ABSTRACTAn analysis of the Fowler-Nordheim tunneling (FNT) theory and its application to temperature dependent current-voltage characteristics, of very thin films of SiO2 on silicon, is presented. The final results are believed to provide the most complete examination of FN emission theory and predict the breakdown electric field in thin SiO2 films. The role of the roughness, at the Si-SiO2 interface, in determining the FNT current in these structures is also discussed.
ABSTRACTThe (100), (111) and randomly oriented PZT thin films were fabricated on Pt/Ti/Coming 7059 glass using sol-gel method. The thin films having different orientation were fabricated by different drying conditions for pyrolysis. The preferred orientations of the PZT thin films were observed using XRD, rocking curves, and pole figures. The microstructures were investigated using SEM. The hysteresis loops and capacitance-voltage characteristics of the films were investigated using a standardized ferroelectric test system. The dielectric constant and current-voltage characteristics of the films were investigated using an impedance analyzer and pA meter, respectively. The films oriented in a particular direction showed superior electrical characteristics to the randomly oriented films.
The photoconductivity of a nanocomposite MEH-PPV:TiO2 thin film is investigated. The nanocomposite MEH-PPV:TiO2 thin film was deposited on a glass substrate by spin coating technique. The composition of the TiO2 powder was varied from 5 wt% to 20 wt% (with 5 wt% interval). The concentration of the MEH-PPV is given by 1 mg/1 ml. The current voltage characteristics were measured in dark and under illumination. The photoconductivity showed increment in value as the composition of the TiO2 is raised in the polymer based solution. The absorption showed augmentation as the amount of TiO2 is increased. The escalation of the current voltage is then supported by the results of surface morphology.
A study of forward current-voltage characteristics of Ni/4H-SiC Schottky diodes (SDs) before and after irradiation with He+ ions revealed features that characterize defect structures and reveal the degradation mechanism of the diodes. These features are the presence of excess currents of certain type in the unirradiated SDs, their appearance in forward-biased originally ideal SDs, and a >10 orders of magnitude scatter of the series resistance of the SDs upon their irradiation with He+ ions. A model of localized defect-induced current paths (shunts) in the form of unintentionally produced SDs with the substrate is suggested.
La-doped bismuth titanate (Bi4-xLaxTi3O12: BLT) and pure Bi4Ti3O12 (BIT) thin films with random orientation were fabricated on Pt/Ti/SiO2/Si substrates by rf magnetron sputtering technique. These samples had polycrystalline Bi-layered perovskite structure without preferred orientation, and consisted of well developed rod-like grains with random orientation. For the samples with x=0.25 and 1.0 the current-voltage characteristics exhibited negative differential resistance behaviors and their P-V hysteresis loops were characterized by large leakage current, whereas for the samples with x=0.5 and 0.75 the current-voltage characteristics showed simple ohmic behaviors and their P-V hysteresis loops were the saturated and undistorted hysteresis loops. The remanent polarization ( Pr ) and coercive field (Ec) of the BLT ceramic with x=0.75 were above 20μC/cm2 and 85KV/cm , respectively.
Abstract
Carrier transport properties of ferroelectric Hf0.5Zr0.5O2 (HZO) thin films have been investigated on metal-ferroelectric-metal (MFM) capacitor in the first current flow of ferroelectric poling treatment. In current–voltage (I–V) measurement of MFM capacitor, a kink or discontinuity point of derivative in I–V characteristic appears, and after the cyclic voltage sweep this kink disappears. This phenomenon is different from the ferroelectric instabilities after several thousand or million voltage cycle applies reported as the wake-up and fatigue. From the analysis using Poole-Frenkel plot of I–V characteristics, it is suggested that irreversible trap generation by electric field apply occurs in poling treatment.
ABSTRACTElectric field – induced effects are studied in thin films of amorphous Si grown by magnetron sputtering performed in continuous and pulse modes. Current-voltage characteristics are measured under the room temperature in different spectral ranges. It is shown that the investigated dependencies are of exponential character in all range of applied bias. Good photosensitivity was revealed by the samples prepared in continuous mode in the near-IR and visible interval. The samples grown by the pulse magnetron technology were shown room-temperature photosensitivity in near-IR range after 2000C hydrogenation.
Overall current-voltage characteristics of space charge controlled currents for thin films by a single carrier species