Structural phase transitions in YPtGe2 and GdPtGe2

2018 ◽  
Vol 47 (17) ◽  
pp. 6075-6088 ◽  
Author(s):  
Oliver Janka ◽  
Rolf-Dieter Hoffmann ◽  
Birgit Heying ◽  
Rainer Pöttgen
Keyword(s):  
Phase Transitions ◽  
Single Crystal ◽  
Diffraction Data ◽  
Structural Phase ◽  
Structural Phase Transitions ◽  
X Ray Diffraction ◽  
Temperature Dependent ◽  
X Ray ◽  
Arc Melting

The germanides YPtGe2 and GdPtGe2 were synthesized from REGe2 precursor compounds and platinum by arc-melting and their structures were studied on the basis of temperature-dependent single crystal X-ray diffraction data.

Temperature-induced structural phase transitions in RERhSn (RE = Y, Gd-Tm, Lu)

2021 ◽  
Vol 0 (0) ◽  
Author(s):  
Simon Engelbert ◽  
Rolf-Dieter Hoffmann ◽  
Jutta Kösters ◽  
Steffen Klenner ◽  
Rainer Pöttgen
Keyword(s):  
Rare Earth ◽  
Phase Transitions ◽  
Driving Force ◽  
Room Temperature ◽  
Structural Phase ◽  
Structural Phase Transitions ◽  
Line Broadening ◽  
X Ray Diffraction ◽  
Temperature Dependent ◽  
X Ray

Abstract The structures of the equiatomic stannides RERhSn with the smaller rare earth elements Y, Gd-Tm and Lu were reinvestigated on the basis of temperature-dependent single crystal X-ray diffraction data. GdRhSn crystallizes with the aristotype ZrNiAl at 293 and 90 K. For RE = Y, Tb, Ho and Er the HP-CeRuSn type (approximant with space group R3m) is already formed at room temperature, while DyRhSn adopts the HP-CeRuSn type below 280 K. TmRhSn and LuRhSn show incommensurate modulated variants with superspace groups P31m(1/3; 1/3; γ) 000 (No. 157.1.23.1) (γ = 3/8 for TmRhSn and γ = 2/5 for LuRhSn). The driving force for superstructure formation (modulation) is a strengthening of Rh–Sn bonding. The modulation is expressed in a 119Sn Mössbauer spectrum of DyRhSn at 78 K through line broadening.

scholarly journals Studies of Optical, Dielectric, Ferroelectric, and Structural Phase Transitions in 0.9[KNbO3]-0.1 [BaNi1/2Nb1/2O3−δ]

Crystals ◽  
2021 ◽  
Vol 12 (1) ◽  
pp. 35
Author(s):  
Blanca Yamile Rosas ◽  
Alvaro A. Instan ◽  
Karuna Kara Mishra ◽  
S. Nagabhusan Achary ◽  
Ram S. Katiyar
Keyword(s):  
Phase Transitions ◽  
Room Temperature ◽  
Elevated Temperatures ◽  
Structural Phase ◽  
Cubic Phase ◽  
Structural Phase Transitions ◽  
X Ray Diffraction ◽  
Temperature Dependent ◽  
X Ray ◽  
Wide Range

The compound 0.9[KNbO3]-0.1[(BaNi1/2Nb1/2O3−δ] (KBNNO), a robust eco-friendly (lead-free) ferroelectric perovskite, has diverse applications in electronic and photonic devices. In this work, we report the dielectric, ferroelectric, and structural phase transitions behavior in the KBNNO compound using dielectric, X-ray diffraction, and Raman studies at ambient and as a function of temperature. Analyses of X-ray diffraction (XRD) data at room temperature (rtp) revealed the orthorhombic phase (sp. Gr. Amm2) of the compound with a minor secondary NiO cubic phase (sp. Gr. Fm3m). A direct optical band gap Eg of 1.66 eV was estimated at rtp from the UV–Vis reflectance spectrum analysis. Observation of non-saturated electric polarization loops were attributed to leakage current effects pertaining to oxygen vacancies in the compound. Magnetization studies showed ferromagnetism at room temperature (300 K) in this material. XRD studies on KBNNO at elevated temperatures revealed orthorhombic-to-tetragonal and tetragonal-to-cubic phase transitions at 523 and 713 K, respectively. Temperature-dependent dielectric response, being leaky, did not reveal any phase transition. Electrical conductivity data as a function of temperature obeyed Jonscher power law and satisfied the correlated barrier-hopping model, indicating dominance of the hopping conduction mechanism. Temperature-dependent Raman spectroscopic studies over a wide range of temperature (82–673 K) inferred the rhombohedral-to-orthorhombic and orthorhombic-to-tetragonal phase transitions at ~260, and 533 K, respectively. Several Raman bands were found to disappear, while a few Raman modes such as at 225, 270, 289, and 831 cm−1 exhibited discontinuity across the phase transitions at ~260 and 533 K.

Studies of U(C5H5)3Cl: I-Evidence for structural phase transitions below room temperature

1994 ◽  
Vol 209 (9) ◽  
Author(s):  
P. Raison ◽  
J. Rebizant ◽  
C. Apostolidis ◽  
G. H. Lander ◽  
A. Delapalme ◽  
...  
Keyword(s):  
Phase Transitions ◽  
Single Crystal ◽  
Organometallic Compound ◽  
Room Temperature ◽  
Structural Phase ◽  
Unit Cell ◽  
Structural Phase Transitions ◽  
X Ray Diffraction ◽  
X Ray

AbstractWe have used neutron and X-ray diffraction techniques on both single crystal and polycrystalline samples to examine the symmetry of the unit cell of the organometallic compound uranium tris(cyclopentadienyl)chlorine, U(C

Ternary Antimonides RE4T7Sb6 (RE=Gd–Lu; T =Ru, Rh) with Cubic U4Re7Si6-type Structure

2013 ◽  
Vol 68 (9) ◽  
pp. 971-978 ◽  
Author(s):  
Inga Schellenberg ◽  
Ute Ch. Rodewald ◽  
Christian Schwickert ◽  
Matthias Eul ◽  
Rainer Pöttgen
Keyword(s):  
Magnetic Susceptibility ◽  
Single Crystal ◽  
Magnetic Moment ◽  
Induction Furnace ◽  
X Ray Diffraction ◽  
Temperature Dependent ◽  
X Ray ◽  
Antiferromagnetic Ordering ◽  
Arc Melting ◽  
Intermediate Valent

The ternary antimonides RE4T7Sb6 (RE=Gd-Lu; T =Ru, Rh) have been synthesized from the elements by arc-melting and subsequent annealing in an induction furnace. The samples have been characterized by powder X-ray diffraction. Four structures were refined on the basis of single-crystal X-ray diffractometer data: U4Re7Si6 type, space group Im3m with a=862.9(2) pm, wR2=0.0296, 163 F2 values for Er4Ru7Sb6; a=864.1(1) pm, wR2=0.1423, 153 F2 values for Yb4Ru7Sb6; a=872.0(2) pm, wR2=0.0427, 172 F2 values for Tb4Rh7Sb6; and a=868.0(2) pm, wR2=0.0529, 154 F2 values for Er4Rh7Sb6, with 10 variables per refinement. The structures have T1@Sb6 octahedra and slightly distorted RE@T26Sb6 cuboctahedra as building units. The distorted cuboctahedra are condensed via all trapezoidal faces, and this network leaves octahedral voids for the T1 atoms. The ruthenium-based series of compounds was studied by temperature-dependent magnetic susceptibility measurements. Lu4Ru7Sb6 is Pauli-paramagnetic. The antimonides RE4Ru7Sb6 with RE=Dy, Ho, Er, and Tm show Curie-Weiss paramagnetism. Antiferromagnetic ordering occurs at 10.0(5), 5.1(5) and 4.0(5) K for Dy4Ru7Sb6, Ho4Ru7Sb6 and Er4Ru7Sb6, respectively, while Tm4Ru7Sb6 remains paramagnetic. Yb4Ru7Sb6 is an intermediate-valent compound with a reduced magnetic moment of 3.71(1) μB per Yb as compared to 4.54 μB for a free Yb3+ ion