Enhancing oxygen reduction reaction durability via coating graphene layers on iron-nitrogen supported carbon nanotubes

RSC Advances ◽  
2016 ◽  
Vol 6 (77) ◽  
pp. 73581-73588 ◽  
Author(s):  
Cai-Di Liu ◽  
Guang-Lan Li ◽  
Guang-Chun Cheng ◽  
Ce Hao ◽  
Si-Mei Chen ◽  
...  
Keyword(s):  
Carbon Nanotubes ◽  
Oxygen Reduction Reaction ◽  
Oxygen Reduction ◽  
Reduction Reaction ◽  
Graphene Layers

Fe-N-CNT@GN catalyst was designed through coating several graphene layers derived from the disodium edentate to enhance ORR durability.

scholarly journals Correction: Fast prediction of oxygen reduction reaction activity on carbon nanotubes with a localized geometric descriptor

2021 ◽  
Vol 23 (7) ◽  
pp. 4454-4454
Author(s):  
Kunran Yang ◽  
Jeremie Zaffran ◽  
Bo Yang
Keyword(s):  
Carbon Nanotubes ◽  
Oxygen Reduction Reaction ◽  
Oxygen Reduction ◽  
Chem Phys ◽  
Reduction Reaction ◽  
Oxygen Reduction Reaction Activity ◽  
Fast Prediction ◽  
Phys Chem Chem Phys

Correction for ‘Fast prediction of oxygen reduction reaction activity on carbon nanotubes with a localized geometric descriptor’ by Kunran Yang et al., Phys. Chem. Chem. Phys., 2020, 22, 890–895, DOI: 10.1039/C9CP04885E.

Fe/Fe 3 C Nanoparticles Confined in Graphitic Layers/Carbon Nanotubes as Efficient Oxygen Reduction Reaction Catalysts

2019 ◽  
Vol 4 (36) ◽  
pp. 10863-10867
Author(s):  
Yanping Huang ◽  
Weifang Liu ◽  
Shuting Kan ◽  
Penggao Liu ◽  
Hongtao Liu ◽  
...  
Keyword(s):  
Carbon Nanotubes ◽  
Oxygen Reduction Reaction ◽  
Oxygen Reduction ◽  
Reduction Reaction

scholarly journals Enhanced Electrocatalytic Activity and Stability toward the Oxygen Reduction Reaction with Unprotected Pt Nanoclusters

Nanomaterials ◽  
2018 ◽  
Vol 8 (11) ◽  
pp. 955 ◽  
Author(s):  
Jing Liu ◽  
Jiao Yin ◽  
Bo Feng ◽  
Tao Xu ◽  
Fu Wang
Keyword(s):  
Carbon Nanotubes ◽  
Oxygen Reduction Reaction ◽  
Oxygen Reduction ◽  
Specific Activity ◽  
Catalytic Performance ◽  
Reduction Reaction ◽  
Top Down ◽  
Methanol Tolerance ◽  
Pt Nanoclusters ◽  
Mass Activity

The Pt particles within diameters of 1–3 nm known as Pt nanoclusters (NCs) are widely considered to be satisfactory oxygen reduction reaction (ORR) catalysts due to higher electrocatalytic performance and cost effectiveness. However, the utilization of such smaller Pt NCs is always limited by the synthesis strategies, stability and methanol tolerance of Pt. Herein, unprotected Pt NCs (~2.2 nm) dispersed on carbon nanotubes (CNTs) were prepared via a modified top-down approach using liquid Li as a solvent to break down the bulk Pt. Compared with the commercial Pt/C, the resultant Pt NCs/CNTs catalyst (Pt loading: 10 wt.%) exhibited more desirable ORR catalytic performance in 0.1 M HClO4. The specific activity (SA) and mass activity (MA) at 0.9 V for ORR over Pt NCs/CNTs were 2.5 and 3.2 times higher than those over the commercial Pt/C (Pt loading: 20 wt.%). Meanwhile, the Pt NCs/CNTs catalyst demonstrated more satisfactory stability and methanol tolerance. Compared with the obvious loss (~69%) of commercial Pt/C, only a slight current decrease (~10%) was observed for Pt NCs/CNTs after the chronoamperometric measurement for 2 × 104 s. Hence, the as-prepared Pt NCs/CNTs material displays great potential as a practical ORR catalyst.

scholarly journals In situ synthesis of metal embedded nitrogen doped carbon nanotubes as an electrocatalyst for the oxygen reduction reaction with high activity and stability

RSC Advances ◽  
2018 ◽  
Vol 8 (44) ◽  
pp. 25051-25056 ◽  
Author(s):  
Yanhong Yin ◽  
Hengbo Zhang ◽  
Rongzhen Gao ◽  
Aili Wang ◽  
Xinxin Mao ◽  
...  
Keyword(s):  
Carbon Nanotubes ◽  
Carbon Nanotube ◽  
Oxygen Reduction Reaction ◽  
Oxygen Reduction ◽  
High Activity ◽  
Reduction Reaction ◽  
In Situ Synthesis ◽  
Nitrogen Doped ◽  
Nitrogen Doped Carbon

In this work, a Co–N doped carbon nanotube (CNT) catalyst was fabricated via a simple pyrolysis approach.

Sign in / Sign up

Export Citation Format

Share Document