Polystyrene (PS) spheres encapsulated core-shell composites of SiO2or TiO2nanoparticles were prepared by the spray drying technique and hollow spheres of SiO2or TiO2nanoparticles were then derived by removing the PS cores with calcinations. The PS spheres were dispersed into the SiO2or TiO2colloids, forming a suspension and then the suspensions were sprayed to form micrometer-sized droplets, as the droplets rush through the drying chamber, the PS spheres were encapsulated into the core of SiO2or TiO2particles due to the high temperatures and the instant evaporation, obtaining PS@SiO2, PS@TiO2or PS@SiO2/TiO2core-shell composites. After removing the PS core by calcination at 550°C, SiO2or TiO2hollow spheres were then derived. The influence of drying temperature, the concentration of the SiO2or TiO2particles and the ratio of PS sphere to the particles on the structures and specific surface area of the hollow spheres were studied with scanning electron microscopy (SEM) and nitrogen adsorption-desorption measurements.