(111) Monocrystalline Nickel Films

1972 ◽  
Vol 30 ◽  
pp. 512-513
Author(s):  
T.E. Pratt ◽  
R.W. Vook
Keyword(s):  
Film Thickness ◽  
Deposition Rate ◽  
Room Temperature ◽  
Narrow Range ◽  
High Vacuum ◽  
Residual Pressure ◽  
Temperature Dependent ◽  
Deposition Parameters ◽  
Transmission Electron ◽  
Substrate Temperatures

(111) oriented thin monocrystalline Ni films have been prepared by vacuum evaporation and examined by transmission electron microscopy and electron diffraction. In high vacuum, at room temperature, a layer of NaCl was first evaporated onto a freshly air-cleaved muscovite substrate clamped to a copper block with attached heater and thermocouple. Then, at various substrate temperatures, with other parameters held within a narrow range, Ni was evaporated from a tungsten filament. It had been shown previously that similar procedures would yield monocrystalline films of CU, Ag, and Au.For the films examined with respect to temperature dependent effects, typical deposition parameters were: Ni film thickness, 500-800 A; Ni deposition rate, 10 A/sec.; residual pressure, 10-6 torr; NaCl film thickness, 250 A; and NaCl deposition rate, 10 A/sec. Some additional evaporations involved higher deposition rates and lower film thicknesses.Monocrystalline films were obtained with substrate temperatures above 500° C. Below 450° C, the films were polycrystalline with a strong (111) preferred orientation.