scholarly journals Detecting and identifying reversible changes in perovskite solar cells by electrochemical impedance spectroscopy

RSC Advances ◽  
2019 ◽  
Vol 9 (57) ◽  
pp. 33436-33445 ◽  
Author(s):  
Dino Klotz ◽  
Ganbaatar Tumen-Ulzii ◽  
Chuanjiang Qin ◽  
Toshinori Matsushima ◽  
Chihaya Adachi
Keyword(s):  
Solar Cells ◽  
Electrochemical Impedance Spectroscopy ◽  
Impedance Spectroscopy ◽  
Electrochemical Impedance ◽  
Perovskite Solar Cells

Reversible changes in perovskite solar cells (PSC) are detected and analysed by electrochemical impedance spectroscopy (EIS).

scholarly journals Electrochemical Impedance Spectroscopy Analysis of Hole Transporting Material Free Mesoporous and Planar Perovskite Solar Cells

Nanomaterials ◽  
2020 ◽  
Vol 10 (9) ◽  
pp. 1635
Author(s):  
Sumayya M. Abdulrahim ◽  
Zubair Ahmad ◽  
Jolly Bahadra ◽  
Noora J. Al-Thani
Keyword(s):  
Solar Cells ◽  
Electrochemical Impedance Spectroscopy ◽  
Impedance Spectroscopy ◽  
Electrochemical Impedance ◽  
Perovskite Solar Cells ◽  
Cost Effective ◽  
Hole Transport ◽  
Large Area ◽  
The Future ◽  
Hole Transporting Material

The future photovoltaic technologies based on perovskite materials are aimed to build low tech, truly economical, easily fabricated, broadly deployable, and trustworthy solar cells. Hole transport material (HTM) free perovskite solar cells (PSCs) are among the most likely architectures which hold a distinctive design and provide a simple way to produce large-area and cost-effective manufacture of PSCs. Notably, in the monolithic scheme of the HTM-free PSCs, all layers can be printed using highly reproducible and morphology-controlled methods, and this design has successfully been demonstrated for industrial-scale fabrication. In this review article, we comprehensively describe the recent advancements in the different types of mesoporous (nanostructured) and planar HTM-free PSCs. In addition, the effect of various nanostructures and mesoporous layers on their performance is discussed using the electrochemical impedance spectroscopy (EIS) technique. We bring together the different perspectives that researchers have developed to interpret and analyze the EIS data of the HTM-free PSCs. Their analysis using the EIS tool, the limitations of these studies, and the future work directions to overcome these limitations to enhance the performance of HTM-free PSCs are comprehensively considered.

scholarly journals Long-Term Stability Analysis of 3D and 2D/3D Hybrid Perovskite Solar Cells Using Electrochemical Impedance Spectroscopy

Molecules ◽  
2020 ◽  
Vol 25 (24) ◽  
pp. 5794
Author(s):  
Sumayya M. Abdulrahim ◽  
Zubair Ahmad ◽  
Jolly Bhadra ◽  
Noora Jabor Al-Thani
Keyword(s):  
Solar Cells ◽  
Electrochemical Impedance Spectroscopy ◽  
Impedance Spectroscopy ◽  
Electrochemical Impedance ◽  
Perovskite Solar Cells ◽  
Layer By Layer ◽  
Term Stability ◽  
Long Term Stability ◽  
The Stability

Despite the remarkable progress in perovskite solar cells (PSCs), their instability and rapid degradation over time still restrict their commercialization. A 2D capping layer has been proved to overcome the stability issues; however, an in-depth understanding of the complex degradation processes over a prolonged time at PSC interfaces is crucial for improving their stability. In the current work, we investigated the stability of a triple cation 3D ([(FA0.83MA0.17)Cs0.05]Pb(I0.83Br0.17)3) and 2D/3D PSC fabricated by a layer-by-layer deposition technique (PEAI-based 2D layer over triple cation 3D perovskite) using a state-of-art characterization technique: electrochemical impedance spectroscopy (EIS). A long-term stability test over 24 months was performed on the 3D and 2D/3D PSCs with an initial PCE of 18.87% and 20.21%, respectively, to suggest a more practical scenario. The current-voltage (J-V) and EIS results showed degradation in both the solar cell types; however, a slower degradation rate was observed in 2D/3D PSCs. Finally, the quantitative analysis of the key EIS parameters affected by the degradation in 3D and 2D/3D PSCs were discussed.

Analysis of Charge Transport and Recombination Studied by Electrochemical Impedance Spectroscopy for Dye-sensitized Solar Cells With Atomic Layer Deposited Metal Oxide Treatment on TiO2 Surface

2010 ◽  
Vol 1270 ◽  
Author(s):  
Braden Bills ◽  
Mariyappan Shanmugam ◽  
Mahdi Farrokh Baroughi ◽  
David Galipeau
Keyword(s):  
Solar Cells ◽  
Electrochemical Impedance Spectroscopy ◽  
Impedance Spectroscopy ◽  
Electrochemical Impedance ◽  
Photovoltaic Performance ◽  
Dye Sensitized Solar Cells ◽  
Atomic Layer ◽  
Back Reaction ◽  
Dye Sensitized ◽  
Sensitized Solar Cells

AbstractThe performance of dye-sensitized solar cells (DSSCs) is limited by the back-reaction of photogenerated electrons from the porous titanium oxide (TiO2) nanoparticles back into the electrolyte solution, which occurs almost exclusively through the interface. This and the fact that DSSCs have a very large interfacial area makes their performance greatly dependant on the density and activity of TiO2 surface states. Thus, effectively engineering the TiO2/dye/electrolyte interface to reduce carrier losses is critically important for improving the photovoltaic performance of the solar cell. Atomic layer deposition (ALD), which uses high purity gas precursors that can rapidly diffuse through the porous network, was used to grow a conformal and controllable aluminum oxide (Al2O3) and hafnium oxide (HfO2) ultra thin layer on the TiO2 surface. The effects of this interfacial treatment on the DSSC performance was studied with dark and illuminated current-voltage and electrochemical impedance spectroscopy (EIS) measurements.

scholarly journals Investigation of Temperature and Aging Effects in Nanostructured Dye Solar Cells Studied by Electrochemical Impedance Spectroscopy

2009 ◽  
Vol 2009 ◽  
pp. 1-15 ◽  
Author(s):  
Minna Toivola ◽  
Janne Halme ◽  
Lauri Peltokorpi ◽  
Peter Lund
Keyword(s):  
Solar Cells ◽  
Electrochemical Impedance Spectroscopy ◽  
Impedance Spectroscopy ◽  
Electrochemical Impedance ◽  
Charge Transfer Resistance ◽  
Aging Effects ◽  
Transfer Resistance ◽  
Deterioration Rate ◽  
Dye Solar Cells ◽  
Effects Of Aging

Effects of aging and cyclically varying temperature on the electrical parameters of dye solar cells were analyzed with electrochemical impedance spectroscopy. Photoelectrode total resistance increased as a function of time due to increasing electron transport resistance in theTiO2film. On the other hand, photoelectrode recombination resistance was generally larger, electron lifetimes in theTiO2were film longer, and charge transfer resistance on the counter electrode was smaller after the temperature treatments than before them. These effects correlated with the slower deterioration rate of the temperature-treated cells, in comparison to the reference cells.

Sign in / Sign up

Export Citation Format

Share Document