Retrieving the Constitutive Parameters of MetalBacked Radar Absorbing Material by Phase Unwrapping Method

2018 ◽  
Author(s):  
Bin Fu ◽  
Xin Ma ◽  
Guobin Wan
Keyword(s):  
Phase Unwrapping ◽  
Radar Absorbing Material ◽  
Absorbing Material ◽  
Constitutive Parameters

Development of Electroless Ni-P/NRAM Nanocomposite Powder with Enhanced Microwave Absorption Properties

2009 ◽  
Vol 67 ◽  
pp. 59-64 ◽  
Author(s):  
Rahul Sharma ◽  
Ramesh Chandra Agarwala ◽  
Vijaya Agarwala
Keyword(s):  
Electron Microscope ◽  
Microwave Absorption ◽  
Radiation Power ◽  
Nanocomposite Powder ◽  
Absorption Properties ◽  
Microwave Absorption Properties ◽  
Radar Absorbing Material ◽  
Transmission Electron ◽  
Absorbing Material ◽  
Nanocomposite Powders

Nano radar absorbing material (NRAM) i.e. BaMe2Fe16O27 (Me2+=Fe2+) powder (10 nm) is coated with amorphous Ni-P nano layer (5-10 nm) by using electroless (EL) technology to develop EL Ni-P/NRAM nanocomposite powder. The experimental processes parameters and EL Ni-P bath composition were optimized to obtain the deposition. As-deposited nanocomposite powder was microwave annealed (MWA) with increasing radiation power from 160 to 760 watts for 5 minutes. The surface morphology, elemental contents, phase transformation and magnetic properties of NRAM powders were examined under field emission scanning electron microscope (FESEM), transmission electron microscope (TEM), X-ray diffraction (XRD) and vibrating sample magnetometer (VSM) respectively. Maximum reflection loss (RL) 33.75 dB at 15.80 GHz for nanocomposite powder MWA at 760 watt was obtained the absorption range under −15 dB is from 13.76 to 16.77 GHz with 2 mm thickness layer in Ku Band. Excellent microwave absorption properties due to accurate electromagnetic (EM) match in the nanocomposite microstructure, a strong natural resonance and multipolarization. Such (Ni+ Ni3P)/NRAM nanocomposite powders may be attractive candidates for EM absorption.

scholarly journals Iron oxide/titania composites for radar absorbing material (RAM) applications

Cerâmica ◽  
2019 ◽  
Vol 65 (375) ◽  
pp. 470-476 ◽  
Author(s):  
A. Fisli ◽  
D. S. Winatapura ◽  
E. Sukirman ◽  
S. Mustofa ◽  
W. A. Adi ◽  
...  
Keyword(s):  
Iron Oxide ◽  
Pore Volume ◽  
Weight Ratio ◽  
Total Pore Volume ◽  
Precipitation Method ◽  
Oxide Content ◽  
Iron Oxide Content ◽  
Radar Absorbing Material ◽  
Radar Signature ◽  
Absorbing Material

Abstract Iron oxide/titania composites were synthesized by precipitation method. Amount of iron oxide was varied in the composites. The single phase (anatase) was obtained for the weight ratio of 0-20% and three phases (anatase, magnetite and hematite) were found for the weight ratio of 30% and 40% of iron oxide. The crystallite size of titania decreased with increasing of iron oxide content. The specific surface area, total pore volume and BJH pore volume of the sample increased with increasing iron oxide content in the composite. The composites possessed mesoporous characteristic (6.5-9.6 nm in pore diameter) and exhibited ferromagnetic properties. The measurement of the microwave absorption showed that the 40Fe/Ti composite had the best reflection loss of -14 dB at a frequency of 10.9 GHz. This meant that the electromagnetic wave was absorbed 80% in that frequency. Thus, the developed material can be a promising microwave absorbing agent in radar signature reduction.

Radar Absorbing Materials Based on Metamaterials

2010 ◽  
Vol 75 ◽  
pp. 215-223
Author(s):  
Andrey Nikolayevich Lagarkov ◽  
Vladimir Nikolayevich Kisel ◽  
Vladimir Nikolayevich Semenenko
Keyword(s):  
Electromagnetic Wave ◽  
Reflection Coefficient ◽  
Frequency Band ◽  
Radar Absorbing Material ◽  
Wide Range ◽  
Absorbing Materials ◽  
Different Types ◽  
Absorbing Material ◽  
Wave Incidence

The use of metamaterial for design of radar absorbing material (RAM) is discussed. The typical features of the frequency dependencies of , , ,  of composites manufactured of different types of resonant inclusions are given as an example. The RAM characteristics obtained by the use of the composites are given. It is shown that it is possible to use for RAM design the metamaterials with both the positive values of ,  and negative ones. Making use of the frequency band with negative  and  it is possible to create a RAM with low reflection coefficient in a wide range of the angles of electromagnetic wave incidence.