Preparation and characterization of flame retardant polyurethane foams containing phosphorus–nitrogen-functionalized lignin

RSC Advances ◽  
2014 ◽  
Vol 4 (98) ◽  
pp. 55271-55279 ◽  
Author(s):  
Haibin Zhu ◽  
Zumao Peng ◽  
Yongmei Chen ◽  
Gaiyun Li ◽  
Lei Wang ◽  
...  
Keyword(s):  
Mechanical Strength ◽  
Flame Retardant ◽  
Polyurethane Foams ◽  
High Mechanical Strength ◽  
Rigid Polyurethane Foams

Lignin-based phosphate melamine was used as a partial substitute for polyols to synthesize rigid polyurethane foams which exhibit high mechanical strength and low flammability.

Preparation and Characterization of Soybean Oil-based Flame Retardant Rigid Polyurethane Foams Containing Phosphaphenanthrene Groups

2020 ◽  
Vol 17 (10) ◽  
pp. 760-771
Author(s):  
Qirui Gong ◽  
Niangui Wang ◽  
Kaibo Zhang ◽  
Shizhao Huang ◽  
Yuhan Wang
Keyword(s):  
Soybean Oil ◽  
Flame Retardant ◽  
Chemical Structure ◽  
Cell Structure ◽  
Polyurethane Foams ◽  
Limiting Oxygen Index ◽  
Rigid Polyurethane Foams ◽  
Degradation Activation Energy ◽  
Ft Ir

A phosphaphenanthrene groups containing soybean oil based polyol (DSBP) was synthesized by epoxidized soybean oil (ESO) and 9,10-dihydro-oxa-10-phosphaphenanthrene-10-oxide (DOPO). Soybean oil based polyol (HSBP) was synthesized by ESO and H2O. The chemical structure of DSBP and HSBP were characterized with FT-IR and 1H NMR. The corresponding rigid polyurethane foams (RPUFs) were prepared by mixing DSBP with HSBP. The results revealed apparent density and compression strength of RPUFs decreased with increasing the DSBP content. The cell structure of RPUFs was examined by scanning electron microscope (SEM) which displayed the cells as spherical or polyhedral. The thermal degradation and flame retardancy of RPUFs were investigated by thermogravimetric analysis, limiting oxygen index (LOI), and UL 94 vertical burning test. The degradation activation energy (Ea) of first degradation stage reduced from 80.05 kJ/mol to 37.84 kJ/mol with 80 wt% DSBP. The RUPF with 80 wt% DSBP achieved UL94 V-0 rating and LOI 28.3. The results showed that the flame retardant effect was mainly in both gas phase and condensed phase.

Preparation and Characterization of Excellent Flame Retarded Rigid Polyurethane Foams

2011 ◽  
Vol 374-377 ◽  
pp. 1563-1566
Author(s):  
An Zhen Zhang ◽  
Yi He Zhang
Keyword(s):  
Flame Retardant ◽  
Flame Retardants ◽  
Polyurethane Foams ◽  
Expandable Graphite ◽  
Dimethyl Methylphosphonate ◽  
Limiting Oxygen Index ◽  
Rigid Polyurethane Foams ◽  
Foaming Process ◽  
Flame Retarded

Rigid polyurethane foams were excellent thermal insulation materials with widely used, which was highly flammable at the same time. In order to obtain safe application, flame retarded polyurethane foams were needed. In this paper, series flame retarded rigid polyurethane foams were prepared with loading different flame retardants such as ammonium polyphosphate, expandable graphite, red phosphorus, Tri (2-chloroethyl) phosphate and dimethyl methylphosphonate. The effects of flame retardants on the foaming-process and flame retardant property of the rigid polyurethane foams were investigated by otary viscometer and limiting oxygen index. The results showed that the combination of solid and liquid flame retardants was necessary to improve the flame retardant and different flame retardants played synergistic roles in rigid polyurethane foams. The limiting oxygen indexes of the foams could be up to 30wt% and 29.6% with 25wt% solid flame retardants and 10wt% liquid retardants, respectively.

Synthesis and characterization of flame-retardant rigid polyurethane foams derived from gutter oil biodiesel

2021 ◽  
Vol 147 ◽  
pp. 110329
Author(s):  
Guangxu Bo ◽  
Xiaoling Xu ◽  
Xiaoke Tian ◽  
Jiao Wu ◽  
Xin He ◽  
...  
Keyword(s):  
Flame Retardant ◽  
Polyurethane Foams ◽  
Synthesis And Characterization ◽  
Rigid Polyurethane Foams

Effects of a novel phosphorus–nitrogen flame retardant on rosin-based rigid polyurethane foams

2015 ◽  
Vol 120 ◽  
pp. 427-434 ◽  
Author(s):  
Meng Zhang ◽  
Zhenyang Luo ◽  
Jinwen Zhang ◽  
Shuigen Chen ◽  
Yonghong Zhou
Keyword(s):  
Flame Retardant ◽  
Polyurethane Foams ◽  
Rigid Polyurethane Foams

A facile strategy to fabricate microencapsulated expandable graphite as a flame-retardant for rigid polyurethane foams

2015 ◽  
Vol 132 (31) ◽  
pp. n/a-n/a ◽  
Author(s):  
Xiao-Liang Zhang ◽  
Hong-Ji Duan ◽  
Ding-Xiang Yan ◽  
Li-Quan Kang ◽  
Wei-Qin Zhang ◽  
...  
Keyword(s):  
Flame Retardant ◽  
Polyurethane Foams ◽  
Expandable Graphite ◽  
Rigid Polyurethane Foams

Expandable Graphite For Halogen-Free Flame-Retardant of High-Density Rigid Polyurethane Foams

2005 ◽  
Vol 44 (7) ◽  
pp. 1323-1337 ◽  
Author(s):  
Lei Shi ◽  
Zhong-Ming Li ◽  
Ming-Bo Yang ◽  
Bo Yin ◽  
Qiu-Ming Zhou ◽  
...  
Keyword(s):  
Flame Retardant ◽  
Polyurethane Foams ◽  
High Density ◽  
Expandable Graphite ◽  
Rigid Polyurethane Foams ◽  
Halogen Free
Sign in / Sign up

Export Citation Format

Share Document