Spectroscopic and DFT investigations on the corrosion inhibition behavior of tris(5-methyl-2-thioxo-1,3,4-thiadiazole)borate on high carbon steel and aluminium in HCl media

RSC Advances ◽  
2013 ◽  
Vol 3 (45) ◽  
pp. 23681 ◽  
Author(s):  
Ramalingam Tamilarasan ◽  
Anandaram Sreekanth
Keyword(s):  
Carbon Steel ◽  
Corrosion Inhibition ◽  
High Carbon Steel ◽  
High Carbon

Chemical and electrochemical investigations of high carbon steel corrosion inhibition in 10 % HCl medium by quinoline chalcones

Ionics ◽  
2012 ◽  
Vol 19 (6) ◽  
pp. 919-932 ◽  
Author(s):  
Ganesan Ayyannan ◽  
Kuppusamy Karthikeyan ◽  
Shanmuga Sundaram Vivekananthan ◽  
Mayakrishnan Gopiraman ◽  
Arumugam Rathinavelu
Keyword(s):  
Carbon Steel ◽  
Corrosion Inhibition ◽  
High Carbon Steel ◽  
Steel Corrosion ◽  
High Carbon ◽  
Hcl Medium

scholarly journals Data on Evaluation of the Corrosion Inhibition Effect of L-alpha-aminoisocaproate on High Carbon Steel Corrosion in Dilute Acid Media

2019 ◽  
Vol 25 (4) ◽  
pp. 422-426
Author(s):  
Roland LOTO ◽  
Cleophas LOTO
Keyword(s):  
Carbon Steel ◽  
Corrosion Inhibition ◽  
High Carbon Steel ◽  
Open Circuit ◽  
Time Dependent ◽  
Secondary Amines ◽  
High Carbon ◽  
Acid Media ◽  
Potential Measurement ◽  
Inhibition Performance

Corrosion inhibition performance of l-alpha-aminoisocaproate on high carbon steel in 1 M HCl solution has been studied by weight loss measurement, open circuit potential measurement, optical microscopy and ATF-FTIR spectral analysis. The results showed the inhibition performance of l-alpha-aminoisocaproate is time dependent attaining an optimal value of 85.88 % at 5.63 % l-alpha-aminoisocaproate concentration (highest concentration) after 288 h of exposure. The corrosion potential plots of the high carbon steel at 0.91 % (lowest concentration) and 5.63 % l-alpha-aminoisocaproate concentration were more electropositive than the plots at 0% l-alpha-aminoisocaproate concentration due to the effective inhibition performance of l-alpha-aminoisocaproate in counteracting the oxidation of the carbon steel in the presence of chloride anions. Identified functional groups of alcohols, phenols, primary and secondary amines and amides, carboxylic acids, alkynes, aromatics, alkenes and alkanes consisting of O–H stretch, free hydroxyl, H–bonded, N–H stretch, –C(triple bond)C–H: C–H stretch, C–H stretch and =C–H stretch bonds where responsible for the corrosion inhibition. The optical morphology of the carbon steel after 7200 s of exposure in the acid solution without l-alpha-aminoisocaproate was severely corroded in contrast to the morphology of the steel in the presence of l-alpha-aminoisocaproate which underwent minor deterioration due to the time dependent action of the inhibitor.

scholarly journals Electrochemical analysis of the corrosion inhibition properties of L-leucine and trypsin complex admixture on high carbon steel in 1 M H2SO4 solution

2018 ◽  
Vol 47 (2) ◽  
pp. 12-20 ◽  
Author(s):  
Roland Loto
Keyword(s):  
Carbon Steel ◽  
Corrosion Inhibition ◽  
High Carbon Steel ◽  
Electrochemical Analysis ◽  
H2so4 Solution ◽  
High Carbon ◽  
Los Grupos

Se evaluó la inhibición de la corrosión por parte de compuestos químicos biodegradables (complejo de L-leucina y tripsina) sobre acero de alto contenido de carbono en H2SO4 1 M a través de técnica de polarización potenciodinámica, análisis de pérdida de peso, medición de potencial de circuito abierto, microscopía óptica y espectroscopia ATR-FTIR. Los datos obtenidos mostraron que la mezcla tiene una eficacia de inhibición máxima de 82,4% y 90,08%, a partir de las pruebas electroquímicas con propiedades de inhibición de tipo mixto. La adición de la mezcla cambia significativamente el potencial de corrosión del acero a los valores de pasivación de la medición del potencial de circuito abierto. Los resultados de los cálculos termodinámicos indicaron un mecanismo de adsorción por quimisorción de acuerdo con las isotermas Langmuir, Freundlich y Frumkin, acopladas con coeficientes de correlación de 0,9994; 0,9651 y 0,8834, respectivamente. El análisis estadístico mostró que el tiempo de exposición es la variable más importante en la inhibición de la corrosión. Los grupos funcionales de la mezcla, identificados mediante espectroscopía ATF-FTIR, fueron completamente adsorbidos en la superficie de acero al carbono; esto se dedujo a partir de la observación de la disminución de la intensidad de pico. Las imágenes de microscopía óptica de las superficies de acero inhibidas y desinhibidas contrastan entre sí, debido a la presencia de macro-pozos y óxido poroso en el acero desinhibido.