Constructing a multicomponent junction for improved visible-light photocatalytic performance induced by Au nanoparticles

2015 ◽  
Vol 51 (11) ◽  
pp. 2173-2176 ◽  
Author(s):  
Lequan Liu ◽  
Peng Li ◽  
Tao Wang ◽  
Huilin Hu ◽  
Haiying Jiang ◽  
...  
Keyword(s):  
Visible Light ◽  
Photocatalytic Performance ◽  
Au Nanoparticles ◽  
Effective Strategy ◽  
Visible Light Photocatalytic

The construction of a multicomponent junction nanostructure is demonstrated to be an effective strategy to promote Au-induced visible-light photocatalytic performance.

scholarly journals The improvement of photocatalysis O2 production over BiVO4 with amorphous FeOOH shell modification

2019 ◽  
Vol 9 (1) ◽  
Author(s):  
Ying Zhang ◽  
Lei Shi ◽  
Zhongxing Geng ◽  
Tieqiang Ren ◽  
Zhanxu Yang
Keyword(s):  
Visible Light ◽  
Photocatalytic Performance ◽  
Photocatalytic Property ◽  
Interface Effect ◽  
Experimental Results ◽  
Effective Strategy ◽  
O2 Production ◽  
Visible Light Photocatalytic

AbstractA novel amorphous FeOOH modified BiVO4 photocatalyst (A-FeOOH/BiVO4) was successfully produced and characterized by various techniques. The results showed that amorphous FeOOH with about 2 nm thickness evenly covered on BiVO4 surface, which caused resultant A-FeOOH/BiVO4 exhibiting higher visible light photocatalytic performance for producing O2 from water than BiVO4. When the covered amount of amorphous FeOOH was 8%, the resultant photocatalyst possessed the best photocatalytic performance. To find the reasons for the improvement of photocatalytic property, electrochemical experiments, DRS, PL and BET, were also measured, the experimental results indicated that interface effect between amorphous FeOOH and BiVO4 could conduce to migration of photogenerated charge, and exhibit stronger light responded capacity. These positive factors promoted A-FeOOH/BiVO4 presenting improved the photocatalytic performance. In a word, the combination of amorphous FeOOH with BiVO4 is an effective strategy to conquer important challenges in photocatalysis field.

scholarly journals Construction of Ag3PO4/SnO2 Heterojunction on Carbon Cloth with Enhanced Visible Light Photocatalytic Degradation

2020 ◽  
Vol 10 (9) ◽  
pp. 3238
Author(s):  
Min Liu ◽  
Guangxin Wang ◽  
Panpan Xu ◽  
Yanfeng Zhu ◽  
Wuhui Li
Keyword(s):  
Visible Light ◽  
Photocatalytic Performance ◽  
Separation Efficiency ◽  
Photogenerated Electron ◽  
Carbon Cloth ◽  
Electron Hole ◽  
Step Process ◽  
Photogenerated Electrons ◽  
Rapid Transfer ◽  
Visible Light Photocatalytic

In this study, the Ag3PO4/SnO2 heterojunction on carbon cloth (Ag3PO4/SnO2/CC) was successfully fabricated via a facile two-step process. The results showed that the Ag3PO4/SnO2/CC heterojunction exhibited a remarkable photocatalytic performance for the degradation of Rhodamine B (RhB) and methylene blue (MB), under visible light irradiation. The calculated k values for the degradation of RhB and MB over Ag3PO4/SnO2/CC are 0.04716 min−1 and 0.04916 min−1, which are higher than those calculated for the reactions over Ag3PO4/SnO2, Ag3PO4/CC and SnO2/CC, respectively. The enhanced photocatalytic activity could mainly be attributed to the improved separation efficiency of photogenerated electron-hole pairs, after the formation of the Ag3PO4/SnO2/CC heterojunction. Moreover, carbon cloth with a large specific surface area and excellent conductivity was used as the substrate, which helped to increase the contact area of dye solution with photocatalysts and the rapid transfer of photogenerated electrons. Notably, when compared with the powder catalyst, the catalysts supported on carbon cloth are easier to quickly recycle from the pollutant solution, thereby reducing the probability of recontamination.

scholarly journals Enhanced Visible-Light Photocatalytic Performance of SAPO-5-Based g-C3N4 Composite for Rhodamine B (RhB) Degradation

Materials ◽  
2019 ◽  
Vol 12 (23) ◽  
pp. 3948
Author(s):  
Lingfang Qiu ◽  
Zhiwei Zhou ◽  
Mengfan Ma ◽  
Ping Li ◽  
Jinyong Lu ◽  
...  
Keyword(s):  
Photocatalytic Activity ◽  
Visible Light ◽  
Redox Reactions ◽  
Photocatalytic Performance ◽  
Dye Degradation ◽  
Thermal Polymerization ◽  
Light Illumination ◽  
Electron Hole ◽  
Visible Light Illumination ◽  
Visible Light Photocatalytic

Novel visible-light responded aluminosilicophosphate-5 (SAPO-5)/g-C3N4 composite has been easily constructed by thermal polymerization for the mixture of SAPO-5, NH4Cl, and dicyandiamide. The photocatalytic activity of SAPO-5/g-C3N4 is evaluated by degrading RhB (30 mg/L) under visible light illumination (λ > 420 nm). The effects of SAPO-5 incorporation proportion and initial RhB concentration on the photocatalytic performance have been discussed in detail. The optimized SAPO-5/g-C3N4 composite shows promising degradation efficiency which is 40.6% higher than that of pure g-C3N4. The degradation rate improves from 0.007 min−1 to 0.022 min−1, which is a comparable photocatalytic performance compared with other g-C3N4-based heterojunctions for dye degradation. The migration of photo-induced electrons from g-C3N4 to the Al site of SAPO-5 should promote the photo-induced electron-hole pairs separation rate of g-C3N4 efficiently. Furthermore, the redox reactions for RhB degradation occur on the photo-induced holes in the g-C3N4 and Al sites in SAPO-5, respectively. This achievement not only improves the photocatalytic activity of g-C3N4 efficiently, but also broadens the application of SAPOs in the photocatalytic field.