ABSTRACTElectrical conduction properties of charge ordering type ferroelectrics YFe2O4 were investigated. YFe2O4 was synthesized in reduced atmosphere at 1200 °C. Oxygen partial pressure of the reduced atmosphere was controlled by the equilibrium state of CO and CO2. YFe2O4 is paramagnetic at room temperature and has Néel temperature around 250K. The Néel temperature was decreased with increasing the amount of oxygen deficiency. Moreover, YFe2O4 showed ohmic conduction from 260 to 100 K. The temperature dependence of the DC conductivity showed an inflection point at the Néel temperature, which indicated the development of charge ordering of Fe2+ and Fe3+ ions. From the complex impedance measurements, the equivalent circuits of YFe2O4 with different oxygen deficiency were determined at various temperatures.