scholarly journals Synthesis and retarder mechanism study of a novel amphoteric composite high temperature-resistant retarder for oil well cement

RSC Advances ◽  
2018 ◽  
Vol 8 (27) ◽  
pp. 14812-14822 ◽  
Author(s):  
Peng Zhigang ◽  
Zhang Jian ◽  
Feng Qian ◽  
Zou Changjun ◽  
Zheng Yong ◽  
...  
Keyword(s):  
High Temperature ◽  
Oil Well ◽  
Composite Polymer ◽  
Mechanism Study ◽  
Modified Montmorillonite ◽  
Oil Well Cement ◽  
Cement Retarder ◽  
Well Cement ◽  
Polymerization Method

An amphoteric composite polymer (hereinafter referred to as PAADM) as high temperature-resistant cement retarder was prepared byin situintercalated polymerization method with AMPS, AA and DMDAAC as monomers, and modified montmorillonite as an active polymerization filler.

Development of Functional Polymer as Oil-Well Cement Retarder

2015 ◽  
Vol 814 ◽  
pp. 191-198 ◽  
Author(s):  
Xiu Jian Xia ◽  
Jin Tang Guo ◽  
Shuo Qiong Liu ◽  
Jian Zhou Jin ◽  
Yong Jin Yu ◽  
...  
Keyword(s):  
High Temperature ◽  
Ultrasonic Method ◽  
Strength Development ◽  
Cement Stone ◽  
Oil Well ◽  
Cement Slurry ◽  
Oil Well Cement ◽  
Cement Retarder ◽  
The Stability ◽  
Well Cement

In this study, a novel polymer retarder DRH-200LG was synthesized to solve the problems of retarding failure, strong dispersivity under high temperature and adverse impact on the strength development of cement stone. The composition of the polymer was confirmed by IR, and its thermal stability was proved by DSC, TG analysis and thermal treatment at 200 °C. Furthermore, the stability and strength development of cement slurry was evaluated by the comparative consistency method and ultrasonic method, respectively. The results show that DRH-200LG has good high temperature-resistance and retarding performance, presenting favourable influence on the stability and strength development of cement slurry. DRH-200LG shows a good application prospect in the cementation of deep & ultra-deep wells. And it has some guiding significance in the research and innovation of a novel polymer used as oil well cement retarder.

Performance Evaluation of Polycarboxylic Acid Dispersant for Oil Well Cementing

2020 ◽  
Vol 993 ◽  
pp. 1341-1350
Author(s):  
Xiu Jian Xia ◽  
Yong Jin Yu ◽  
Jian Zhou Jin ◽  
Shuo Qiong Liu ◽  
Ming Xu ◽  
...  
Keyword(s):  
High Temperature ◽  
Salt Resistance ◽  
Strength Development ◽  
Fluid Loss ◽  
Oil Well ◽  
Polycarboxylic Acid ◽  
Cement Slurry ◽  
Deep Wells ◽  
Oil Well Cement ◽  
Well Cement

The conventional oil-well cement dispersant has the characteristics of poor dispersion at high temperature, poor compatibility with other additives, and environmental pollution during the production process. In this article, with ultra-early strong polyether monomer, acrylic acid, 2-acrylamine-2-methylpropyl sulfonic acid, sodium methacrylate as copolymer monomers, an environmentally friendly polycarboxylic acid dispersant, DRPC-1L, was prepared by the aqueous solution free-radical polymerization. The chemical composition and thermal stability of the synthetic copolymer were characterized by FTIR and TGA techniques. The evaluation results show that DRPC-1L has a wide temperature range (30~210 °C), good salt-resistance and dispersing effect. It can significantly improve the rheological performance of cement slurry, and it is well matched with oil-well cement additives such as fluid loss agent, retarder and so on. Moreover, it is beneficial to the mechanical strength development of set cement, especially the early compressive strength. It can also inhibit the abnormal gelation phenomenon of cement slurry, flash set, that occurs during high temperature thickening experiments, which plays an important role in enhancing the comprehensive performance of cement slurry. Consequently, the novel polycarboxylic acid dispersant has good application prospects in deep and ultra-deep wells cementing.

Sign in / Sign up

Export Citation Format

Share Document