Experimental and theoretical studies of 4,6-diamino-2-mercaptopyrimidine as a copper inhibitor in 3.5 wt% NaCl solution

RSC Advances ◽  
2016 ◽  
Vol 6 (18) ◽  
pp. 15210-15219 ◽  
Author(s):  
Zhi Cheng ◽  
Shi Mo ◽  
Jing Jia ◽  
Ji Feng ◽  
Hong Qun Luo ◽  
...  
Keyword(s):  
Corrosion Inhibition ◽  
Inhibition Efficiency ◽  
Copper Surface ◽  
Theoretical Studies ◽  
Nacl Solution ◽  
High Corrosion ◽  
Corrosion Inhibition Efficiency ◽  
Experimental And Theoretical Studies

4,6-Diamino-2-mercaptopyrimidine can be adsorbed on copper surface and exhibits a high corrosion inhibition efficiency in 3.5 wt% NaCl solution.

Corrosion Inhibition of Polyethylene Glycol for Magnesium Alloy AZ91 at Different Temperatures

2014 ◽  
Vol 1015 ◽  
pp. 692-695
Author(s):  
Wei Shang ◽  
Zhou Lan Yin ◽  
Yu Qing Wen ◽  
Xu Feng Wang
Keyword(s):  
Polyethylene Glycol ◽  
Magnesium Alloy ◽  
Corrosion Inhibition ◽  
Inhibition Efficiency ◽  
Nacl Solution ◽  
Alloy Az91 ◽  
Magnesium Alloy Az91 ◽  
Polyethylene Glycol 200 ◽  
Different Temperatures ◽  
Corrosion Inhibition Efficiency

the corrosion inhibition of polyethylene glycol 200 for magnesium alloy AZ91 in 1% NaCl solution at different temperatures are studied. The morphology of the sample at 25°C is analyzed by SEM. And CHI600C electrochemistry workstation is employed to investigate the corrosion inhibition of the samples. The results show that the corrosion inhibition efficiency of polyethylene glycol 200 to the magnesium alloy AZ91 is affected by temperature. Polyethylene glycol 200 has superior corrosion inhibition to the magnesium alloy at the temperature of 25°C.

Adsorption and corrosion inhibition characteristics of two medicinal molecules

2019 ◽  
Author(s):  
Chem Int
Keyword(s):  
Hydrochloric Acid ◽  
Corrosion Rate ◽  
Mild Steel ◽  
Corrosion Inhibition ◽  
Half Life ◽  
Thermodynamic Data ◽  
Inhibition Efficiency ◽  
Gravimetric Method ◽  
Corrosive Environment ◽  
Corrosion Inhibition Efficiency

The corrosion inhibition characteristics of two medicinal molecules phenylalanine and rutin on mild steel in 1.0M Hydrochloric acid were evaluated using gravimetric method. Corrosion inhibition efficiency of 83.78 and 90.40 % was obtained respectively after seven days. However, phenylalanine showed weak accumulative higher corrosion inhibition efficiency. The presence of both molecules in the corrosive environment reduced the corrosion rate constant and increased the material half-life. Thermodynamic data calculated suggests a spontaneous adsorption of the molecules on the mild steel’s surface.

Sign in / Sign up

Export Citation Format

Share Document