Sol–gel-processed (001)-textured BiFeO3 thin films on Pt(111)/Ti/SiO2/Si substrates with PbO seeding nanocrystals

RSC Advances ◽  
2016 ◽  
Vol 6 (1) ◽  
pp. 489-494 ◽  
Author(s):  
Wei Sun ◽  
Zhen Zhou ◽  
Jing-Feng Li
Keyword(s):  
Thin Films ◽  
Sol Gel ◽  
Layer By Layer ◽  
Si Substrates ◽  
Bifeo3 Thin Films ◽  
Annealing Method

Highly (001)-oriented BiFeO3 thin films were grown on Pt(111)/Ti/SiO2/Si substrates with PbO seeding nanocrystals by a layer-by-layer annealing method.

Phase transition and piezoelectricity of sol–gel-processed Sm-doped BiFeO3 thin films on Pt(111)/Ti/SiO2/Si substrates

2015 ◽  
Vol 3 (9) ◽  
pp. 2115-2122 ◽  
Author(s):  
Wei Sun ◽  
Jing-Feng Li ◽  
Qi Yu ◽  
Li-Qian Cheng
Keyword(s):  
Thin Films ◽  
Phase Transition ◽  
Sol Gel ◽  
Orthorhombic Phase ◽  
High Quality ◽  
Si Substrates ◽  
Bifeo3 Thin Films ◽  
Gel Processing

We prepared high-quality Bi1−xSmxFeO3 films on Pt(111)/Ti/SiO2/Si substrates by sol–gel processing and found rhombohedral–orthorhombic phase transition with enhanced piezoelectricity.

scholarly journals Chemical Solution Deposition of BiFeO3 Films with Layer-by-Layer Control of the Coverage and Composition

Coatings ◽  
2020 ◽  
Vol 10 (5) ◽  
pp. 438 ◽  
Author(s):  
Alexander Abramov ◽  
Denis Alikin ◽  
Alexander Sobol ◽  
Dmitry Myakishev ◽  
Vladislav Slabov ◽  
...  
Keyword(s):  
Thin Films ◽  
Chemical Solution Deposition ◽  
Large Scale ◽  
Phase Distribution ◽  
Sol Gel ◽  
Piezoelectric Response ◽  
Layer By Layer ◽  
Chemical Solution ◽  
Solution Deposition ◽  
Bifeo3 Thin Films

Chemical solution deposition of BiFeO3 thin films is one of the most commercially available techniques to produce large-scale low-cost coatings for further application in memory devices. In this contribution, we implemented piezoresponse force and conductive atomic force microscopies to study the layer-by-layer sol-gel deposition of BiFeO3 thin films focusing on the local phase distribution, morphology, piezoelectric response, and leakage current. The final properties of resulting thin films are found to be determined not only by the composition of the gel and crystallization step but by the gelation step as well. The drying temperature and treatment duration of the solution are shown to drastically influence the film coverage, which finally determines the morphology of the films and behavior of the crystallization process.

Synthesis and Ferroelectric Properties of Sol–Gel Derived Intergrowth-Superlattice-Structured SrBi4Ti4O15-Bi4Ti3O12 Thin Films

2011 ◽  
Vol 197-198 ◽  
pp. 1781-1784
Author(s):  
Hua Wang ◽  
Jian Li ◽  
Ji Wen Xu ◽  
Ling Yang ◽  
Shang Ju Zhou
Keyword(s):  
Thin Films ◽  
Remanent Polarization ◽  
Annealing Temperature ◽  
Ferroelectric Properties ◽  
Sol Gel ◽  
Hysteresis Loops ◽  
Si Substrates ◽  
Gel Processing ◽  
Coercive Electric Field ◽  
Clockwise Hysteresis

Intergrowth-superlattice-structured SrBi4Ti4O15–Bi4Ti3O12(SBT–BIT) films prepared on p-Si substrates by sol-gel processing. Synthesized SBT–BIT films exhibit good ferroelectric properties. As the annealing temperature increases from 600°C to 700°C, the remanent polarization Prof SBT–BIT films increases, while the coercive electric field Ecdecreases. SBT–BIT films annealed at 700°C have a Prvalue of 18.9µC/cm2which is higher than that of SBT (16.8µC/cm2) and BIT (14.6µC/cm2), and have the lowest Ecof 142 kV/cm which is almost the same as that of SBT and BIT. The C-V curves of Ag/SBT-BIT/p-Si heterostructures show the clockwise hysteresis loops which reveal the memory effect due to the polarization. The memory window in C-V curve of Ag/SBT-BIT/p-Si is larger than that of Ag/SBT/p-Si heterostructure or Ag/BIT/p-Si heterostructure.

A Study on the Piezoelectric Properties of PZT and Doped PZT Thin Films by Sol-Gel Method

2010 ◽  
Vol 663-665 ◽  
pp. 650-653
Author(s):  
Jin Moo Byun ◽  
Jeong Sun Han ◽  
Jae Hyoung Park ◽  
Seong Eui Lee ◽  
Hee Chul Lee
Keyword(s):  
Thin Films ◽  
Piezoelectric Coefficient ◽  
Energy Harvester ◽  
Sol Gel ◽  
Pure Perovskite Structure ◽  
Pzt Thin Films ◽  
Gel Method ◽  
Sol Gel Method ◽  
Si Substrates ◽  
Pzt Thin Film

This study examined the effect of crystalline orientation and dopants such as Nb and Zn on the piezoelectric coefficient of sol-gel driven Pb1(Zr0.52Ti0.48)O3(PZT) and doped PZT thin films. Crack-free 1-μm-thick PZT and doped PZT thin films prepared by using 2-Methoxyethanol-based sol-gel method were fabricated on Pt/Ti/SiO2/Si substrates. The highly (111) oriented PZT thin films of pure perovskite structure could be obtained by controlling various parameters such as a PbTiO3 seed layer and a concentration of sol-gel solution. The Nb-Zn doped PZT thin films exhibited high piezoelectric coefficient which was about 50 % higher than that of undoped PZT thin film. The highest measured piezoelectric coefficient was 240 pC/N, which could be applicable to piezoelectrically operated MEMS actuator, sensor, or energy harvester devices.

Effects of Sputter-Deposited LaNiO3 Electrode on the Deposition and Properties of Ferroelectric Thin Films

1996 ◽  
Vol 433 ◽  
Author(s):  
T. B. Wu ◽  
J. M. Wu ◽  
C. M. Wu ◽  
M. J. Shyu ◽  
M. S. Chen ◽  
...  
Keyword(s):  
Thin Films ◽  
Magnetron Sputtering ◽  
Perovskite Phase ◽  
Sol Gel ◽  
Processing Condition ◽  
Fatigue Property ◽  
Rf Magnetron Sputtering ◽  
Ferroelectric Films ◽  
Si Substrates ◽  
Sputter Deposited

AbstractHighly (100)-textured thin film of metallic LaNiO3 (LNO) was grown on the Pt/Ti/SiO2/Si substrates by rf magnetron sputtering at ˜300°C, which was used as a bottom electrode to prepare highly (100)-textured ferroelectric films. Examples on the deposition of PbTiO3, (Pbl−xLax)TiO3, Pb(Zr0.53Ti0.47)O3, Pb[(Mg1/3Nb2/3)1−xTix]O3, and (Ba1−xSrx)TiO3 thin films by rf magnetron sputtering or sol-gel method are shown. A reduction of temperature for perovskite phase formation can be achieved, especially for those difficult to crystallize. The surface roughness of the ferroelectric films is also improved as compared to that of films deposited on conventional Pt electrode. Although the electrical properties of the ferroelectric films are affected by the out-diffusion of LNO when a higher temperature was used in the preparation of the films, under an appropriate processing condition, the highly (100)-textured films can have satisfactory electrical characteristics for application. Moreover, the polarization-fatigue property can be also improved by the use of LNO electrode.

scholarly journals Dielectric tunable characteristics of compositional-gradient BaTi1−xSnxO3 thin films

2021 ◽  
Vol 11 (04) ◽  
pp. 2150019
Author(s):  
Chenjing Wu ◽  
Manwen Yao
Keyword(s):  
Thin Films ◽  
Impedance Matching ◽  
Sol Gel ◽  
Temperature Stability ◽  
Dielectric Behavior ◽  
Compositional Gradient ◽  
Dielectric Tunability ◽  
Temperature Range ◽  
Si Substrates ◽  
Low Leakage

Compositional-gradient [Formula: see text][Formula: see text]O3 thin films on Pt(100)/Ti/SiO2/Si substrates are fabricated with sol–gel using spin coating. All of the structures of the prepared thin films are of single-phase crystalline perovskite with a dense and crack-free surface morphology. BTS10/15/20 thin film exhibits enhanced temperature stability in its dielectric behavior. The temperature coefficient of capacitance [Formula: see text] in the temperature range from [Formula: see text]C to [Formula: see text]C is [Formula: see text]C and that of [Formula: see text] in the temperature range from [Formula: see text]C to [Formula: see text]C is [Formula: see text]C. Furthermore, the thin films show low leakage current density and dielectric loss. High and stable dielectric tunable performances are found in BTS10/15/20 thin films: the dielectric tunability of the thin films is around 20.1% under a bias voltage of 8 V at 1 MHz and the corresponding dielectric constant is in the range between 89 and 111, which is beneficial for impedance matching in circuits. Dielectric tunability can be obtained under a low tuning voltage, which helps ensure safety. The simulated resonant frequency of the compositional-gradient BTS thin films depends on the bias electric field, showing compositional-gradient BTS thin films could be used in electrically tunable components and devices. These properties make compositional-gradient BTS thin films a promising candidate for dielectric tuning.

An Effective Way to Suppress the Pyrochlore Phase Formation in SBT Thin Films

2003 ◽  
Vol 784 ◽  
Author(s):  
Se-Yeon Jung ◽  
Woo-Chul Kwak ◽  
Seung-Joon Hwang ◽  
Yun-Mo Sung
Keyword(s):  
Thin Films ◽  
Phase Formation ◽  
Seed Layer ◽  
Sol Gel ◽  
Pyrochlore Phase ◽  
Energy Difference ◽  
Ion Diffusion ◽  
Aurivillius Phase ◽  
Si Substrates ◽  
Coating Methods

ABSTRACTSr0.7Bi2.4Ta2O9 (SBT) thin films were deposited on Pt/Ti/SiO2/Si substrates with and without a seed layer of ∼40 nm thickness using sol-gel and spin coating methods. The influence of seed layer on the phase formation characteristics of SBT thin films was investigated using x-ray diffraction (XRD) and scanning electron microscopy (SEM) analyses. Formation of pyrochlore as well as Aurivillius phase was observed in both the unseeded and seeded SBT films heated at 740°C. However, it was revealed that Aurivillius phase formation was enhanced in seeded SBT thin films and pyrochlore phase formation was highly suppressed. In this study, two possible mechanisms for the suppression of pyrochlore phase formation were proposed from the perspectives of activation energy difference for Aurivillius and pyrochlore phase formation and Bi-ion diffusion to pyrochlore phase.

Influence of Bi3.15Nd0.85Ti3O12 Buffer Layer on Structure and Electrical Properties of Bi0.94Ce0.06Fe0.97Ti0.03O3 Thin Films

2014 ◽  
Vol 703 ◽  
pp. 51-55
Author(s):  
Jia Zeng ◽  
Ming Hua Tang ◽  
Zhen Hua Tang ◽  
Yong Guang Xiao ◽  
Long Peng ◽  
...  
Keyword(s):  
Thin Films ◽  
Electrical Properties ◽  
Buffer Layer ◽  
Current Density ◽  
Coercive Field ◽  
Remnant Polarization ◽  
Sol Gel ◽  
Hysteresis Loops ◽  
Si Substrates ◽  
Sol Gel Process

Bi0.94Ce0.06Fe0.97Ti0.03O3 and Bi0.94Ce0.06Fe0.97Ti0.03O3/Bi3.15Nd0.85Ti3O12 double-layered thin films were fabricated via sol-gel process on Pt/Ti/SiO2/Si substrates. The influence of Bi3.15Nd0.85Ti3O12 buffer layer on microstructure and electrical properties of Bi0.94Ce0.06Fe0.97Ti0.03O3 thin films were investigated in detail. Well-saturated P-E hysteresis loops can be obtained in Bi0.94Ce0.06Fe0.97Ti0.03O3 films with Bi3.15Nd0.85Ti3O12 buffer. The remnant polarization (2Pr) of the double-layered thin films is 112 μC/cm2. The coercive field (2Ec) of double-layered films is 672 kV/cm, which is much lower than that of the Bi0.94Ce0.06Fe0.97Ti0.03O3 thin films. The leakage current density of Bi0.94Ce0.06Fe0.97Ti0.03O3/Bi3.15Nd0.85Ti3O12 double-layered thin films is 4.12×10-5 A/cm2.

Sign in / Sign up

Export Citation Format

Share Document