Growth stress in SiO2 during oxidation of SiC fibers

2012 ◽  
Vol 111 (6) ◽  
pp. 063527 ◽  
Author(s):  
R. S. Hay
Keyword(s):  
Growth Stress ◽  
Sic Fibers

TEM characterization of reaction zone in a SiC fiber-reinforced titanium alloy

1988 ◽  
Vol 46 ◽  
pp. 738-739
Author(s):  
G. Das ◽  
R. E. Omlor
Keyword(s):  
Titanium Alloys ◽  
Reaction Zone ◽  
Carbon Layer ◽  
Fiber Reinforced ◽  
Reaction Products ◽  
Sic Fibers ◽  
Sic Fiber ◽  
The Matrix ◽  
Immense Potential

Fiber reinforced titanium alloys hold immense potential for applications in the aerospace industry. However, chemical reaction between the fibers and the titanium alloys at fabrication temperatures leads to the formation of brittle reaction products which limits their development. In the present study, coated SiC fibers have been used to evaluate the effects of surface coating on the reaction zone in the SiC/IMI829 system.IMI829 (Ti-5.5A1-3.5Sn-3.0Zr-0.3Mo-1Nb-0.3Si), a near alpha alloy, in the form of PREP powder (-35 mesh), was used a茸 the matrix. CVD grown AVCO SCS-6 SiC fibers were used as discontinuous reinforcements. These fibers of 142μm diameter contained an overlayer with high Si/C ratio on top of an amorphous carbon layer, the thickness of the coating being ∽ 1μm. SCS-6 fibers, broken into ∽ 2mm lengths, were mixed with IMI829 powder (representing < 0.1vol%) and the mixture was consolidated by HIP'ing at 871°C/0. 28GPa/4h.

Growth stress and interdiffusion analysis of NiCoCrAlYTa coating during oxidation

2020 ◽  
pp. 1-10
Author(s):  
Hongzhi Yang ◽  
Jianpeng Zou ◽  
Qian Shi ◽  
Zhongzhan Xu ◽  
Mingjiang Dai ◽  
...  
Keyword(s):  
Growth Stress

Microstructural, strength, and creep characterization of Sylramic™, Sylramic™-iBN and super Sylramic™-iBN SiC fibers

2021 ◽  
Vol 41 (9) ◽  
pp. 4697-4709
Author(s):  
R.T. Bhatt ◽  
F. Sola’ ◽  
L.J. Evans ◽  
R.B Rogers ◽  
D.F. Johnson
Keyword(s):  
Sic Fibers

scholarly journals Effects of SiC Fibers and Laminated Structure on Mechanical Properties of Ti–Al Laminated Composites

Materials ◽  
2021 ◽  
Vol 14 (6) ◽  
pp. 1323
Author(s):  
Chenyang Hou ◽  
Shouyin Zhang ◽  
Zhijian Ma ◽  
Baiping Lu ◽  
Zhenjun Wang
Keyword(s):  
Volume Fraction ◽  
Raw Materials ◽  
Laminated Composites ◽  
Intermetallic Layer ◽  
Longitudinal Direction ◽  
Fracture Mechanisms ◽  
Compact Structure ◽  
Laminated Structure ◽  
Sic Fibers ◽  
Sic Fiber

Ti/Ti–Al and SiCf-reinforced Ti/Ti–Al laminated composites were fabricated through vacuum hot-pressure using pure Ti foils, pure Al foils and SiC fibers as raw materials. The effects of SiC fiber and a laminated structure on the properties of Ti–Al laminated composites were studied. A novel method of fiber weaving was implemented to arrange the SiC fibers, which can guarantee the equal spacing of the fibers without introducing other elements. Results showed that with a higher exerted pressure, a more compact structure with fewer Kirkendall holes can be obtained in SiCf-reinforced Ti/Ti–Al laminated composites. The tensile strength along the longitudinal direction of fibers was about 400 ± 10 MPa, which was 60% higher compared with the fabricated Ti/Ti–Al laminated composites with the same volume fraction (60%) of the Ti layer. An in situ tensile test was adopted to observe the deformation behavior and fracture mechanisms of the SiCf-reinforced Ti/Ti–Al laminated composites. Results showed that microcracks first occurred in the Ti–Al intermetallic layer.

scholarly journals Effects of Roughness on Stresses in an Oxide Scale Formed on a Superalloy Substrate

Coatings ◽  
2021 ◽  
Vol 11 (4) ◽  
pp. 479
Author(s):  
Yang Zhao ◽  
Fan Sun ◽  
Peng Jiang ◽  
Yongle Sun
Keyword(s):  
Residual Stress ◽  
Surface Roughness ◽  
Residual Stresses ◽  
Oxide Scale ◽  
Rough Surface ◽  
Alumina Scale ◽  
Growth Stress ◽  
Oxide Growth ◽  
Substrate Thickness ◽  
Roughness Effect

The effects of surface roughness on the stresses in an alumina scale formed on a Fecralloy substrate are investigated. Spherical indenters were used to create indents with different radii and depths to represent surface roughness and then the roughness effect was studied comprehensively. It was found that the residual stresses in the alumina scale formed around the rough surface are almost constant and they are dominated by the curvature rather than the depth of the roughness. Oxidation changes the surface roughness. The edge of the indent was sharpened after oxidation and the residual stress there was released presumably due to cracking. The residual stresses in the alumina scale decrease with increase in oxidation time, while the substrate thickness has little effect, given that the substrate is thicker than the alumina scale. Furthermore, the effect of roughness on the oxide growth stress is analysed. This work indicates that the surface roughness should be considered for evaluation of stresses in coatings.

scholarly journals Hybrid Triploid Induced by Megaspore Chromosome Doubling in Jujube (Ziziphus jujuba Mill.) ‘Maya’ and Its Characteristics

Forests ◽  
2021 ◽  
Vol 12 (2) ◽  
pp. 112
Author(s):  
Songshan Liu ◽  
Chenxing Zhang ◽  
Weicong Yang ◽  
Xiang Li ◽  
Lu Hou ◽  
...  
Keyword(s):  
Chromosome Doubling ◽  
Colchicine Treatment ◽  
Fruit Trees ◽  
Growth Stress ◽  
Optimal Timing ◽  
Photosynthetic Parameters ◽  
Flower Bud ◽  
Treatment Methods ◽  
Triploid Individual ◽  
Colchicine Solution

Polyploid breeding is an important strategy for tree improvement because polyploid individuals typically show superior traits, such as improved growth, stress resistance, and superior fruit quality. Artificial induction of chromosome doubling of female gametes is an effective approach to obtain triploid progeny. However, no triploid fruit tree cultivars have been developed using this approach. The objective of this study was to explore the utility of chromosome doubling in female gametes of ‘Maya’ jujube to produce triploid individuals. The temporal relationship between flower bud morphology and the megaspore meiotic stage was studied to guide the optimal timing of colchicine treatment. Colchicine solution was applied to bearing shoots of mature ‘Maya’ jujube trees in a field experiment using two treatment methods (improved cotton leaching and injection method) and three concentrations (0.3%, 0.4%, and 0.5%). The water transport rate of ‘Maya’ jujube shoots was studied using dye solution to judge the effectiveness and timing of the colchicine treatment methods. Two triploids were identified among the progenies from the colchicine-treated shoots. The highest efficiency of triploid production was 3.3% when flower buds of diameter 1.76–2.12 mm were treated with 0.3% colchicine solution for 4 h using an improved cotton leaching method. The ground diameter, plant thorn length, leaf width, leaf area, stomatal length, stomatal width, chlorophyll content, and photosynthetic parameters of one triploid individual were significantly higher than those of diploids of identical parentage at 18 months old. Thus, induction of 2n megaspores is an effective approach to generate triploid jujube. These results are expected to promote and accelerate triploid breeding in fruit trees.

Processing, characterization and properties of novel gradient Si3N4/SiC fibers derived from polycarbosilanes

2019 ◽  
Vol 39 (13) ◽  
pp. 3613-3619 ◽  
Author(s):  
Xichao Dong ◽  
Changqing Guo ◽  
Xingyu Liu ◽  
Chong Gu ◽  
Pengfei Wu ◽  
...  
Keyword(s):  
Sic Fibers