Room temperature homogeneous flow in a bulk metallic glass with low glass transition temperature

2011 ◽  
Vol 98 (14) ◽  
pp. 141913 ◽  
Author(s):  
K. Zhao ◽  
X. X. Xia ◽  
H. Y. Bai ◽  
D. Q. Zhao ◽  
W. H. Wang
Keyword(s):  
Glass Transition ◽  
Transition Temperature ◽  
Glass Transition Temperature ◽  
Metallic Glass ◽  
Bulk Metallic Glass ◽  
Room Temperature ◽  
Homogeneous Flow

scholarly journals Effects of Annealing on Enthalpy Recovery and Nanomechanical Behaviors of a La-Based Bulk Metallic Glass

Metals ◽  
2021 ◽  
Vol 11 (4) ◽  
pp. 579
Author(s):  
Ting Shi ◽  
Lanping Huang ◽  
Song Li
Keyword(s):  
Glass Transition ◽  
Transition Temperature ◽  
Glass Transition Temperature ◽  
Metallic Glass ◽  
Bulk Metallic Glass ◽  
Structural Relaxation ◽  
Supercooled Liquid ◽  
Supercooled Liquid Region ◽  
Liquid Region ◽  
Nanoindentation Measurement

Structural relaxation and nanomechanical behaviors of La65Al14Ni5Co5Cu9.2Ag1.8 bulk metallic glass (BMG) with a low glass transition temperature during annealing have been investigated by calorimetry and nanoindentation measurement. The enthalpy release of this metallic glass is deduced by annealing near glass transition. When annealed below glass transition temperature for 5 min, the recovered enthalpy increases with annealing temperature and reaches the maximum value at 403 K. After annealed in supercooled liquid region, the recovered enthalpy obviously decreases. For a given annealing at 393 K, the relaxation behaviors of La-based BMG can be well described by the Kohlrausch-Williams-Watts (KWW) function. The hardness, Young’s modulus, and serrated flow are sensitive to structural relaxation of this metallic glass, which can be well explained by the theory of solid-like region and liquid-like region. The decrease of ductility and the enhancement of homogeneity can be ascribed to the transformation from liquid-like region into solid-like region and the reduction of the shear transition zone (STZ).

scholarly journals Stability of ZrTiCuNiBe Bulk Metallic Glass upon Isothermal Annealing Near the Glass Transition Temperature

2002 ◽  
Vol 17 (6) ◽  
pp. 1385-1389 ◽  
Author(s):  
Wei Hua Wang ◽  
Ru Ju Wang ◽  
W. T. Yang ◽  
B. C. Wei ◽  
P. Wen ◽  
...  
Keyword(s):  
Glass Transition ◽  
Transition Temperature ◽  
Glass Transition Temperature ◽  
Metallic Glass ◽  
Bulk Metallic Glass ◽  
Isothermal Annealing ◽  
Scanning Calorimetry ◽  
The Stability ◽  
Property Changes ◽  
Overlap Method

The stability of Zr41Ti14Cu12.5Ni10Be22.5 bulk metallic glass (BMG) upon isothermal annealing near the glass transition temperature has been investigated by using x-ray diffraction, differential scanning calorimetry, and the pulse echo overlap method. The density, elastic constants, and thermodynamic parameters as well as their annealing time dependence have been determined. The microstructural and properties changes of the annealed BMG were checked by acoustic measurement. Obvious structural and property changes were observed with prolonged annealing of the BMG near the glass transition temperature.

scholarly journals Structural Features of the Extraordinary Low Glass Transition Temperature for Au65Cu18Si17 Bulk Metallic Glass

2013 ◽  
Vol 54 (8) ◽  
pp. 1351-1355 ◽  
Author(s):  
Makoto Matsuura ◽  
Wei Zhang ◽  
Shinichi Yamaura ◽  
Takashi Fujita ◽  
Koji Ohara ◽  
...  
Keyword(s):  
Glass Transition ◽  
Transition Temperature ◽  
Glass Transition Temperature ◽  
Metallic Glass ◽  
Bulk Metallic Glass ◽  
Structural Features

Influence of Structural Relaxation on Compressive Plasticity of Zr64.13Cu15.75Ni10.12Al10 Bulk Metallic Glass

2014 ◽  
Vol 910 ◽  
pp. 48-52 ◽  
Author(s):  
Jian Sheng Gu ◽  
Hui Feng Bo
Keyword(s):  
Differential Scanning Calorimetry ◽  
Glass Transition ◽  
Transition Temperature ◽  
Glass Transition Temperature ◽  
Metallic Glass ◽  
Bulk Metallic Glass ◽  
Free Volume ◽  
Structural Relaxation ◽  
Isothermal Annealing ◽  
Scanning Calorimetry

Structural relaxation through isothermal annealing below the glass transition temperature was conducted on a Zr64.13Cu15.75Ni10.12Al10bulk metallic glass. Differential scanning calorimetry was used to quantify enthalpy differences between the as-cast and relaxed samples, which were then related to average free volume differences. The influence of structural relaxation on plasticity was examined. While the free volume decreasement can be clearly observed between the as-cast and relaxed samples, structural relaxation is not accompanied by severe embrittlement.