increase the tensile properties of the welded samples to values comparable to that of Al6061(T6)-BM. The increased mechanical properties of the FSW joints were attributed to a proper PWHT that resulted in a homogeneous distribution of the precipitation hardening phases in the welding zones.